Relationship between Friction Properties and Friction Surface Status of C/C Composites

CHEN Qing-hua,DENG Hong-bing,XIAO Zhi-chao,SU Jun-ming,PENG Zhi-gang
2008-01-01
Abstract:The pyrocarbon structures of C/C composites were analysed on PLM.The hardness and graphitization degree of serious samples were tested,and the tribological behavior by simulating airplane normal landing condition on a MM1000 brake dynamometer was also investigated.The worn surfaces were observed with a scanning electron microscope(SEM),also the films were analysed by FTIR in order to know the relation between friction properties and friction surface status.The results indicate: specimens heat-treated at 1600℃ can not reach the best friction and wear properties for defect of carbon micro-crystallite and uncompleted film layer,which lead generation of apparent oxidation and adsorption.After heat-treated at 2650℃,continuous and dense friction layer with self-lubrication easily forms for ductility of the rough laminar(RL) pyrocarbon,but increases the effective contacting area at an extent,which increases the integrity of carbon and entire integrity of surface film layer.The specimen represents better friction and wear properties comparing with specimens A.The entire integrity of friction film further increases for specimen with resin densification,which reduces the oxidation and adsorption,and the specimen exists the best friction and wear properties.
What problem does this paper attempt to address?