Effect of post-weld heat treatment on the microstructure and plastic deformation behavior of friction stir welded 2024
Zhili Hu,Shijian Yuan,Xiaosong Wang,Gang Liu,Yongxian Huang
DOI: https://doi.org/10.1016/j.matdes.2011.05.035
IF: 9.417
2011-01-01
Materials & Design
Abstract:To improve the plasticity of friction stir welded joints for plastic processing applications, post-weld heat treatment (PWHT) of 2024-O aluminum alloy friction stir welding joints was carried out at annealing temperatures from 250 °C to 450 °C with an interval of 50 °C for 2 h, followed by cooling to 200 °C in the furnace. The effect of PWHT on the microstructure and plastic deformation behavior of the joints was investigated. It was found that the fine-equiaxed grains are stable and retained in the nugget of the joints even after annealing at 450 °C for 2 h. However, the grains in the thermo-mechanically affected zone (TMAZ) of the joints become coarse and equiaxed as annealing temperature increases. The plastic deformation of as-welded joint is very heterogeneous. In contrast, the plastic deformation of PWHT joint is relatively homogeneous by both the nugget and the base material showing large deformation. The decrease in elongation of as-welded joints is completely recovered by PWHT. The high ductility of the joint is mainly attributed to the retention of the fine-equiaxed grains in the nugget during PWHT. 1 Introduction Due to economical and ecological reasons as well as to improve product properties, aluminum alloy welds, which show high production efficiency and flexibility, have gained more interest in manufacturing lightweight structures for automotives and aircrafts [1–3] . The industrial application of aluminum alloy welds in lightweight constructions is basically connected to one fundamental manufacturing requirement. The formability of welds must be adequate in order to shape the required geometries [4] . It is well known that high-strength aluminum alloys (2XXX series) are widely used for aerospace structures such as fuselage, fins and wings [5] . Unfortunately, such high-strength aluminum alloys are difficult to join by conventional fusion welding due to the occurrence of hot cracking during welding [6] . Friction stir welding (FSW), as a solid state metal joining technique, do prove itself ideal for creating better quality joints compared to fusion welds [6–8] . However, many studies on the transverse tensile properties of FSW joints indicated that the elongations of as-welded joints are only 20–40% those of the BM for the heterogeneous microstructure of the joint [6,9–11] . To improve the mechanical properties of FSW joints, one option is to fully post-weld heat treatment (PWHT) of the welded components. Currently the PWHT mainly consists of solution heat treatment and precipitation or aging treatment, aiming to recover the loss of tensile strength in the nugget zone [12–15] . A few studies on the PWHT of FSW aluminum alloys such as 7449 [14] , 6061-O [12] , 2219-O [13] and 2024-T4 [15] had shown that the PWHT recovered a large portion of the lost strength in the nugget, but there was an accompanying loss in ductility. The joints have a 40–77% decrease in elongation compared to that of base material (BM). In addition, studies in this area have shown that the fine grains in the nugget are not stable during PWHT, which results in undesirable coarsened grain structures [12–20] . This kind of microstructural instability has been identified as abnormal grain growth (AGG). Although in a few studies AGG has proved to be beneficial to recover the lost strength of joint, it is not at all desirable for enhanced plasticity [17–19] . Ductility falls off sharply due to extreme microstructural instability [18,19] . Accordingly, it is necessary to find out some effective remedial process to improve the elongation of joints, and avoid AGG occurring in the nugget at same time. Normally the friction stir welds are used in the as-welded condition or with stabilization aging when BM is in the hardened conditions (T3, T4 and T6 tempers). However, there are some advantages in carrying out the welding with BM in a soft condition. The forming operation after FSW can be much more easily performed if the welding is conducted under O condition. Furthermore, the solution and aging heat treatment can restore the mechanical properties of the joints successfully after the forming operation [12–15,20] . The present letter analyzes the microstructure and plastic deformation behavior of FSW aluminum alloys to evaluate if, with the right selection of post-weld annealing treatment parameters, their plasticity and strength could be optimized. 2 Experimental procedures Some 5 mm-thick 2024 aluminum alloy rolled plates were FSW with a travel speed, a rotational speed and a shoulder diameter of 300 mm/min, 600 rpm and 14 mm, respectively. Then the plates were cut into two parts, one part for PWHT and the other for as-welded examinations. The PWHT included annealing at different temperature from 250 °C to 450 °C with an interval of 50 °C for 2 h, followed by cooling to 200 °C in the furnace. Following FSW and PWHT, The orientation-imaging microscope (OIM) was attached to an S-570/HITACHI-4700 scanning electron microscope (SEM) operating at 25 kV. The OIM was used to evaluate grain size distribution with step size of 1 μm. The Vickers micro-hardness test was carried out along the centerlines of the cross-sections with a distance between neighboring measured points of 1 mm under a load of 100 g for 10 s. The transverse tensile specimens were prepared with reference to China National Standard GB/T2651-2008 [21] (equivalent to ASTM B557-02 [22] ). The room temperature tensile tests were performed at a crosshead speed of 2 mm/min using an Instron-1186 testing machine. An axial extensometer with 25 mm gage length was attached to the test specimens at the gage section. The strain analysis of each specimen was made by the ASAME® automatic strain measuring system, and the tensile properties of the joints were evaluated using three tensile specimens cut from the same joint. 3 Results and discussion 3.1 Microstructures The OIM images of joints in the transition zone from the nugget to thermo-mechanically affected zone (TMAZ) are shown in Fig. 1 . The nugget of as-welded joint is composed of fine-equiaxed recrystallized grains with average grain size of 1.7 μm as seen in Fig. 1 a. After PWHT, average grain size in the nugget of the 300 °C annealed joint and the 450 °C annealed joint are1.8 μm and 2.0 μm, respectively. It indicates that the fine-equiaxed grains are stable in the nugget during PWHT ( Fig. 1 b and c) and no AGG is observed even the annealing temperature up to 450 °C. However, the grain size and shape in the TMAZ vary significantly with the annealing temperature. The initial grains in the TMAZ are rotated and elongated in an upward flowing pattern around the nugget before PWHT ( Fig. 1 a). Such phenomenon can also be observed in the TMAZ of the 300 °C annealed joint ( Fig. 1 b), but nearly all the grains in the TMAZ of the joint become coarse and equiaxed after annealing at 450 °C ( Fig. 1 c). It indicates that the rotated and elongated grains in the TMAZ of joints tend to be coarse and equiaxed with the increasing annealing temperature. The back scattered SEM