Abstract:Using Na+ form of perfluorosulfonic acid (PFSA) and poly(vinyl alcohol) (PVA) as coating materials, polysulfone (PSf) hollow fiber ultrafiltration membrane as a substrate membrane, PFSA-PVA/PSf hollow fiber composite membrane was fabricated by dip-coating method. The membranes were post-treated by two methods of heat treatment and by both heat treatment and chemical crosslinking. Maleic anhydride (MAC) aqueous solution was used as chemical crosslinking agent using 0.5 wt % H2SO4 as a catalyst. PFSA-PVA/PSf hollow fiber composite membranes were used for the pervaporation (PV) separation of isopropanol (IPA)/H2O mixture. Based on the experimental results, PFSA-PVA/PSf hollow fiber composite membrane is suitable for the PV dehydration of IPA/H2O solution. With the increment of heat treatment temperature, the separation factor increased and the total permeation flux decreased. The addition of PVA in PFSA-PVA coating solution was favorable for the improvement of the separation factor of the composite membranes post-treated by heat treatment. Compared with the membranes by heat treatment, the separation factors of the composite membranes post-treated by both heat treatment and chemical crosslinking were evidently improved and reached to be about 520 for 95/5 IPA/water. The membranes post-treated by heat had some cracks which disappeared after chemical crosslinking for a proper time. Effects of feed temperature on PV performance had some differences for the membranes with different composition of coating layer. The composite membranes with the higher mass fraction of PVA in PFSA-PVA coating solution were more sensitive to temperature. It was concluded that the proper preparation conditions for the composite membranes were as follows: firstly, heated at 160 degrees C for 1 h, then chemical crosslinking at 40 degrees C for 3 h in 4% MAC aqueous solution. (c) 2007 Wiley Periodicals, Inc.

Sodium Alginate-Polyvinyl Alcohol/polysulfone (SA-PVA/PSF) Hollow Fiber Composite Pervaporation Membrane for Dehydration of Ethanol-Water Solution

Sodium Alginate and Poly Vinyl Alcohol Hollow Fiber Composite Membrane for Dehydration of Isopropanol

Process Design of Continuous-Flow Pervaporation Separation for Alcohol Dehydration

Polyvinyl Alcohol/polysulfone (PVA/PSF) Hollow Fiber Composite Membranes for Pervaporation Separation of Ethanol/water Solution

Enhanced Pervaporation Performance of SA-PFSA/ceramic Hybrid Membranes for Ethanol Dehydration

Preparation of PFSA/PSf hollow fiber composite membranes with recovered PFSA for the pervaporation separation of EtOH/H 2 O

Preparation of Acid-Resistant PEI/SA Composite Membranes for the Pervaporation Dehydration of Ethanol at Low Ph

Pervaporation separation of ethanol/water mixture by PPO/PSF composite membrane

Chitosan-poly (vinyl Alcohol)/poly (acrylonitrile) (CS–PVA/PAN) Composite Pervaporation Membranes for the Separation of Ethanol–water Solutions

Integral Pva-Pes Composite Membranes by Surface Segregation Method for Pervaporation Dehydration of Ethanol

Pervaporation Dehydration of Ethyl Acetate Aqueous Solution Bychitosan-Alginate/polyacrylonitrile Polyion Complex Membranes

Preparation and pervaporation performance of PVA membrane with biomimetic modified silica nanoparticles as coating

Preparation of PFSA‐PVA/PSf Hollow Fiber Membrane for IPA/H2O Pervaporation Process

Poly (vinyl Alcohol)/Cellulose Nanocomposite Pervaporation Membranes for Ethanol Dehydration

High pervaporation dehydration performance of the composite membrane with an ultrathin alginate/poly(acrylic acid)-Fe3O4 active layer

Pervaporation of Ethanol/water Mixtures by PDMS/PVDF Composite Membranes with High Permeability

Pervaporation Characteristics and Structure of Poly(vinyl Alcohol)/poly(ethylene Glycol)/tetraethoxysilane Hybrid Membranes

Acid-reinforced ionic cross-linking of sodium alginate/polyamidoamine dendrimer blended composite membranes for isopropanol dehydration through pervaporation

Pervaporation dehydration of ethyl acetate aqueous solution using the doubly modified polyvinyl alcohol (PVA) composite membrane

Pervaporation dehydration of ethanol by hyaluronic acid/sodium alginate two-active-layer composite membranes.

Designing High-Performance Pervaporation Membranes with Hierarchical Hydrophobic-Hydrophilic Coating Layers