Abstract:Nano-scale ZrC particles were synthesized by self-propagating high-temperature synthesis (SHS) reaction from 30-40 mass% Al-Zr-C powder mixtures. The size of ZrC particles evidently reduced from similar to 160nm with a nearly spherical shape in 30 mass% Al to similar to 60 nm with a tetragonal morphology in 40 mass% Al. The reaction mechanism to form ZrC was discussed by DTA and X-ray diffraction analysis. The results revealed that ZrAl3 metastable phase was initially formed by Al-Zr reaction, and then the formation of nano-scale ZrC grain was controlled by the dissolution of C into a Zr-Al melt and the precipitation from the melt. Al in the compact serves not only as a diluent inhibiting the ZrC particle from coarsening, but also as an intermediate reactant participating in the reaction process.

Reaction Synthesis Of Nano-Scale Zrc Particulates By Self-Propagating High-Temperature Synthesis From Al-Zr-C Powder Mixtures