micrograph in the nugget of FSW joint is shown in Fig. 2 . There are two different particles in the as-weld joint, marked by A and B ( Fig. 2 a). The Energy Dispersive Spectrometry (EDS) analysis showed that these particles are compounds of Al–Cu–Mg and Al–Cu–Fe–Mn ( Fig. 2 c and d). According to the literatures these compounds are most likely Al 2 CuMg and (Cu, Fe, Mn) Al 6 [23,24] . As seen in Fig. 2 a, the grain size of the strengthening precipitates such as rod or lath shaped Al 2 CuMg are 0.2–0.5 μm, and also it is shown that some of the particles present in the as-welded joint dissolve and slightly coarsen during PWHT. As seen in Fig. 2 b, a much-reduced density of particles with the grain size of 0.5–2 μm is observed after annealing at 450 °C. It is known that strengthening precipitates such as rod or lath shaped Al 2 CuMg can coarsen or dissolve during high temperature heat treatment [6] , while particles, including Fe and Mn, are insoluble in aluminum alloys [25] . Therefore all particles, which can be seen in SEM image after PWHT, are undissolved Al 2 CuMg and insoluble (Cu, Fe, Mn) Al 6 particles. It is reported that a dispersed, thermally stable precipitates may help to control the AGG behavior [16] . Consequently joints do not show any sign of AGG during PWHT and the fine-equiaxed grains are retained in the nugget. 3.2 Micro-hardness The micro-hardness profiles of the joints before and after PWHT can be seen in Fig. 3 . The maximum micro-hardness value of the as-welded joint can reach two times that of the BM. It is known that the hardness in the precipitation-hardening aluminum alloys greatly depends on the grain size and precipitate distribution [26] . The nugget of the as-welded joint is composed of the recrystallized fine-equiaxed grains ( Fig. 1 a) for experiencing intense plastic deformation and frictional heating during FSW [7] . Therefore, the joint is strengthened by FSW process. The micro-hardness values of PWHT joints vary depending on the annealing temperature. The micro-hardness value in the nugget of PWHT joint is slightly higher than that of the BM after annealing at 300 °C, but when the annealing temperature is above 300 °C, the micro-hardness values of the PWHT joints are almost same with that of the BM. It indicates that the micro-harnesses values in the nugget of the PWHT joints decrease with the increasing annealing temperature. It is mainly due to the dissolving and the coarsening of precipitates resulted from the thermal history during PWHT ( Fig. 2 ). 3.3 Tensile properties and fracture surfaces The room temperature tensile properties are summarized in Table 1 . The as-welded joint possesses the same tensile strength as that of the BM. However, the elongation of the joint is 12.5%, which shows a 44% reduction in elongation compared with that of the BM. After PWHT, the elongation of the joints has been significantly improved, and increases with decreasing annealing temperature. The maximum elongation of the joints is up to 20.2% after annealing at 300 °C, equivalent to 1.6 times that of the as-welded joint. Furthermore, all joints show nearly the same tensile strength as that of the BM at different annealing temperature, as shown in Table 1 . It can be attributed to the presence of a dispersed, stable precipitates, which increases strength by pinning grain boundaries and by also interfering with dislocation motion [27] . These results indicate that the plasticity of as-welded joint can be improved by PWHT effectively with no loss of tensile strength. An examination of the tensile fracture surfaces does provide useful information pertaining to the role and contribution of the intrinsic microstructural features on strength and ductility of the joints [9,15] . The fracture surfaces of the tensile tested specimens are characterized using SEM. The SEM photographs are taken from the center regions of the tested specimens, and the pictures are presented in Fig. 4 . The fractures of joints are predominantly transgranular. As seen in Fig. 4 a, an array of randomly fine microscopic cracks and a population of voids of varying size and shape are distributed through the fracture surface of as-welded joint. Cracked second-phase particles and shallow dimples are found covering the transgranular fracture region. Such phenomena can also be observed in fracture faces of PWHT joints. However, The depth and width of the observed dimples in fracture face of the 300 °C annealed joint ( Fig. 4 b) are more, compared with the as-welded joint ( Fig. 4 a) and the PWHT 450 °C joint ( Fig. 4 c). It is reported that the size of the dimples in the fracture surfaces could be indicative of the ductility of FSW joints [9] . The size of the dimples in the fracture surface of joint is large. It suggests that a large stretch zone is present at the tip of the crack. This led to a large plastic zone ahead of the crack and rather high ductility [10] . Consequently, the 300 °C annealed joint shows higher ductility than the as-welded joint and the 450 °C annealed joint. As the dimples increase in size ( Fig. 4 ), the elongation of the joints also increases ( Table 1 ). 3.4 Plastic deformation behavior The microstructure variation occurring through the weld results in a heterogeneous strain distribution when a tensile test is carried out normal to the welding direction, as shown in Fig. 5 . The retreating side and advancing side of each joint are denoted by RS and AS, respectively. As shown in Fig. 5 a, the BM on the advancing side locally elongated to high levels of strain (over 30%), eventually resulting in necking and fracture, whereas the strain of the nugget and the BM on the retreating side experience only 4% and 10%, respectively. It shows that regional deformation of as-welded joint is highly inhomogeneous. It is mainly because the strength of the nugget is higher than that of the BM for the grain size strengthening (average grain size in the nugget is 1.7 μm). Thus deformation in the nugget is small during tensile test. It can be concluded that the highly inhomogeneous deformation throughout the joint, caused by heterogeneous microstructure, is the reason for the 44% decrease in elongation of the as-welded joint compared with that of the BM. The strain map of the 300 °C annealed joint is shown in Fig. 5 b. The plastic deformation concentrates in the BM on the advancing side with the local strain exceeding 30%. The average strain of the nugget and the BM on the retreating side is about 8% and 12%, respectively. It indicates that the deformation inhomogeneity of the joint has been improved by both the nugget and the BM showing large strain, especially, the average strain in the nugget is two times that of the as-welded joints. The slightly harder nature of the nugget promotes plastic deformation of the BM during transverse tensile tests, up to fracture in this zone. Therefore, the joint shows relatively homogeneous deformation and the elongation of the joint increases. The high ductility of the PWHT joint is mainly attributed to the retention of the fine-equiaxed grains in the nugget during PWHT [28] . The strain map of the 450 °C annealed joints on the retreating side is shown in Fig. 5 c. The distribution of the strain for the 450 °C annealed joints is completely different. The deformation localizes in the nugget and TMAZ. This localization extends until fracture, which happens at the nugget/TMAZ boundary. The fracture locations of joints change with the annealing temperature, which can be explained by the grain coarsening in the TMAZ after annealing at 450 °C ( Fig. 1 c). The interface between the nugget and the TMAZ is more clearly visible and becomes a weaker region resulting in the fracture along the interface as seen in Fig. 5 c. When fracture happens, local strain in the interface is only 17%. However, the fracture strain of the as-welded joint and the 300 °C annealed joint are over 30%, indicating that the fracture toughness of the 450 °C annealed joint is low. The decrease in fracture toughness can be correlated to the grain coarsening in the TMAZ and the decrease of precipitates in the nugget after annealing at 450 °C [12,15] . This low fracture toughness results in a much lower ductility of the joint. 