Abstract:Electrospun poly(lactic acid) (PLA) nanofibers would seem be poor carriers for drug delivery due totheir hydrophobicity, high crystallinity, weak mechanical strength and burst drug release due to poor compatibility with hydrophilic drugs. Thus, in this work, cellulose nanocrystals (CNC) as reinforcing agents and polyethylene glycol (PEG) as a compatibilizer to increase dispersion of both CNC and tetracycline hydrochloride (TH) in PLA matrix were successfully electrospun. The addition of CNC/PEG reduced fiber diameters, enhanced fiber uniformity, and the water contact angle was decreased from 117.3° for neat PLA to 98.0° for composite nanofibers with 10 wt% CNC/PEG. When drug-loading levels were further increased, the contact angle was decreased from 119.3° to 75.0°, and fiber diameter was decreased from 680 ± 34 nm for neat PLA with 3 wt% THs to 340 ± 17 nm for composite nanofibers with (TH 30%). More interestingly, more than 95.7% of drug contents were delivered within 1032 h, high drug loading efficiencies of composite nanofibers were more than 98%, and long-term sustained release behavior of composite nanofibers was obtained. The composite nanofibers showed good hydrophilicity and biocompatibility with MG-63 cells. Furthermore, compared to neat PLA, a 57.1% improvement in tensile strength and 240% increase in Young’s modulus were achieved for the composite nanofibers with (TH 15%). Additionally, the maximum decomposition temperature (Tmax) of the composite nanofibers with (TH 30%) was improved by 7.7 °C. The composite nanofibers with improved physical and hydrophilic properties, especially long-term drug release, showed good biocompatibility for use as a drug carrier for long-term sustained drug delivery systems and replacing the traditional medical dressings in biomedical applications.

Fabrication, Characterization and Drug Release Characteristics of Drug Loaded Poly (L-Lactic Acid) Fiber

Development of Random and Ordered Composite Fiber Hybrid Technologies for Controlled Release Functions

Fabrication and sustained release of fluorouracil-loaded biodegradable Poly(L-lactic acid)fiber scaffolds

Potential of alginate fibers incorporated with drug-loaded nanocapsules as drug delivery systems

Nanofiber Prepared by Intermittent Electrospun as Controlled Drug Delivery

The Implantable 5-Fluorouracil-loaded Poly(l-Lactic Acid) Fibers Prepared by Wet-Spinning from Suspension.

Electrospun fibers of acid-labile biodegradable polymers with acetal groups as potential drug carriers.

Encapsulating Drugs in Biodegradable Ultrafine Fibers Through Co-Axial Electrospinning

Coaxial Electrospun Poly(L‐Lactic Acid) Ultrafine Fibers for Sustained Drug Delivery

Modulating Drug Release from Short Poly(ethylene Glycol) Block Initiated Poly(L-lactide) Di-block Copolymers

Fabrication Of Biodegradable Polymer (Plga) Microstructures And Applications In Controlled Drug Delivery

Polylactic acid/silk fibroin composite hollow fibers as excellent controlled drug release systems

Preparation and characterization of electrospun PLGA/gelatin nanofibers as a drug delivery system by emulsion electrospinning.

Fabrication and Characterization of Dual Drug-Loaded Poly (Lactic-Co-glycolic Acid) Fiber-Microsphere Composite Scaffolds

Cellulose nanocrystals/polyethylene glycol as bifunctional reinforcing/compatibilizing agents in poly(lactic acid) nanofibers for controlling long-term in vitro drug release

Preparation and Characterization of Electrospun PLGA-SF Nanofibers As a Potential Drug Delivery System

Mechanism of a Long-Term Controlled Drug Release System Based on Simple Blended Electrospun Fibers

Preparation and properties of a biodegradable polymer as a novel drug delivery system

Biodegradable Hollow Fibres for the Controlled Release of Drugs

Research on novel polylactic acid/polyglycolic acid nano scaffold loaded drug system

Electrospun Core-Shell Plla Nanofiber And Its Potential For Drug Release