Crystal Growth and Characterization of Haldane Chain Compound Ni(C3h10n2)(2)No2clo4

W. Tao,L. M. Chen,X. M. Wang,C. Fan,W. P. Ke,X. G. Liu,Z. Y. Zhao,Q. J. Li,X. F. Sun
DOI: https://doi.org/10.1016/j.jcrysgro.2011.05.013
IF: 1.8
2011-01-01
Journal of Crystal Growth
Abstract:The bulk single crystals of S=1 chain compound Ni(C3H10N2)2NO2ClO4 are grown by using a slow evaporation method at a constant temperature and a slow cooling method. It is found that the optimum condition of growing large crystals is via slow evaporation at 25°C using 0.015mol Ni(ClO4)2·6H2O, 0.015mol NaNO2, and 0.03mol 1,3-propanediamine liquid dissolved into 30ml aqueous solvent. High-quality crystals with size up to 18×7.5×5 mm3 are obtained. The single crystals are characterized by measurements of X-ray diffraction, magnetic susceptibility, specific heat and thermal conductivity. The susceptibilities along three crystallographic axes are found to exhibit broad peaks at ∼55K, and then decrease abruptly to zero at lower temperatures, which is a characteristic of a Haldane chain system. The specific heat and the thermal conductivity along the c-axis can be attributed to the simple phononic contribution and are analyzed using the Debye approximation.
What problem does this paper attempt to address?