Comparative Studies on Catalytic Properties of Immobilized Candida Rugosa Lipase in Ordered Mesoporous Rod-Like Silica and Vesicle-Like Silica

Guowei Zhou,Yijian Chen,Shihe Yang

DOI: https://doi.org/10.1016/j.micromeso.2008.10.013

IF: 5.876

2008-01-01

Microporous and Mesoporous Materials

Abstract:A lipase from Candida rugosa (CRL) has been immobilized in mesoporous rod-like silica and vesicle-like (or onion-like) silica supports by physical adsorption. The mesostructures and characteristics of the two mesoporous materials before and after adsorption of CRL were characterized by HRTEM, FESEM, SAXRD and N2 adsorption–desorption experiments. The pore sizes of the rod-like silica and the vesicle-like silicas were determined to be ca. 11 and 12nm, respectively, larger than enough to accommodate lipase molecules (∼4nm). The structural integrity of the rod-like silica as well as the vesicle-like silica is retained after adsorption of CRL into the mesopores. The catalytic activity, thermostability, and operational stability of the immobilized CRL were measured in phosphate buffer solution by hydrolysis of tributyrin. When the lipase immobilized in the vesicle-like silica was used as biocatalyst for hydrolysis of tributyrin in a batch process, the hydrolysis activity decreased only slightly from 74% to 60% over 10 cycles of reuse, indicating no obvious leaching out of the lipase from the round channels. The activity of vesicle-like silica immobilized CRL for catalytic hydrolysis of tributyrin is 21% and 14% higher than that of rod-like silica immobilized CRL at incubation temperature of 60°C at 30min and 90min, respectively. The results demonstrate that the lipase immobilized in vesicle-like silica is superior to the rod-like silica in terms of higher activity, reusability and thermal stability. The unique curvature and the large size of the interlamellar pores of vesicle-like silica are suggested to be possible factors in achieving the higher activity and stability. Such a distinctive mesoporous geometry of the vesicle-like silica promises technological applications in protein adsorption and catalysis.