Abstract:A series of BaSr2Sc4O9 and Ce3+-doped BaSr2Sc4O9 phosphors were synthesized via the high temperature solid state reaction. Crystal structure information on BaSr2Sc4O9 is first refined using the Rietveld method based on the XRD data, and it is assigned to the trigonal system with the R3 space-group. The photoluminescence properties were investigated in detail, including the emission and excitation spectra, site occupation, decay lifetime, thermal quenching, and quantum efficiency. There are three Ba2+/Sr2+ sites and four Sc3+ sites in this structure. The Ce3+ ions in the 6-fold coordinated Sr2+/Ba2+ sites show a near-ultraviolet-blue emission with a peak at around 407 nm under ultraviolet excitation. The Ce3+ ions in Sc3+ sites exhibit a bright broad orange-red emission with the peak at around 615 nm under near-ultraviolet and blue excitation. The energy transfer process between the different sites is demonstrated based on the spectral analysis, theoretical calculation, and decay lifetime variation. Under excitation of 345 nm, the energy transfer phenomenon and distribution of activator ions lead to the invalidation of part of the Ce3+ ions, and then it causes a higher concentration quenching point. The participation of the energy transfer in the thermal quenching phenomenon causes the abnormal intensity variation, which is ascribed to the energy compensation by the increasing energy transfer efficiency at high temperature. The internal quantum efficiency is 45% under the 420 nm excitation wavelength. An excellent white light emitting diode lamp is obtained by fabricating BaSr2Sc4O9:Ce3+ with BAM:Eu2+, β-sialon:Eu2+, and a 395 nm GaN chip; its CIE coordinate ( x, y), CCT, and Ra are (0.3708, 3463), 4023 K, and 84. These results reveal the correlation between energy transfer and luminescent property and provide a practical foundation to comprehend and adjust the photoluminescence performance.

Luminescent performance of rare earths doped CaBi2Ta 2O9 phosphor

Enhancing Red Emission of CaBi2Ta2O9: Eu3+ Phosphor by La3+ Co-Doping

Luminescence Characteristics of Dy<SUP>3+</SUP>/Eu<SUP>3+</SUP> Doped CaBi<sub>2</sub>Ta<sub>2</sub>O<sub>9</sub> Phosphors

Luminescence Properties of Eu3+ Doped CaBi2Ta2O9 Bismuth Layered-Structure Ferroelectrics

Adjustable luminescence properties of Eu3+ and Bi3+ codoped Ca3Zn3Te2O12 phosphor

Luminescence Properties of Ca2si5n8:Eu2+ Prepared by Gas-Pressed Sintering Using Baf2 As Flux and Cation Substitution

Luminescence Investigation of Eu~(3+)-Bi~(3+) Co-Doped CaMoO_4 Phosphor

Photoluminescence Properties of A Green to Red-Emitting Eu3+, Tb3+ Co-Doped Cabi2ta2o9 Ferroelectrics

Modulation and Enhancement of Red Luminescence in Ca2GdSbO6: Eu3+ Phosphor by Co-Doping with Bi3+

Luminescence properties and energy transfer of a red-emitting Ca3 (PO4)2:Sm3+, Eu3+ phosphor

Eu3+ Doped Ca3LiSbO6 and Eu3+, Li+ Co-Doped Ca3LiSbO6 Phosphors for White Light-Emitting Diodes

Effect of Fluxes on Luminescent Properties of Ca0.98Bi2Ta2O9 ∶ 0.02Pr3 +

Red Photoluminescence and Morphology of Eu3+ Doped Ca3La3(BO3)5 Phosphors

Luminescence properties and energy transfer studies in thermally stable Bi2O3: Sm3+, Eu3+ phosphor

Luminescence properties, tunable emission and energy transfer of Ca9MgLi(PO4)7:Bi3+/Eu3+ phosphor

[Synthesis and Fluorescence Properties of Rare Earth Ions Co-Doped CaMoO(4)].

Enhanced Red Luminescence of Eu3+ and R3+ -Doped La2Mo2O9 Phosphors under Blue Light Excitation

Luminescence properties of Ca<sub>2</sub>GdNbO<sub>6</sub>: Sm<SUP>3+</SUP>, Eu<SUP>3+</SUP> red phosphors with high quantum yield and excellent thermal stability for WLEDs

Enhanced red emission from BaMoO4 : Eu3+ by Bi3+ co-doping.

A Cerium Doped Scandate Broad Orange-Red Emission Phosphor and its Energy Transfer-Dependent Concentration and Thermal Quenching Character

Intense photoluminescence and mechanoluminescence of novel BaLaAl3O7:xEu3+ red nanophosphors