4 Conclusions In this study, the effect of PWHT on the microstructure and plastic deformation behavior of the joints was investigated, and the following conclusions are obtained. (1) The decrease in elongation of as-welded joints is completely recovered by PWHT. The maximum elongation of the PWHT joint is 1.6 times that of the as-welded joints with no loss of tensile strength. (2) The AGG are not observed in the joints during PWHT at 250–450 °C, and the fine-equiaxed grains are retained in the nugget of the joints. However, the grains in the TMAZ of the joints coarsen with increasing annealing temperature. The interface between the nugget and TMAZ become more clearly visible and results in the fracture along the interface. (3) Tensile fractures of PWHT joints are predominantly transgranular, and fracture surface is covered with dimples of varying size and shape, reminiscent of locally ductile failure. The depth and width of the observed dimples in fracture face of the 300 °C annealed joint are more, compared with the as-welded joint. As the dimples increase in size, the elongation of the joints also increases. (4) The micro-hardness value in the nugget of PWHT joint is slight higher than that of the BM after annealing at 300 °C. When annealing temperature is above 300 °C, the micro-hardness values of PWHT joints are almost same with that of the BM. The micro-hardness of the PWHT joints decreases with the increase of annealing temperature. (5) The plastic deformation of as-welded joint is very heterogeneous, but the plastic deformations of the PWHT joints are relatively homogeneous by both the nugget and the BM showing large strain. The slightly harder nature of the nugget promotes plastic deformation of the BM during transverse tensile tests, up to fracture in the BM. (6) A follow on work is planned to study the effect of post-weld heat treatment on mechanical properties of FSW joints in order to improve joint strength. References [1] S.J. Yuan C. Han X.S. Wang Hydroforming of automotive structural components with rectangular-sections Int J Mach Tool Manuf 46 2006 1201 1206 [2] M. Garware G.T. Kridli P.K. Mallick Tensile and fatigue behavior of friction-stir welded tailor-welded blank of aluminum alloy 5754 J Mater Eng Perform 19 2010 1161 1171 [3] M.P. Miles B.J. Decker T.W. Nelson Formability and strength of friction-stir-welded aluminum sheets Metall Mater Trans A 35A 2004 3461 3468 [4] M. Merklein M. Wieland D. Staud Friction stir welds made out of precipitation hardenable aluminum alloys-experimental investigations of formability potential Int J Mater Form 2 2009 323 326 [5] A. Heinz A. Hasler C. Keidel S. Moldenhauer R. Benedictus W.S. Miller Recent development in aluminum alloy for aerospace applications Mater Sci Eng A 280 2000 102 107 [6] C. Genevois A. Deschamps A. Denquin B. Doisneau-cottignies Quantitative investigation of precipitation and mechanical behaviour for AA2024 friction stir welds Acta Mater 53 2005 2447 2458 [7] R. Nandan T. DebRoy H.K.D.H. Bhadeshia Recent advances in friction-stir welding-process, weldment structure and properties Prog Mater Sci 53 2008 980 1023 [8] R.S. Mishra Z.Y. Ma Friction stir welding and processing Mater Sci Eng R 50 2005 1 78 [9] T.S. Srivatsan S. Vasudevan L. Park The tensile deformation and fracture behavior of friction stir welded aluminum alloy 2024 Mater Sci Eng A 466 2007 235 245 [10] H. Aydın A. Bayram A. Uguz S.K. Akay Tensile properties of friction stir welded joints of 2024 aluminum alloys in different heat-treated-state Mater Des 30 2009 2211 2221 [11] W.F. Xu J.H. Liu G.H. Luan C.L. Dong Temperature evolution, microstructure and mechanical properties of friction stir welded thick 2219-O aluminum alloy joints Mater Des 30 2009 3460 3467 [12] K.N. Krishnan The effect of post weld heat treatment on the properties of 6061 friction stir welded joints J Mater Sci 37 2002 473 480 [13] Y.C. Chen H.J. Liu J.C. Feng Effect of post-weld heat treatment on the mechanical properties of 2219-O friction stir welded joints J Mater Sci Lett 41 2006 297 299 [14] A. Sullivan J.D. Robson Microstructural properties of friction stir welded and post-weld heat-treated 7449 aluminum alloy thick plate Mater Sci Eng A 478 2008 351 360 [15] H. Aydın A. Bayram I. Durgun The effect of post-weld heat treatment on the mechanical properties of 2024-T4 friction stir-welded joints Mater Des 31 2010 2568 2577 [16] I. Charit R.S. Mishra Abnormal grain growth in friction stir processed alloys Scr Mater 58 2008 367 371 [17] Y.C. Chen J.C. Feng H.J. Liu Stability of the grain structure in 2219-O aluminum alloy friction stir welds during solution treatment Mater Charact 58 2007 174 178 [18] I. Charit R.S. Mishra High strain rate superplasticity in a commercial 2024 Al alloy via friction stir processing Mater Sci Eng A 359 2003 290 296 [19] K.A.A. Hassan A.F. Norman D.A. Price P.B. Prangnell Stability of nugget zone grain structures in high strength Al alloy friction stir welds during solution treatment Acta Mater 51 2003 1923 1936 [20] J.C. Feng Y.C. Chen H.J. Liu Effects of post-weld heat treatment on microstructure and mechanical properties of friction stir welded joints of 2219-O aluminium alloy Mater Sci Technol 22 2006 86 90 [21] China National Standard, GB/T2651-2008. Tensile test method on welded joints. China; 2008. [22] ASTM Standards, ASTM B557-02. Standard test methods of tension testing wrought and cast aluminum- and magnesium-alloy products, USA; 2002. [23] L.F. Mondolfo Aluminum alloys: structure and properties 1976 Butterworth London [24] Brooks CR. Heat treatment, structure and properties of nonferrous alloys. Metals Park (OH, USA): ASM 1984. [25] I.V. Cravetchi M. Taschuk Y.Y. Tsui R. Fedosejevs Spectrochemical microanalysis of aluminum alloys by laser-induced breakdown spectroscopy Spectrochim Acta B 59 2004 1439 1450 [26] Y.S. Sato S.H.C. Park H. Kokawa Microstructural factors governing hardness in friction-stir welds of solid-solution-hardened Al alloys Metall Mater Trans A 32A 2001 3033 3042 [27] M.J. Starink A. Deschamps S.C. Wang The strength of friction stir welded and friction stir processed aluminium alloys Scr Mater 58 2008 377 382 [28] Mishra RS, Sharma SR, Mara NA, Mahoney MW. Mechanical properties of friction stir welded aluminum alloys. in: Proceedings of the international conference on jointing of advanced and specialty materials III. ASM International; 2000.
