Abstract:The Raman scattering, electron diffraction (ED), and resistivity are measured for a nominal composition of ${\mathrm{Bi}}_{1.8}{\mathrm{Pb}}_{0.2}{\mathrm{Sr}}_{2\ensuremath{-}x}{\mathrm{CuO}}_{y}$ system. It is found that the peaks of ${A}_{lg}$ vibrational modes of the oxygen atom in a SrO layer along the c axis are broadened, the intensity is reduced, and the position of the peak shifts toward low frequency in Raman spectra as Sr content decreases. The reduction of the incommensurate modulation wavelength is observed by ED measurements with the decrease in Sr content. This suggests that the results in Raman spectra and ED are attributed to the shift of the apical oxygen in ${\mathrm{CuO}}_{6}$ octahedron induced by the decrease of Sr content in ${\mathrm{Bi}}_{1.8}{\mathrm{Pb}}_{0.2}{\mathrm{Sr}}_{2\ensuremath{-}x}{\mathrm{CuO}}_{y}$ system. The resistivity measurements show that the shift of the apical oxygen not only brings about the disappearance of superconductivity, but also induces a metal-semiconductor transition.

Zero resistance at 117 K in Bi sub 1. 6 Pb sub 0. 4 Sr sub 2 Ca sub 2 Cu sub 2+x O sub y compounds

Zero resistance at 117 K in BiPbSrCaCuO compounds

ZERO RESISTANCE AT 113 K IN THE (Bi1.9−xPbxSb0.1)Sr2Ca2Cu3Oy SYSTEM (x=0.1, 0.2, 0.3, 0.4)

Zero Resistance at 132K in the Multiphase System of Bi1.9−xPbxSb0.1Sr2Ca2Cu3Oy with X=0.3, 0.4

Superconducting Properties In Bi2-X-Ypbxsbysr2ca2co3oz (X=0,0.1, 0.3, 0.5 Y=0, 0.1)

Preparation and Superconductivity of the High-Tc Phase of Pb-doped Bi-Sr-Ca-Cu-O Superconductor

A NEW SUPERCONDUCTING PHASE IN <font>Bi-Sr-Ca-Cd-Cu-O</font> SYSTEM

PREPARATION AND SUPERCONDUCTIVITY OF SINGLE PHASE Bi1.65Pb0.35Sr2Ca2Cu3Oy WITH ZERO RESISTANCE TEMPERATURE 106.5K

Zero Resistance above 90K in Superconducting Oxide Tm-Ba-Cu-O

47 K superconductivity in Bi1.6Pb0.4Sr1.65La0.35CuOz

Effect of Bi/Pb Ratio and Annealing Temperature on T C and Formation of High- T C Phase in Bi-Pb-Sr-Ca-Cu-O Superconductor

The Superconducting Properties in Bi2−xSbxSr2Ca2Cu3Oy Compounds (x=0.05, 0.1, 0.15, 0.2)

Hole Concentration Dependence of T C in Bi 2 Sr 2 CaCu 2 O Y System

HIGH Tc SUPERCONDUCTIVITY AND SUBSTRUCTURE OF Bi-Sr-Ca-Cu-O SYSTEM

Upper Critical-Field of Bi-Pb-Sr-Ca-Cu-O System

HIGH T<sub>c</sub> SUPERCONDUCTIVITY AND SUBSTRUCTURE OF <font>Bi-Sr-Ca-Cu-O</font> SYSTEM

Thin-Films Bi(Pb)-Sr-Ca-Cu-O (tc(zero)=105k) Prepared by Ion-Beam Sputtering

Superconductivity and Phases of Leaded Bi-Ca-Sr-Cu-O System

Peculiar Property of Single Phase Bi 3 PbCa 3 Sr 3 Cu 4 O Y

Principal Factors on Tce in Pure Bi-Sr-Ca-Cu-O System

Shift of the Apical Oxygen of Thecuo6octahedron and the Superconductivity Inbi1.8…