Preparation of Different Ratio of PLGA / Β-Tricalcium Phosphate Electrospun Nanofibrous Scaffolds and Test

XIE Jiang-hui,JIA Jun,LIU Yi-han,YAN Wei,ZHANG Shao-feng

DOI: https://doi.org/10.3969/j.issn.1003-1634.2011.11.004

2011-01-01

Abstract:Objective:To prapare the different ratio of PLGA/β-tricalcium phosphate electrospun nanofibrous scaffolds and select the more suitable ratio so as to procide a basis for further research of implant.Method:The nanofiber scaffolds of PLGA/β-TCP with different component ratio(10:0,9:1,8:2,7:3,6:4,5:5) were prefabricated by electrospinning technology.The porous structure of nanofiber was observed under scanning electron microscope(SEM),and the porosity was assayed with stereometry.The materials were placed into 1 % pancreatin PBS,then degraded in vitro,measured the biodegradability of the materials.The hydrophilic of the materials was evaluated by the contact angle which measured by contact angle mater.Result:The SEM images showed that the different ratio of PLGA/β-TCP nanofibers(except 6:4 and 5:5) are smooth and uniform with the interwoven and porous morphology.The average porosity of the materials was over 80 % and the porosity of the materials(6:4 and 5:5)was over 85 %.But by SEM the fiber component of this two groups were so limited,most of them were granular and don not have the three-dimensional structure of porous scaffold;In the duration of in vitro degradation,at 7 weeks,the materials degraded completely in the material(7:3,6:4,5:5)groups.Conclusion:The different ratio of PLGA/β-tricalcium phosphate scaffold materials were prapared by electrospinning technology.The groups of 9:1,8:2 and 7:3 meet the demands of bone tissue engineering.In the duration of in vitro degradation,the degradation rate of 7:3 was better than other two groups and hence,it have potential prospect for bone implantation.