What problem does this paper attempt to address?
-
Effects of Post-Weld Heat Treatment on Microstructure and Mechanical Properties of Friction Stir Welded Joints of 2219-O Aluminium Alloy
JC Feng,YC Chen,HJ Liu
DOI: https://doi.org/10.1179/174328406x79298
IF: 1.8
2006-01-01
Materials Science and Technology
Abstract:Post-weld heat treatment (PWHT) of 2219-O aluminium alloy friction stir welding joints was carried out at solution temperatures of 480, 500 and 540°C for 32 min followed by aging at 130°C for 9 h. The effects of PWHT on the microstructure and mechanical properties of the joints were investigated. Experimental results show that PWHT causes coarsening of the grains in the weld, and the coarsening degree increases with increasing solution temperature. The tensile strength of the heat treated joints increases with increasing solution temperature. The maximum tensile strength can reach 260% that of the base material at the solution temperature of 540°C. PWHT has a significant effect on the fracture locations of the joints. When the solution temperature is lower than 500°C, the joints fracture in the base material; when the temperature is higher than 500°C, the joints fracture in the weld. The change of the fracture locations of joints is attributed to the presence of precipitate free zones beside the grain boundaries and coarsening equiaxed grain structures in the weld.
-
Effect of Heat Treatment on Tensile Properties of Friction Stir Welded Joints of 2219-T6 Aluminium Alloy
HJ Liu,YC Chen,JC Feng
DOI: https://doi.org/10.1179/026708306x81513
IF: 1.8
2006-01-01
Materials Science and Technology
Abstract:The effect of post-weld heat treatment (PWHT) on the tensile properties of friction stir welded (FSW) joints of 2219-T6 aluminium alloy was investigated. The PWHT was carried out at aging temperature of 165°C for 18 h. The mechanical properties of the joints were evaluated using tensile tests. The experimental results indicate that the PWHT significantly influences the tensile properties of the FSW joints. After the heat treatment, the tensile strength of the joints increases and the elongation at fracture of the joints decreases. The maximum tensile strength of the joints is equivalent to 89% of that of the base material. The fracture location characteristics of the heat treated joints are similar to those of the as welded joints. The defect free joints fracture in the heat affected zone on the retreating side and the joints with a void defect fracture in the weld zone on the advancing side. All of the experimental results can be explained by the hardness profiles and welding defects in the joints.
-
Post-weld heat treatment effects on microstructure, crystal structure, and mechanical properties of donor stir–assisted friction stir welding material of AA6061-T6 alloy
Aiman H. Al-Allaq,Manish Ojha,Yousuf S. Mohammed,Srinivasa N. Bhukya,Zhenhua Wu,Abdelmageed A. Elmustafa
DOI: https://doi.org/10.1007/s00170-023-12407-9
IF: 3.563
2023-10-11
The International Journal of Advanced Manufacturing Technology
Abstract:Friction stir welding (FSW) technology combines heat input from friction and extreme plastic deformation to produce high-quality joints in aluminum and other alloy systems. This necessitates examining the final welded joint's mechanical and structural properties. Post-weld heat-treated AA6061-T6 alloy that resulted from the application of a Cu donor stir–assisted (CDSA) friction stir welding (FSW) material was examined for crystal structure and mechanical properties. CDSA FSW samples were tested at a constant tool rotational speed of 1400 rpm and a welding translational speed of 1 mm/s. CDSA samples of 20% and 60% thickness of the AA6061-T6 base alloy were selected to assist the FSW joining at the plunge stage. The FSW AA6061-T6 samples were solid solution treated at 540 °C for 1 h, followed by quenching in water at room temperature. The samples were then artificially aged at 180 °C for 6 h, respectively, followed by air cooling. The samples were tested for microstructure, crystal structure, chemical composition, and mechanical properties using optical microscopy, scanning electron microscopy, X-ray diffraction, and nanoindentation. The microstructure shows the additional grain refinement in the stir zone (SZ) due to recovery and recrystallization with increasing aging time. Examination of the chemical contents of the FSW AA6061-T6 alloy samples using scanning electron microscopy with energy-dispersive spectroscopy (EDS) revealed Al (parent material) as the predominant element, while Cu (CDSA) was minimally present as expected. XRD results of the CDSA FSW samples depicted crystal orientations similar to the orientations of the AA6061-T6 alloy. Nanoindentation tests revealed softening effects due to the dissolution of hardening precipitates at the SZ. The hardness of the base metal (BM), left and right regions, is reported as ~ 0.65 GPa, whereas at the SZ, the hardness is ~ 0.55 GPa at a depth of indentation of 4.7 μm.
engineering, manufacturing,automation & control systems
-
Effects of Solution Heat Treatment on Friction Stir Welding Joints of 7B04-O Aluminum Alloy
Peipei Han
DOI: https://doi.org/10.3901/JME.2015.22.035
Abstract:： The aero Al-coating 7B04-O aluminum alloy plates with the thickness of 3 mm are subjected to friction stir welding (FSW), the effect of solution heat treatment on the microstructure and tensile property of the FSW joints are investigated. The results show that, with the rotation rate of 800 r/min, the welding speed of 200 mm/min and the shoulder diameter of 12 mm, sound FSW joints with no defect are obtained. Dynamic recrystallization take place in the nugget zones(NZs) with fine and equiaxed grains generated. After the heat treatment, the abnormal growth of grain is found in both the upper and the bottom parts of the NZs, whereas the fine equiaxed grains in the center part is retained. During the tensile test, the fraction position occurs in the base metal of the welded joint. The ultimate tensile strength of the welded joint is 198 MPa, which is equal to that of the base metal. the breaking elongation is about 13.2%. After the solution heat treatment, the tensile strength and breaking elongation of the FSW joint are about 310 MPa and 11.2% respectively, and the joint fails in the NZ during the tensile test, which shows incomplete ductile fracture.
