Abstract:CuO-based catalysts are usually used for CO oxidation owing to their low cost and excellent catalytic activities. In this study, a series of metal oxide (La2O3, Fe2O3, PrO2, Sm2O3, and MnO2)-doped CuO-based catalysts with mesoporous Ce0.8Zr0.2O2 support were simply prepared by the incipient impregnation method and used directly as catalysts for CO catalytic oxidation. These mesoporous catalysts were systematically characterized by X-ray powder diffraction (XRD), N2 physisorption, transmission electron microscopy (TEM), energy-dispersed spectroscopy (EDS) mapping, X-ray photoelectron spectroscopy (XPS), and H2 temperature programmed reduction (H2-TPR). It was found that the CuO and the dopants were highly dispersed among the mesoporous framework via the incipient impregnation method, and the strong metal framework interaction had been formed. The effects of the types of the dopants and the loading amounts of the dopants on the low-temperature catalytic performances were carefully studied. It was concluded that doped transition metal oxides could regulate the oxygen mobility and reduction ability of catalysts, further improving the catalytic activity. It was also found that the high dispersion of rare earth metal oxides (PrO2, Sm2O3) was able to prevent the thermal sintering and aggregation of CuO-based catalysts during the process of calcination. In addition, their presence also evidently improved the reducibility and significantly reduced the particle size of the CuO active sites for CO oxidation. The results demonstrated that the 15CuO-3Fe2O3/M-Ce80Zr20 catalyst with 3 wt. % of Fe2O3 showed the best low-temperature catalytic activity toward CO oxidation. Overall, the present Fe2O3-doped CuO-based catalysts with mesoporous nanocrystalline Ce0.8Zr0.2O2 solid solution as support were considered a promising series of catalysts for low-temperature CO oxidation.

Mesoporous CuO–Fe2O3 composite catalysts for low-temperature carbon monoxide oxidation

Low-temperature CO Oxidation over CuO/Fe2O3 Catalysts

Preparation, Characterization and Catalytic Behavior of Nanostructured Mesoporous CuO/Ce0.8Zr0.2O2 Catalysts for Low-Temperature CO Oxidation

CeO2 nanoparticles modified by CuO nanoparticles for low-temperature CO oxidation with high catalytic activity

CuO Catalysts Supported on Porous TiO2 Microspheres for Low-Temperature CO Oxidation

CO Oxidation over Metal Oxide (La2O3, Fe2O3, PrO2, Sm2O3, and MnO2) Doped CuO-Based Catalysts Supported on Mesoporous Ce0.8Zr0.2O2 with Intensified Low-Temperature Activity

High activity of CuO/#-Fe2O3 for low temperature CO oxidation: Effect of support crystal types in catalyst design

Sequencing the CuOx Active Species for CO Preferential Oxidation at Low-Temperature over CeO2-CuO Composite Catalysts

CuO/TiO2/Ti Monolithic Catalysts for Low-Temperature CO Oxidation

Transition Metal (fe2o3, Co3O4 and NiO)-Promoted CuO-Based Α-Mno2 Nanowire Catalysts for Low-Temperature CO Oxidation

New Au/FeOx/SiO2 Catalysts Using Deposition–precipitation for Low-Temperature Carbon Monoxide Oxidation

Low-Temperature Co Oxidation Over Cuo/Co3o4 Catalysts

CuO/TiO 2 /Ti Monolithic Catalysts for Low-Temperature CO Oxidation

FeOx-Modified Ultrafine Platinum Particles Supported on MgFe2O4 with High Catalytic Activity and Promising Stability toward Low-Temperature Oxidation of CO

N-Coordinated Dual-Metal Single-Site Catalyst for Low-Temperature CO Oxidation

CO Oxidation over the Cu2O/CuO Hollow Sphere Heterojunction Catalysts with Enhanced Low-Temperature Activities

Highly Efficient Nano-octahedral Au/γ-Fe2O3 Catalyst Synthesized by Dealloying Combined with Calcination for Low-Temperature CO Oxidation

Facile synthesis of supported copper manganese oxides catalysts for low temperature CO oxidation in confined spaces

Large-scale Synthesis and Catalytic Activity of Nanoporous Cu–O System Towards CO Oxidation

Mechanistic study of low-temperature CO oxidation over CuO/Cu2O interfaces with oxygen vacancy modification

Role of the FeOx support in constructing high-performance Pt/FeOx catalysts for low-temperature CO oxidation