Nonlinear Optical Properties of Silver Colloidal Solution by in Situ Synthesis Technique

Yan Deng,Youyi Sun,Pei Wang,Douguo Zhang,Xiaojin Jiao,Hai Ming,Qijing Zhang,Yang Jiao,Xiaoquan Sun

DOI: https://doi.org/10.1016/j.cap.2007.03.007

IF: 2.856

2008-01-01

Current Applied Physics

Abstract:The silver colloidal solutions were prepared by in situ synthesis technique in the presence of the Polymethyl Methacrylate, which was polymerized by reversible addition-fragmentation transfer. The UV–VIS spectra and transmission electron microscopy had shown the formation of sphere silver nanoparticles with average size of 10nm. Nonlinear optical properties as a function of silver concentration were studied using Z-scan technique with 13ns pulse duration at 532nm. The optical nonlinearity enhancement was observed by increasing the concentration. The third-order nonlinear susceptibility χ(3) was measured to 1.045×10−11esu when the concentration was 2.13mg/ml. Besides, the sample was founded to exhibit a shift from saturable absorption to reverse saturable absorption at higher incident laser energy. The reverse saturable absorption was observed to be responsible for the optical limiting characteristics in our experiments.