Engineering,Materials Science
-
Effect of post-weld heat treatment on double-sided friction stir welded joint of 120 mm ultra-thick SiCp/Al composite plates
Qi Qiao,Yishi Su,He Cao,Di Zhang,Qiubao Ouyang
DOI: https://doi.org/10.1016/j.matchar.2020.110668
IF: 4.537
2020-11-01
Materials Characterization
Abstract:<p>Friction stir welding (FSW) is a very promising and efficient technique in joining aluminum matrix composites (AMCs) without clear drawbacks, and post-weld heat treatment (PWHT) is a viable option to improve the mechanical properties of friction stir welded joint for heat treatable AMCs. In this work, 120 mm ultra-thick plates of 16 vol% SiCp/2014Al composites were successfully joined by double-sided FSW and subsequently friction stir welded joints were subjected to four different PWHTs (T6–25, T6–70, T4–25 and T4–70, denoting T6 or T4 heat treatment and being quenched in water at 25 °C or 70 °C after solution during heat treatment), respectively. The effect of PWHT on the distributions of microstructures and mechanical properties along the thickness direction in the nugget zone (NZ) of friction stir welded joint is investigated. For as-FSW joint, the tensile strength first decreases gradually along the thickness direction in the shoulder-affected and pin-affected regions, and then increases in the overlapping region. For T6–25 joint, the tensile strength does not vary a great deal in the shoulder-affected and pin-affected regions, and then increases slightly in the overlapping region. After T6–25 PWHT, the finer precipitates θ' are detected, aluminum grains grow up, and the tensile strength is obviously improved both in the NZ and base material attributing to the precipitation strengthening effect from finer precipitates θ'. The distributions of microstructures and mechanical properties along the thickness direction in the NZ are changed from heterogeneous distribution for as-FSW joint to nearly homogeneous distribution for T6–25 joint except in the overlapping region. After different PWHTs, the T6–25 joint shows the highest Vickers hardness in the NZ, followed by T6–70, T4–25 and T4–70 joints, and the as-FSW joint shows the lowest Vickers hardness. A comprehensive understanding can be provided for the effect of PWHT on the double-sided friction stir welded joint of thick or ultra-thick metal matrix composite plates.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing
-
Microstructure and properties of friction stir welding 6061 aluminum alloy joint
Haiyan Wang,Wenjun Qi,Deng Nong,Feiyan Zheng
DOI: https://doi.org/10.3969/j.issn.0258-7076.2010.05.002
2010-01-01
Abstract:The 6061-T4 aluminum alloy plates with the thickness of 6 mm were welded by friction stir welding. Microstructure and fractographs of the friction stir welding (FSW) joint were studied and contrasted with base metal by optical microscope (OM) and scanning electron microscope (SEM). Meanwhile, the tensile properties and microhardness at room temperature were measured. According to the experimental results, the suited parameters of friction stir welding process for 6061-T4 aluminum alloy plate were selected as follows: the rotation speed of the mixing head was 1200 r · min-1, and the speed of the workpiece feeding during welding was 300 mm · min-1. The strength and toughness of the FSW joints were equal to or close to that of the base metal under the above parameters, which provided the alloys a dependable technology for applying to key components of autos. The microstructure and properties of the weld nugget zone in the FSW joint were significantly better than other areas. The heat affected zone was the weakest part in the joint. The weld nugget zone had the highest hardness while the heat affected zone had the lowest one. The grains were refined due to the recovery and recrystallization occurred in the metal of FSW joints. The fractograph analysis indicated that fracture occurred in the heat affected zone where the grains grew larger and the microstructure was coarsened for the rotation of the mixing head and the cumulating of heat quality. The optimization results of process parameters showed that there was a certain relationship between the influence of rotation speed and welding speed on joint properties. Adjustment of the processing parameters could control the microstructure of the heat affected zone effectively and improve the properties of the joint. Grain refining was the main reason for the improvement of the FSW joint's strength and toughness.
-
The Effect of High-Temperature Deformation on the Mechanical Properties and Corrosion Resistance of the 2024 Aluminum Alloy Joint after Friction Stir Welding
Qiu Pang,Man Zhao,Zhichao Zhang
DOI: https://doi.org/10.3390/ma17122969
2024-06-17
Abstract:The 2024 aluminum alloy is one of the high-quality lightweight materials. Friction stir welding (FSW) has shown advantages in reducing welding defects and improving welding quality in 2024 aluminum alloys. Currently, the research regarding FSW joint corrosion performance is mainly about the joint without plastic deformation. However, FSW joints often need to be formed into complex shapes by plastic deformation. The influence of plastic deformation on the corrosion performance of FSW joints is the focus of scientific research. To address this problem, the effect of high-temperature deformation on the mechanical properties and corrosion behavior of 2024 aluminum alloy joints was researched. The exfoliation corrosion test, scanning electron microscopy, energy-dispersive spectroscopy, and transmission electron microscopy were employed to analyze the corrosion mechanism and microstructure. The results show that high-temperature deformation of the weld nugget zone greatly affects the mechanical properties and corrosion behavior of the FSW joint. Compared with the 0% deformation specimen, the hardness and tensile strength of the 20% deformation FSW joint increased by 32% and 21%, respectively. The FSW joint with 20% deformation shows the best mechanical properties and corrosion resistance. The number of precipitated S' phases of the FSW joint increases when the deformation increases to 20%, and the shape of the S' phase is a regular round particle shape. The dislocation density of the FSW joint increases continuously during deformation, which provides a favorable nucleation location for the S' phase.
