Synthesis of Nano ZnO Without Catalyst and the Study of Its Optical Characteristics

YANG Zhi-mei,YU Zhou,LIN Hai,WANG Shuai,ZHONG Zhi-qin,CHEN Hao,WU Zhan-wen,SUN Xiao-song,JIN Yong,HE Yi,GONG Min
DOI: https://doi.org/10.3969/j.issn.1004-5929.2006.03.016
2006-01-01
Abstract:Nano zinc oxide were grown on n-Si(111) substrate by directly evaporating high pure zinc powder without employing catalyst at 800°C in oxygen.The nano zinc-oxide were mainly tetrapod.The angles of the symbiotic T-ZnO nanowires were about 110°,the length was 1.5μm and the diameter was 100nm.Raman spectra analysis showed E_2(H) existed in different kinds of zinc oxide;photoluminescence spectroscopy(PL) study was also employed,which indicated PL of zinc oxide related to both material property and defects of impurity,blue and green emission bands were originated from defects in ZnO.