Abstract:Chemical stability of ferritic (Fe-Cr) alloy interconnect material was examined under anode gas atmospheres for use in solid oxide fuel cells (SOFCs). In H-2-H2O and CH4-H2O atmospheres, oxide scale layers were formed on the alloy surface. The surface morphology of the alloy was varied with forming oxide scales at 1073 K for an extended annealing time. Secondary ion mass spectrometry (SIMS) was applied to analyze the distribution of major and minor elements as a function of depth. From surface to inner alloy, the following distribution was identified: Mn, Fe rich -> Cr rich -> Si rich -> alloy bulk Al2O3 inner oxides. The parabolic growth rate constants of oxide scales (k(p)) were calculated for each atmosphere as follows: 3.76 x 10(-6) mu m(2)s(-1) for H-2-H2O and 5.23 x 10(-6) mu m(2)s(-1) for CH4-H2O. The growth rate constants were similar between these two atmospheres.

Characterization of Fe–Cr Alloys for Reduced Operation Temperature SOFCs