-
Influence of multiple friction stir welding passes on the microstructure and mechanical properties of AA2024 age-hardened aluminum alloy
Sunil Kumar Yadav,Mohd Zaheer Khan Yusufzai,Sanjay Mishra,DK Singh
DOI: https://doi.org/10.1177/14644207241290196
2024-10-16
Proceedings of the Institution of Mechanical Engineers Part L Journal of Materials Design and Applications
Abstract:Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications, Ahead of Print. Friction stir welding (FSW) is a promising joining process for age-hardened aluminum alloys. However, when the process is used for welding age-hardened aluminum alloys, the hardness and joint efficiency are poor mainly because the strengthening precipitates become incoherent and/or get dissolved during the welding process. In this novel work, efforts have been made to enable the reprecipitation of the strengthening precipitates using multi-pass FSW. After producing FSW welds on AA2024 alloy, the welds have been processed by the same tool and at the same parameters several times to facilitate the reprecipitation of strengthening precipitates. As the precipitation kinetics of age-hardened aluminum alloys are temperature-dependent, a thermal imaging camera was utilized to record the temperature history during welding and subsequent cooling of the welded plates. The metallurgical examination of welded samples was carried out using optical microscopy, Scanning Electron Microscope (SEM), energy dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), and microhardness test. It was observed that grain refinement occurs continuously due to dynamic recrystallization and severe plastic deformation up to the third FSW pass, after which there is no significant change in grain size. Generally, the microhardness value was higher in the stir zone than the heat-affected zone (HAZ), and the hardness in the stir zone increased after 4 passes of FSW. SEM images show clusters of incoherent precipitates, fragmentation, precipitate dispersion, dissolution, and reprecipitation of precipitates during each subsequent pass. The identification of the precipitates was carried out using EDS and XRD analysis.
materials science, multidisciplinary
-
Improving joint performance of friction stir welded 2195-O Al–Li alloy by post-weld heat treatment and rolling deformation
Jiaxin Chen,Rong Chen,Hongfei Liao,Yuanyuan He,Peng Chen,Ye Tian,Bo Zhang,Zhiqing Zhang
DOI: https://doi.org/10.1016/j.jmrt.2024.03.009
IF: 6.267
2024-03-04
Journal of Materials Research and Technology
Abstract:Post-weld heat treatment and rolling deformation are used to improve the mechanical properties of 2195-O Al–Li alloy friction stir welding (FSW) joints, and the effects on the grain structure, precipitation behaviors, hardness distribution, and tensile performance are discussed. Microstructural characterization was conducted using scanning electron microscopy (SEM), electron backscattered diffraction (EBSD), and transmission electron microscopy (TEM). Mechanical properties were measured by hardness test and tensile test. Results show that coarse precipitates are subjected to various degrees of dissolution after FSW. Solution treatment following artificial aging (SAA) and 40% rolling deformation + SAA treatment (R40-SAA) enables the dissolution of coarse precipitates completely and precipitation of strengthening phases (T 1 and θ′) in the nugget zone (NZ), thermo-mechanically affected zone and heat-affected zone (HAZ). These strengthening precipitates have little difference in precipitation behavior after SAA and R40-SAA treatment and remain consistent across all regions, resulting in joint hardness change a little between these two joints with a homogeneous distribution. The change in precipitates leads to an increase in hardness and enhances both the SAA joint strength and the R40-SAA joint strength to 503 MPa and 528 MPa (superior to the original joints by 309 MPa and 334 MPa, respectively), respectively. The SAA joints fracture in the NZ resulting from the development of AGG, and develop an intergranular fracture morphology with an elongation of 4.2%. The R40-SAA joints have an elongation of 7.2% due to the generation of uniformly fine grains in the NZ, and fail in the HAZ exhibiting a brittle fracture mechanism.
materials science, multidisciplinary,metallurgy & metallurgical engineering
-
Microstructure and mechanical properties of friction stir welded powder metallurgy AA2024 alloy
Wei-hao Han,Pei Li,Nan Liu,Cun-guang Chen,Shi-peng Dong,Zhi-meng Guo,Fang Yang,Yan-li Sui,Alex A. Volinsky
DOI: https://doi.org/10.1007/s11771-022-4962-4
2022-03-01
Journal of Central South University
Abstract:The extruded plate of powder metallurgy AA2024 aluminum alloy was successfully solid-state joined by friction stir welding (FSW) to demonstrate potential applications in the aerospace and automotive industries. For determining the optimal processing parameters of FSW, the microstructure, mechanical properties, and fracture behavior of FSW joints were evaluated. When the processing parameters were optimized with 2000 r/min rotation speed and 100 mm/min traverse speed, high quality welds were achieved. The ultimate tensile strength yield strength and elongation of the joint can reach 415 MPa (85% of the base metal strength), 282 MPa, and 9.5%, respectively. The hardness of the joint gradually decreased from the alloy matrix to the heat-affected zone. The lowest strength and hardness appeared near the heat-affected zone because of the over-aging caused by heat flow from repeated stirring during FSW. The average grain size of the stir zone (2.15 µm) was smaller than that of the base metal (4.43 µm) and the heat-affected zone (5.03 µm), whose grains had <110> preferred orientation.
metallurgy & metallurgical engineering
-
Enhancing Tensile Properties of Pulsed CMT–MIG Welded High Strength AA2014-T6 Alloy Joints: Effect of Post Weld Heat Treatment
C. Rajendran,Tushar Sonar,Mikhail Ivanov,Ch. Sandeep,C. Shanthi,Naveen Kumar Gurajala,K. Balachandar,Jinyang Xu
DOI: https://doi.org/10.1016/j.ijlmm.2023.10.004
2024-01-01
International Journal of Lightweight Materials and Manufacture
Abstract:The main objective of this investigation is to study the effect of post weld heat treatments (PWHTs) on tensile properties, hardness, and microstructure of pulsed CMT-MIG (cold metal transfer arc – metal inert gas) welded AA20214-T6 aluminium alloy joints. The welded joints were subjected to PWHT of artificial aging (AA), solution annealing treatment (ST) and ST + aging (STA). The tensile properties and microhardness of joints were evaluated. The microstructure of joints was studied using optical (OM) and transmission electron microscope (TEM). The fractured surface of tensile specimens was analyzed using scanning electron microscope (SEM). Results showed that the tensile properties and hardness of as welded and PWHT joints are inferior compared to BM. This mainly refers to the microstructural heterogeneity in different regions of joints and softening of heat affected zone (HAZ) induced by the weld thermal cycle. The PWHTs of AA and ST did not show significant effect on tensile strength and hardness of AW joints. However, the slight reduction in elongation was observed in AA and ST joints. The STA joints showed higher joint efficiency of 71.6%, than other joints by compromising on the elongation. This refers to the greater precipitation of hardening precipitates in STA joints compared to AA and ST joints. It exhibited the higher tensile and yield strength of 326 MPa and 266 MPa and the lowest elongation of 3.8%. The STA joints showed 28.35%, 38.28% and 57.77% reduction in tensile strength, yield strength and elongation compared to base metal (BM) respectively. All the tensile specimens of joints failed in HAZ owing to the lower hardness. This refers to dissolution of precipitates in HAZ. However, the HAZ softening is less severe in STA joints than AW, AA, and ST joints.
