Influence of Size of Fly Ash Cenosphere on the Microstructure and Property of 35% FAC/Geopolymer Matrix Composite

Wang Meirong,Jia Dechang,He Peigang,Zhou Yu

2011-01-01

Rare Metal Materials and Engineering

Abstract:Fly ash cenosphere/geopolymers matrix composite were prepared by adding fly ash cenosphere (FAC) with various sizes. The effect of the size of FAC on the microstructure, mechanical properties, thermal conductivity, density and thermal shrinkage of the composite was studied. When the diameter of FAC is increased to 306 mu m, the flexural strength, density and thermal conductivity of the composites are decreased from 28.5 MPa, 1.37 g.cm(-3) and 0.361 W.(m-K)(-1) to 6.4 MPa, 0.99 g-cm(-3) and 0.178 W.(m.K)(-1), respectively. The results of SEM indicate that FAC distributes evenly in geopolymers matrix. An amorphous phase layer with thickness of 250 nm between FAC and matrix is observed by TEM, and its chemical composition is Al9.9Si19O69.9KFe2.2 (at%). This amorphous phase layer has an effect on the decreasing of thermal conductivity. The results show that the composite which not only has low density, low thermal conductivity, and low thermoshrinking but also can meet the requirement of the mechanical properties is prepared by adding 35% FAC with diameter of 306 mu m.