Abstract:Fe3O4 nanowire arrays with different diameters of D=50, 100, 150 and 200 nm were prepared in anodic aluminum oxide (AAO) templates by an electrodeposition method followed by heat-treating processes. A vibrating sample magnetometer (VSM) and a Quantum Design SQUID MPMS magnetometer were used to investigate the magnetic properties. At room temperature the nanowire arrays change from superparamagnetism to ferromagnetism as the diameter increases from 50 to 200 nm. The zero-field-cooled (ZFC) and field-cooled (FC) magnetization measurements show that the blocking temperature TB increases with the diameter of nanowire. The ZFC curves of D=50 nm nanowire arrays under different applied fields (H) were measured and a power relationship between TB and H were found. The temperature dependence of coercivity below TB was also investigated. Mössbauer spectra and micromagnetic simulation were used to study the micro-magnetic structure of nanowire arrays and the static distribution of magnetic moments of D=200 nm nanowire arrays was investigated. The unique magnetic behaviors were interpreted by the competition of the demagnetization energy of quasi-one-dimensional nanostructures and the magnetocrystalline anisotropy energy of particles in nanowires.

Size-dependent Melting Behavior of Zn Nanowire Arrays

Size-dependent Melting Behavior of Indium Nanowires

Melting of Ni Nanowires with and Without Oxide Capping

Size effects on the melting of nickel nanowires: a molecular dynamics study

A Molecular Dynamics Study on the Melting of Silver Nanowires

Direct Observation of Melting Behaviors at the Nanoscale under Electron Beam and Heat to Form Hollow Nanostructures.

Study on Size Effect of Melting Temperature of Pb Nanowires

Melting and recrystallizing behaviors of Bi nanowires in the pores of anodic aluminum oxide template by Joule heating

Melting Behavior of One-Dimensional Zirconium Nanowire

Size Dependence of Melting of GaN Nanowires with Triangular Cross Sections

The fabrication and characteristic properties of amorphous Co1-xZnx alloy nanowire arrays

Thermal properties of bi nanowire arrays with different orientations and diameters

Thermal expansion of Cu nanowire arrays

Size Dependent Melting Behaviors Of Nanocrystalline In Particles Embedded In Amorphous Matrix

Abnormal resistance–temperature characteristic of the melting Bi nanowires

Size effects on magnetic properties in Fe0.68Ni0.32 alloy nanowire arrays

Morphology and Field Emission from Zno Nanowire Arrays Synthesized at Different Temperature

ATOMISTIC STUDY OF THE MELTING BEHAVIOR OF Ni3Al ALLOYS: FROM NANOWIRES TO BULK

Fabrication and Magnetic Properties of Fe3O4 Nanowire Arrays in Different Diameters

MODELING THE MELTING TEMPERATURE OF METALLIC NANOWIRES

Diameter-Depended Thermal Expansion Properties of Bi Nanowire Arrays