-
Effect of Local Post Weld Heat Treatment on Tensile Properties in Friction Stir Welded 2219-O Al Alloy
Guannan Chu,Lei Sun,Caiyuan Lin,Yanli Lin
DOI: https://doi.org/10.1007/s11665-017-2998-7
IF: 2.3
2017-01-01
Journal of Materials Engineering and Performance
Abstract:To improve the formability of the aluminum alloy welds and overcome the size limitation of the bulk post weld heat treatment (BPWHT) on large size friction stir welded joints, a local post weld heat treatment method (LPWHT) was proposed. In this method, the resistance heating as the moving heat source is adopted to only heat the weld seam. The temperature field of LPWHT and its influence on the mechanical properties and formability of FSW 2219-O Al alloy joints was investigated. The evaluation of the tensile properties of FSW samples was also examined by mapping the global and local strain distribution using the digital image correlation methodology. The results indicated that the formability was improved greatly after LPWHT, while the hardness distribution of the FSW joint was homogenized. The maximum elongation can reach 1.4 times that of as-welded joints with increase the strength and the strain of the nugget zone increased from 3 to 8% when annealing at 300 °C. The heterogeneity on the tensile deformation of the as-welded joints was improved by the nugget zone showing large local strain value and the reason was given according to the dimple fracture characteristics at different annealing temperatures. The tensile strength and elongation of LPWHT can reach 93.3 and 96.1% of the BPWHT, respectively. Thus, the LPWHT can be advantageous compared to the BPWHT for large size welds.
-
A Microstructural Evaluation of Friction Stir Welded 7075 Aluminum Rolled Plate Heat Treated to the Semi-Solid State
P. Kapranos,A. Chegeni
DOI: https://doi.org/10.3390/MET8010041
2018-01-09
Abstract:Two rolled plates of 7075 aluminum alloy were used as starting material. The plates were welded using a simultaneous double-sided friction stir welding (FSW) process. One way of obtaining feedstock materials for Semi-solid processing or thixoforming is via deformation routes followed by partial melting in the semi-solid state. As both the base plate materials and the friction weld area have undergone extensive deformation specimens were subjected to a post welding heat-treatment in the semi-solid range at a temperature of 628 °C, for 3 min in order to observe the induced microstructural changes. A comparison between the microstructural evolution and mechanical properties of friction stir welded plates was performed before and after the heat-treatment in the Base Metal (BM), the Heat Affected Zone (HAZ), the Thermomechanically Affected Zone (TMAZ) and the Nugget Zone (NZ) using optical microscopy, Scanning Electron microscopy (SEM) and Vickers hardness tests. The results revealed that an extremely fine-grained structure, obtained in the NZ after FSW, resulted in a rise of hardness from the BM to the NZ. Furthermore, post welding heat-treatment in the semi-solid state gave rise to a consistent morphology throughout the material which was similar to microstructures obtained by the thixoforming process. Moreover, a drop of hardness was observed after heat treatment in all regions as compared to that in the welded microstructure.
Materials Science,Engineering
-
Influence of Weld Defects and Postweld Heat Treatment of Gas Tungsten Arc-Welded AA-6061-T651 Aluminum Alloy
Mohammad W. Dewan,M. A. Wahab,Ayman M. Okeil
DOI: https://doi.org/10.1115/1.4030333
2015-09-04
Journal of Manufacturing Science and Engineering
Abstract:Welding defects and the reduction of mechanical performances are the foremost problems for fusion welded aluminum alloys joints. The influences of weld defects and postweld heat treatment (PWHT) on tensile properties of gas tungsten arc (GTA) welded aluminum alloy AA-6061-T651 joints are investigated in this current study. All welded specimens are nondestructively inspected with phased array ultrasonic testing (PAUT) to classify weld defect and measure the projected defects area-ratio (AR). Ultimate tensile strength (UTS) decreased linearly with the increase of the size of weld defect but tensile toughness behaved nonlinearly with defect size. Depending on defect size, defective samples' joint efficiency (JE) varied from 35% to 48% of base metal's (BM) UTS. Defect-free as-welded (AW) specimens observed to have 53% and 34% JE based on UTS and yield strength (YS) of BM, respectively. PWHT was applied on defect-free welded specimens to improve tensile properties by precipitation hardening, microstructures refining, and removal of postweld residual stresses. Solution treatment (ST) (at 540 °C) followed by varying levels of artificial age-hardening (AH) time was investigated to obtain optimum tensile properties. For GTA-welded AA-6061-T651, peak aging time was 5 hr at 180 °C. PWHT specimens showed 85% JE based on UTS and up to a 71% JE based on YS of BM. However, toughness values decreased about 29% due to the presence of precipitate-free fusion zones. The experimental investigations can be used to establish weld acceptance/rejection criteria and for the design of welded aluminum alloy structures.
engineering, mechanical, manufacturing
-
Effect of post-weld heat treatment on microstructure and mechanical properties of 7055 aluminum alloy electron beam welded joint
Zheng Wang,Shaogang Wang,Chengcong Zhang,Zhiguo Wang
DOI: https://doi.org/10.1088/2053-1591/ab9cea
IF: 2.025
2020-06-01
Materials Research Express
Abstract:Abstract The spray forming 7055 aluminum alloy is welded by electron beam welding (EBW). After welding, the single solution treatments under different temperatures and then aging treatment (STA) and the stepped solution treatment and then aging treatment (SSTA) are carried out for the welded joints respectively. The effect of different post-weld heat treatment (PWHT) procedures on the microstructure and mechanical properties of welded joints is systematically investigated. Results show that, in as-welded condition, the fusion zone mainly consists of α -Al phase, and there are some precipitated phases such as Mg 32 (Al,Zn) 49 , Al 7 Cu 2 Fe, Al 2 CuMg, and a small amount of phase MgZn 2 in weld metal. After PWHT, the continuous network structures at grain boundary disappear. There are only a few isolated particle phases at grain boundary, and many ellipsoidal η ′ phases and rod-like η phases are precipitated within grains. The mechanical property of welded joint is improved after PWHT. Compared with that of in STA condition, the strengthening effect to welded joint is more obvious after SSTA. In SSTA condition, the hardness of weld zone is close to that of base metal (BM), and the tensile strength of welded joint reaches 486.2 MPa, which is 85.6% of that of BM. There are many equiaxed dimples on the tensile fracture surface, and the joint mainly presents the characteristic of ductile fracture.
materials science, multidisciplinary
-
Microstructure and microhardness of aluminium alloy friction stir welds with heat treatment
Yudong Huang,Long Wan,Zongliang Lv,Shixiong Lv,L. Zhou,J.C. Feng
DOI: https://doi.org/10.1080/13621718.2016.1152748
2016-01-01
Abstract:In this study, the Al-Mg-Si aluminium alloy with a T6 temper is self-support friction stir welded, and the effect of post-weld heat treatment on joints is investigated by detailed microstructural investigations and microhardness measurements. The hardness decreases from average 59 to 52 HV with holding time ranging from 10 to 60 minutes at temperature 723 K. With increasing holding temperature, the microhardness becomes more uniform and increases. Microhardness profiles are explained by precipitate distributions and precipitation sequences. The fine grain structure undergoes abnormal grain growth, and the degree of which depends on holding temperature and intense plastic deformation, and the biggest size is more than 1 mm.
