Abstract:alpha-Alumina (alpha-Al2O3), widely used as a raw material or production in advanced manufacturing industry, has attracted much attention in terms of its preparation temperature. A simple dissolution-evaporation-precipitation process was employed to obtain the amorphous Al-oxalate (AAO) precursor, serving as the starting material for the low temperature preparation of nano alpha-Al2O3. The crystalline structure and thermal behavior of the AAO were compared with commercially available aluminum hydroxide (Al(OH)(3)) powder using the X-ray powder diffraction (XRD) instrument, the thermal gravity analysis and differential scanning calorimetry (TG-DSC). The phase transition mechanism of AAO was investigated by the fourier transform infrared spectroscopy (FTIR), transmission electron microscope (TEM), scanning electron microscope (SEM), and Al-27 magic angle spinning nuclear magnetic resonance (Al-27-MAS-NMR). The DSC results indicated that AAO underwent a phase transformation at 982 degrees C. The alpha-alumina diffraction peaks appeared in AAO at 1000 degrees C, while alpha-Al2O3 phase was observed for Al(OH)(3) at 1200 degrees C. Furthermore, an absorption peak at 452 cm(-1), corresponding to Al-O bond in alpha-alumina was detected at 1000 degrees C. The proposed low-temperature preparation mechanism of alpha-alumina from AAO is as follows: four coordination Al-oxalate species entities coexist within the AAO sample; with increasing temperature, organic acid functional groups oxidize and volatilize, resulting in the formation of tetra-coordinate [AlO4], penta-coordinate [AlO5], and hexa-coordinate [AlO6] atomic groups; these atomic clusters further polymerize to form a structurally dense alpha-alumina crystal at the nano-scale (similar to 50 nm) at around 1000 degrees C. The experimental findings present a novel approach and method for the low-temperature preparation of nano-sized alumina powder. Additionally, a feasible theoretical reference for the low-temperature phase transition mechanism of amorphous Al-oxalate was provided.

Temperature-Controlled Growth of Alpha-Al2o3 Nanobelts and Nanosheets

Facile Synthesis of Hierarchical Flower-Like Γ-Alooh Films Via Hydrothermal Route on Quartz Surface

Controlled Synthesis and Characterization of 10 Nm Thick Al2O3 Nanowires

Catalysed Growth of Novel Aluminium Oxide Nanorods

Photoluminescence and Infrared Properties of Alpha-Al2o3 Nanowires and Nanobelts

Morphology-Controllable Synthesis of Carbon Nanomaterials Directly on Al2o3 Substrates, and Their Photoluminescence

Synthesis and Photoluminescence of Alpha-Al2o3 Nanowires

A Simple Hydrothermal Method to Synthesise Highly Pure Hexagonal and Rhombus Alpha-Lialo2 Nanosheets

Morphology Controllable Synthesis Of Gamma-Alumina Nanostructures Via An Ionic Liquid-Assisted Hydrothermal Route

Low Temperature Phase Transition Mechanism of Amorphous Al-oxalate to Nano Α-Alumina

Synthesis of Aluminium Borate Nanowires by Sol–gel Method

Selective Synthesis Of Alpha-Feooh And Alpha-Fe2o3 Nanorods Via A Temperature Controlled Process

Facile synthesis of nano-crystalline alpha-alumina at low temperature via an absolute ethanol sol-gel strategy

Preparation and Characterization of Alumina Nanofibers by Gas-Solid Reaction Method

Controlled growth of large-area, uniform, vertically aligned arrays of alpha-Fe2O3 nanobelts and nanowires.

Growth of Single-Crystalline Alzno Nanorods by Simple Vapor Deposition Method

Monte Carlo Study for the Growth of Alpha-Fe2o3 Nanowires Synthesized by Thermal Oxidation of Iron.

Hydrothermal synthesis of microscale boehmite and gamma nanoleaves alumina

Low-Temperature Synthesis and Nanomagnetism of Large-Area Alpha-Fe2o3 Nanobelts

Controlled Growth of Large-Area, Uniform, Vertically Aligned Arrays of α-Fe<sub>2</sub>O<sub>3</sub>Nanobelts and Nanowires

Preparation And Characterization Of Gamma-Alooh Nanotubes And Nanorods