Flammability characteristics and flame retardant mechanism of phosphate-intercalated hydrotalcite in halogen-free flame retardant EVA blends

Lei Ye,Baojun Qu

DOI: https://doi.org/10.1016/j.polymdegradstab.2008.02.002

IF: 5.204

2008-01-01

Polymer Degradation and Stability

Abstract:The flammability characteristics and flame retardant mechanism of phosphate-intercalated hydrotalcite (MgAl-PO4) in the halogen-free flame retardant ethylene vinyl acetate (EVA) blends have been studied by X-ray diffraction (XRD), Fourier transfer infrared (FTIR) spectroscopy, cone calorimeter test (CCT), scanning electron microscopy (SEM), thermogravimetric analysis (TGA), limiting oxygen index (LOI) and UL-94 tests. The results show that the hydrotalcite MgAl-PO4 intercalated by phosphate possesses the enhanced thermal stability and flame retardant properties compared with ordinary carbonate-intercalated hydrotalcite MgAl-CO3 in the EVA blends. The CCT tests indicate that the heat release rate (HRR) and mass loss rate (MLR) values of the EVA/MgAl-PO4 samples are much lower than those of the EVA/MgAl-CO3 samples. The TGA data show that the thermal degradation rates of MgAl-PO4 and EVA/MgAl-PO4 samples are much slower and leave more charred residues than those of MgAl-CO3 and its corresponding EVA blends. The LOI values of EVA/MgAl-PO4 samples are 2% higher than those of the corresponding EVA/MgAl-CO3 samples at the range of 40–60wt% loadings, while the EVA sample with 55wt% MgAl-PO4 can reach the UL-94 V-1 rating. The dynamic FTIR spectra reveal that the flame retardant mechanism of MgAl-PO4 can be ascribed to its catalysis degradation of the EVA resin, which promotes the formation of charred layers with the P–O–P and P–O–C complexes in the condensed phase. The SEM observations give further evidence of this mechanism that the compact charred layers formed from the EVA/MgAl-PO4 sample effectively protect the underlying polymer from burning.