-
Parametric effect on microstructure evolution, grain size and mechanical behaviour of friction stir butt welding of AA6061-T6 alloy
Virendra Pratap Singh,Deepak Kumar,Basil Kuriachen
DOI: https://doi.org/10.1080/01694243.2024.2303244
IF: 2.431
2024-01-20
Journal of Adhesion Science and Technology
Abstract:This study examines how friction stir welding (FSW) changes the microstructure and mechanical properties of an AA6061-T6 alloy joint. Results showed that welding speeds (WSs) affected microstructure evolution, joint impact toughness, tensile strength, and ductility. Frictional heat and deformation rate affect grain size and shape. Additionally, the agitated zone on the advancing side had substantially less precipitates than on the retreating side. Tensile strength and impact toughness increased mostly due to high angle grain boundaries (HABs) and grain refining. X-ray diffraction (XRD) results revealed that intermetallic compounds, such as Mg 2 Si, MgZn 2 , and Al 2 CuMg were formed in various regions of stir zone (SZ), whereas β(Mg 2 Si) and β′′(Mg 5 Si 6 ) were found in Si-rich zones. Impact test revealed a drop in impact energy at all set of parameters when comparing to ambient temperatures (25 °C), i.e. 23%, 20%, and 22% for sample A1 (rotational speed (RS)/WS-710/40), 15%, 24%, and 30% for sample A2 (RS/WS-710/100), and 12%, 7.5%, and 17% for sample A3 (RS/WS-710/160) at 0 °C, −20 °C, and −40 °C, respectively. The maximum joint efficiency of 74.5% was obtained for sample A3. Hardness value was also found to be higher for sample A3 in SZ due to the increase the precipitates and the dislocation densities walls and substructures.
materials science, multidisciplinary,engineering, chemical,mechanics
-
On the Effect of Quenching on Postweld Heat Treatment of Friction-Stir-Welded Aluminum 7075 Alloy
S. V. Sajadifar,G. Moeini,E. Scharifi,C. Lauhoff,S. Böhm,T. Niendorf
DOI: https://doi.org/10.1007/s11665-019-04252-3
IF: 2.3
2019-08-08
Journal of Materials Engineering and Performance
Abstract:This work focuses on the effect of postweld heat treatment (PWHT) on the mechanical properties and microstructural evolution of aluminum 7075 alloy processed via friction stir welding (FSW). FSW is known to be capable of grain refinement in the nugget zone (NZ). Two different quench media (water and air) were employed for PWHT. Regardless of the quench media, the PWHT led to the occurrence of grain growth in the NZ of the FSWed aluminum 7075 alloy. Abnormal grain growth occurred in the water quenched specimen. It is shown that ductility and strength of FSWed aluminum 7075 alloy are strongly dependent on the quenching rate. Changes in the mechanical properties and microstructure reveal that only at lower cooling rate this alloy is prone to the formation of precipitate-free zones (PFZs) in the vicinity of grain boundaries. Eventually, the PFZs deteriorate mechanical properties of this alloy.
materials science, multidisciplinary
-
Effect of post-weld heat treatment on 6156 aluminum alloy joint formed by electron beam welding
Shaogang Wang,Junke Xu,Yongpeng Wang
DOI: https://doi.org/10.1515/htmp-2022-0253
2023-01-01
High Temperature Materials and Processes
Abstract:Abstract The 6156 aluminum alloy is welded by electron beam welding, and different post-weld heat treatments (PWHTs) are carried out on the joints. The microstructure, mechanical property, and corrosion behavior of the welded joint before and after PWHT are investigated, respectively. Results show that the fusion zone is composed of columnar crystal and equiaxed grain in as-welded (AW) condition. There are mainly α-Al matrix phase, and some strengthening phases β′′(Mg 2 Si) and Q(Al 4 CuMg 5 Si 4 ) in weld metal. After PWHT, the quantity of strengthening phases in weldment is greatly increased, and their distribution is also improved. The tensile strength of welded joint is 65.8% of that of the base metal (BM) in AW condition. After the heat treatment of HT2, the strength coefficient of joint reaches 85.1%. There are many dimples on the tensile fracture surface, and the joint obviously presents the characteristic of ductile fracture. The electrochemical corrosion performance and resistance to intergranular corrosion of weldment in AW condition are higher than that of the BM. However, they are decreased to a certain extent after PWHT. Compared with that of the AW joint, the resistance to intergranular corrosion is slightly decreased after PWHT, and that of the HT2 joint is the best among them.
materials science, multidisciplinary
-
Quantitative Investigation of the Tensile Plastic Deformation Characteristic and Microstructure for Friction Stir Welded 2024 Aluminum Alloy
Z. L. Hu,X. S. Wang,S. J. Yuan
DOI: https://doi.org/10.1016/j.matchar.2012.08.007
IF: 4.537
2012-01-01
Materials Characterization
Abstract:The effect of the microstructure heterogeneity on the tensile plastic deformation characteristic of friction stir welded (FSW) 2024 aluminum alloy was investigated for the potential applications on light weight design of vehicles. The microstructure characteristics of the FSW joints, such as the grain structure, dislocation density and the distribution of precipitation, were studied by electron backscattered diffraction (EBSD) and transmission electron microscopy (TEM). The tensile deformation characteristic of the FSW joints was examined using the automatic strain measuring system (ASAME) by mapping the global and local strain distribution, and then was analyzed by mechanics calculation. It is found that the tensile deformation of the FSW joints is highly heterogeneous leading to a significant decrease in global ductility. The FSW joints mainly contain two typical deformation zones, which show great effect on the regional inhomogeneous deformation. One is the nugget zone (NZ) with a region of 8mm in width, and the other is part of the BM with a region of 10mm in width. The BM of the joints is the weakest region where the strain localizes early and this localization extends until fracture with a strain over 30%, while the strain in the NZ is only 4%. Differences in regional strain of FSW joints, which are essentially controlled by grain structure, the distribution of precipitation and dislocation density, result in decrease on the overall mechanical properties.