STUDY ON THE ELECTROCATALYTIC OXIDATION OF PHENOL CONTAINING WASTE WATER BY Ce DOPED Fe-Sn LOADED CLINOPTILOLITE

Li Xiaofei,Wang Dong,Wen Fuxue

DOI: https://doi.org/10.3969/j.issn.1000-3770.2013.08.016

2013-01-01

Abstract:The supported catalyst was prepared with clinoptilolite as its carrier and mixing with Fe,Sn,Ce oxide,by impregnated roasting method.The surface shape crystal structure of the catalyst was analyzed via scanning electron microscopy(SEM) and X-ray diffraction(XRD).Moreover,the catalytic properties of the catalyst in the electrical degradation of the phenol simulate wastewater were measured.The effects of catalyst dosage,current density and initial pH of solution on the degradation process of phenol were observed.The result shows obvious Fe,Sn,Ce oxide diffraction peaks,indicating that a load oxide layer was formed on the surface of the catalyst when the Fe,Sn,Ce molar ratio is 6:3:1.When the clinoptilolite was used in a 3D electro-catalytic phenol degradation system,in which the initial phenol concentration was 100 mg/L,the pH was 5,the catalyst concentration was 15 g/L,the current densit y was 42.6 mA/cm2 and the aeration amount was 0.1 m3/h,the phenol a nd total organic carbon(TOC) removal rate was 93.03% and 80.34% respectively after 60-minute electrolysis.Furthermore,the catalyst retained good catalytic activity after being utilized 6 times.Meanwhile,phenol and TOC removal rate still reaching 80.31% and 75.56%,respectively.