A Reactive Oxide Overlayer on Rh Nanoparticles During CO Oxidation and Its Size Dependence Studied by in Situ Ambient Pressure XPS
Michael Graß,Yawen Zhang,Derek R. Butcher,Jeong Young Park,Yimin Li,Hendrik Bluhm,Kaitlin M. Bratlie,Tianfu Zhang,Gábor A. Somorjai
DOI: https://doi.org/10.1002/ange.200803574
2008-01-01
Angewandte Chemie
Abstract:Reactive Oxide Gverlayer on Rh Nanoparticles during CO Oxidation and its Size Dependence Studied by In Situ Ambient Pressure XPS** Michael E. Grass, Yaw en Zhang, Derek R. Butcher, Jeong Y. Park, YiminLi, Hendrik Bluhm, Kaitlin M. Bratlie, Tianfu Zhang, and Gabor A. Somorjai* M.E. Grass, D. Butcher, Dr. J.Y. Park, Dr. Y. Li, Dr. H. Bluhm, Dr. K.M. Bratlie, Dr. T. Zhang, Prof. G.A. Somorjai. Department of Chemistry University of California, Berkeley Chemical and Materials Sciences Divisions Lawrence Berkeley National Laboratory Berkeley, C A 94720, USA Fax: (+1) 510-643-9668 E-mail: Somorjai@berkeley.edu Prof. Y. Zhang College of Chemistry and Molecular Engineering Peking University Beijing 100871, China This work was supported by the Director, Office of Science, Office of Advanced Scientific Computing Research, Office of Basic Energy Sciences, Materials Sciences and Engineering, and Chemical Sciences, Geosciences, and Biosciences Division of the U.S. Department of Energy under Contract No. DE-AC02-05CH11231. We also thank the Molecular Foundry and the Advanced Light Source, LBNL for use of their facilities and Prof. Miquel Salmeron and Dr. Zhi Liu for valuable discussions. Y.W.Z. appreciates financial aid of Huaxin Distinguished Scholar Award from Peking University Education Foundation of China. Supporting information for this article is available on the WWW under http://www.angewandte.org or from the author. CO oxidation is one of the most studied heterogeneous reactions, being scientifically and industrially important, particularly for removal of CO from exhaust streams ' and preferential oxidation for hydrogen purification in fuel cell applications' . The precious metals Ru, Rh, Pd, Pt, and Au are most commonly used for this reaction because of their high activity and stability. Despite the wealth of experimental and theoretical data, it remains unclear what is the active surface for CO oxidation under catalytic conditions for these metals. In this communication, we utilize in situ synchrotron ambient pressure X-ray photoelectron spectroscopy (APXPS) to monitor the oxidation state at the surface of Rh nanoparticles during CO oxidation and demonstrate that the active catalyst is a surface oxide, the formation of which is dependent on particle size. The amount of oxide formed and the reaction rate both increase with decreasing particle size. Many single crystal CO oxidation studies over Rh suggest that the reaction is structure insensitive and that oxide formation decreases the reaction rate.' ' However, recent advances in synthetic techniques and in situ experimentation have revealed that the oxidation state and stoichiometry of the surface oxide greatly affects CO oxidation rates.' ' At low temperatures or low O2/CO ratios, CO strongly adsorbs to the catalyst surface and inhibits 0 adsorption. At high temperatures or high 0 /CO ratios, the catalyst surface becomes saturated with O atoms and the reaction proceeds more rapidly. It has been demonstrated that small nanoparticles (NPs) of Pd' ' are more active for CO oxidation than larger particles and single crystals, while the opposite is reported in the case of Pt.' For Rh NPs, no particle size effect was observed for supported Rh catalysts,' but a strong particle size dependence was observed for CO desorption, dissociation, and transient CO oxidation over electron beam prepared Rh NPs precovered with oxygen.' For this investigation we have prepared small, polymer stabilized Rh NPs with a narrow size distribution and studied CO oxidation; polymer stabilized NP syntheses enable control of NP size, shape and/or composition for reaction studies.' ' The turnover frequency (TOF) for CO oxidation at 200 °C increases 6-fold and the apparent activation decreases from 27.9 kcal mol to 19.0 kcal mol as the particle size decreases from 11 nm to 2 nm. APXPS of 2 nm and 7 nm Rh NP films during CO oxidation near 1 Torr provides the first in situ measurement of the oxidation state of Rh NPs during CO oxidation and demonstrates that smaller particles are more oxidized than larger particles during reaction at 150 - 200 °C. A surface oxygen species is also observed during CO oxidation that is not present when heating in O2 alone, possibly indicating a unique active oxide phase on Rh NPs. This oxide phase may alter the relative bonding geometries of CO and/or O on the Rh surface, thereby lowering the activation energy for the reaction.' The synthesis of monodisperse Rh NPs by polyol reduction using polyvinylpyrrolidone (PVP) as a capping agent and Rh(acac) as a Rh precursor' was extended to smaller sizes by the addition of sodium citrate. Using this approach, Rh NPs of 3.5 nm (3.6 ± 0.5 nm), 2.5 nm (2.5 ± 0.4 nm), and 2 nm (1.9 ± 0.3 nm) were formed by increasing the amount of sodium citrate. Monolayer films of these particles were then prepared in a Langmuir-Blodgett (LB) trough and characterized with transmission electron microscopy (TEM) and XPS (Figure 1). Panels a, b, and c of Figure 1 show TEM images of the NPs with insets of size distribution histograms taken from 100 particles. Figure If shows X-ray photoelectron spectra for the Rh 3d peak of the as-synthesized (no pretreatment) particles after LB deposition onto a silicon wafer. It is clear that the ratio of oxidized Rh to reduced Rh increases as the particle size decreases. The three samples of smallRhNP(2,2.5, and 3.5 nm) LB films and two samples previously synthesized, 7 nm(7.1 ± 0.5 nm) and 11 nm (10.7 ± 0.9 nm) LB films (Figure Id and e) were tested for catalytic activity in CO oxidation by 0 in a batch reactor monitored with a gas