Growth and near-infrared optical properties of Nd<SUP>3+</SUP>-doped KGd<sub>0.1</sub>Lu<sub>0.9</sub>(WO<sub>4</sub>)<sub>2</sub> crystal
Zhipeng Zhang,Rujia Chen,Xiliang Jiang,Yimin Yang,Zhuang Leng,Lingbo Zhou,Chunyu Zuo,Chun Li,Weiling Yang,Fanming Zeng,Hai Lin,Shasha Li,Lina Liu,Zhongmin Su
DOI: https://doi.org/10.1016/j.infrared.2023.104990
IF: 2.997
2023-01-01
Infrared Physics & Technology
Abstract:In this paper, x at.% Nd3+: KGd0.1Lu0.9-x(WO4)2 (x = 1, 2, 3, 4, 5) crystals were grown by the top seed solution growth method (TSSG). The crystal structure was analyzed by X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR), and the crystal structure data was obtained by Rietveld refinement. The absorption spectra, near-infrared emission spectra and fluorescence decay curves of Nd3+ ions in the crystal were measured at indoor temperature. According to Judd-Ofelt theory, the spectral intensity parameters omega 2 , omega 4 and omega 6 are calculated. When the doping concentration is 3 at.%, omega 2 is the largest, which is 3.84 x 10-20 cm2 , while the spectral mass factor is the lowest, which is 0.3734. The absorption and emission cross-section are calculated by combining the absorption spectrum and emission spectrum, and the maximum calculated result of emission cross-section is 1.35 x 10-19 cm2. The results show that Nd3+: KGd0.1Lu0.9(WO4)2 crystals has great application potential in the 1.0 mu m field.