A One-Step Approach to the Highly Efficient Preparation of Core-Stabilized Polymeric Micelles with A Mixed Shell Formed by Two Incompatible Polymers
TR Hui,DY Chen,M Jiang
DOI: https://doi.org/10.1021/ma050435c
IF: 5.5
2005-01-01
Macromolecules
Abstract:Polymeric micelles are core-shell structured nanospheres with an aggregated core being surrounded and stabilized by a hairlike shell.1,2 During past decades, polymeric micelles have attracted much attention due to their great potential applications for the use as nanocarriers for catalytic particles, molecules with electronic and photonic functions, biological and medical species, and so forth.3-9 It is well-known that the applications of the polymeric micelles mainly depend on the properties of the core and the shell.6 The changes in the structure and the composition of the core or shell will bring new properties to and further broaden the applications of the polymeric micelles.10,11 It is expected that the polymeric micelles with a mixed shell (PMMS, i.e., the hairlike shell is composed of two linear polymers), particularly when the two shell-forming polymers have distinctly different properties and the cores are stabilized, are capable of meeting various requirements in applications. For examples, the PMMS with a shell of hydrophilic/hydrophobic polymers could be soluble in water as well as in low-polarity organic solvents; the PMMS with a shell of biocompatible/chemically active (capable of being modified for targeting) polymers may be a desirable precursor for the preparation of targeting drug delivery systems.6 In the existing methods, the PMMS were prepared by micellization of an A-b-B-b-C triblock copolymer12,13 or a pair of diblock copolymers A-b-B and C-b-B in the solvent being selective for both A and C blocks,14,15 leading to B core and A/C shell.11,16 In these methods, polymers A and C should be sufficiently compatible so that A and C chains can be fully mixed in the shell of the resultant micelles.11 However, the overwhelming majority of polymers differing in chemical nature are incompatible, whereas, regarding applications, a sufficient difference in the properties between the shell-forming blocks is necessary. Besides, the micellization has to be carried out at low concentrations, and the preparation efficiency is low.17 In this paper, we describe a one-step approach to the preparation of core-stabilized PMMS with PEO/PS as the shell by directly cross-linking P2VP in PS-b-P2VP (polystyrene-block-poly(2-vinylpyridine)) and PEO-bP2VP (poly(ethylene oxide)-block-poly(2-vinylpyridine)) mixture in DMF, which is the common solvent of the block copolymers, using 1,4-dibromobutane as the crosslinker. Although the PEO chains and the PS chains are strongly incompatible,18 the cross-linking of P2VP blocks connects both the PEO and the PS chains to a common core and enables the sufficient mixing of the unlike blocks in the shell. In addition, the preparation efficiency is much higher than that of the existing methods. The block copolymers used for this study are PS-bP2VP (PS: Mn ) 23 600 g/mol, Mw ) 25 900 g/mol; P2VP: Mn ) 10 400 g/mol, Mw ) 11 500 g/mol) and PEO-b-P2VP (PEO: Mn ) 15 400 g/mol, Mw ) 16 000 g/mol; P2VP: Mn ) 14 200 g/mol, Mw ) 14 800 g/mol). DMF is the common solvent of both the PS-b-P2VP and the PEO-b-P2VP. When the two block copolymers used in this study were mixed in DMF at different compositions and at the total concentrations lower than or equal to 50.0 mg/mL, no aggregation was detected by dynamic light scattering (DLS) at room temperature. It is also demonstrated that the block copolymers are molecularly dispersed in DMF at concentrations of the copolymers of 10.0 or 50.0 mg/mL and at 100 °C since no opalescence can be observed. However, with the addition of 1,4dibromobutane in the solutions (at 100 °C), opalescence appeared gradually, indicating the occurrence of aggregation in the solutions. In this study, the weight ratio of PS-b-P2VP/PEG-b-P2VP in the solutions is fixed at 1/1 (the molar ratio is 1/1.14). The resultant aggregate solutions in DMF were diluted to the concentration of 0.1 mg/mL with DMF or 1,4-dioxane or dialyzed against water and then diluted to 0.1 mg/mL with water. These solutions at 0.1 mg/mL were characterized by DLS, and the results are listed in Table 1. As indicated in Table 1, DLS measurements demonstrate the formation of aggregates via the cross-linking reaction. We have measured the aggregates (both S1 and S2 in Table 1) in DMF at the concentrations of 10.0, 1.0, and 0.1 mg/mL by DLS and found that the dilution has little effect on the structure of the resultant aggregates. Obviously, this could be attributed to their cross-linked structure. In addition, the angular dependence of laser light scattering was investigated for S1 and S2 (in DMF at 0.1 mg/mL). The linear relation of Γ ∼ q2 (Supporting Information SI1) indicates that the micelles have an isotropic diffusive behavior and the micelles have a spherical structure.20 It has been proved that cross-linking P2VP homopolymer in DMF under the same conditions results in precipitation. In contrast, the cross-linking reaction of P2VP blocks of the copolymer mixture in DMF leads to the formation of regular aggregates, as shown by the data in Table 1. We have demonstrated that the quaternization of pyridine units cannot lead to the aggregation. The reason is that the pyridinium, which is produced by the reaction between pyridine units and the alkylogen molecules, can be well solubilized in DMF.21 Additionally, in a control experiment, when the mixture of PEO-b-P2VP and PS-b-P2VP was reacted Table 1. DLS Characterization Data of the Aggregates Produced by Cross-Linking P2VP of PS-b-P2VP and PEO-b-P2VP Mixture in DMF