Abstract:The specific heat down to 0.08 K of the iron pnictide superconductor KFe2As2 was measured on a single-crystal sample with a residual resistivity ratio of similar to 650, with a T-c(onset) determined by a specific heat of 3.7 K. The zero-field normal-state specific heat divided by temperature, C/T, was extrapolated from above T-c to T = 0 by insisting on agreement between the extrapolated normal-state entropy at T-c, S-n(extrap) (T-c), and the measured superconducting-state entropy at T-c, S-s(meas) (T-c), since for a second-order phase transition the two entropies must be equal. This extrapolation would indicate that this rather clean sample of KFe2As2 exhibits non-Fermi-liquid behavior; i.e., C/T increases at low temperatures, in agreement with the reported non-Fermi-liquid behavior in the resistivity. However, specific heat as a function of magnetic field shows that the shoulder feature around 0.7 K, which is commonly seen in KFe2As2 samples, is not evidence for a second superconducting gap as has been previously proposed but instead is due to an unknown magnetic impurity phase, which can affect the entropy balance and the extrapolation of the normal-state specific heat. This peak (somewhat larger in magnitude) with similar field dependence is also found in a less pure sample of KFe2As2, with a residual resistivity ratio of only 90 and T-c(onset)=3.1 K. These data, combined with the measured normal-state specific heat in field to suppress superconductivity, allow the conclusion that an increase in the normal-state specific heat as T. 0 is in fact not seen in KFe2As2; i.e., Fermi-liquid behavior is observed.

Specific Heat Of The Iron-Based High-T-C Superconductor Smo1-Xfxfeas

Superconductivity and Transport Properties in Th and F Codoped Sm1-Xthxfeaso1-Yfy

Superconductivity and transport properties in Th and F codoped Sm 1-xTh xFeAsO 1-yF y

Anomalous Transport Properties and Phase Diagram of the Feas-Based Smfeaso1-Xfx Superconductors

Effect of Co Doping on Superconductivity and Transport Properties in SmFe$_{1-x}$Co$_{x}$AsO

Thermodynamic properties of Ba<sub>1−<i>x</i></sub>K<sub><i>x</i></sub>Fe<sub>2</sub>As<sub>2</sub>and Ca<sub>1−<i>x</i></sub>Na<sub><i>x</i></sub>Fe<sub>2</sub>As<sub>2</sub>

Crystal structure and phase transitions across the metal-superconductor boundary in the SmFeAsO1-xFx (0 < x < 0.20) family

Upper Critical Fields Well above 100 T for the Superconductorsmfeaso0.85f0.15withtc

Phase Diagram and Quantum Critical Point in Newly Discovered Superconductors: SmO_{1-x}F_xFeAs

Superconductivity at 57.3 K in La-Doped Iron-Based Layered Compound Sm 0.95 La 0.05 O 0.85 F 0.15 FeAs

Quantum Criticality And Superconductivity In Smfe1-Xcoxaso

Thermodynamic properties of Ba1-xMxFe2As2 (M = La and K)

Specific Heat In Kfe2as2 In Zero And Applied Magnetic Field

Specific Heat Discontinuity DeltaC vs Tc in Annealed Ba(Fe1-xCox)2As2

A large moment antiferromagnetic order in overdoped high-Tc superconductor 154SmFeAsO1-xDx

Anisotropic Structural And Magnetic Properties Of The Field-Aligned Superconducting System Smfeaso1-Xfx (X=0, 0.1, 0.2, 0.25 And 0.3)

Doping-insensitive density-of-states suppression in polycrystalline iron-based superconductor SmO$_{1-x}$F$_{x}$FeAs

Pressure Effects on the Superconducting and Spin-Density-Wave States of the Newly Discovered Sm(O1-xFx)FeAs

Superconductivity at 57.3 K in La-Doped Iron-Based Layered Compound Sm<sub>0.95</sub>La<sub>0.05</sub>O<sub>0.85</sub>F<sub>0.15</sub>FeAs

Fe-doping–induced Superconductivity in the Charge-Density-wave System 1T-Tas 2

Superconductivity at 43 K in Samarium-arsenide Oxides $SmFeAsO_{1-x}F_x$