Giant magnetoresistance, magnetostrain and magnetocaloric effects in a Cu-doped -textured Ni45Co5Mn36In13.2Cu0.8 polycrystalline alloy
Xiao-Ming Huang,Ying Zhao,Hai-Le Yan,Nan Jia,Bo Yang,Zongbin Li,Yudong Zhang,Claude Esling,Xiang Zhao,Liang Zuo
DOI: https://doi.org/10.1016/j.jallcom.2021.161652
IF: 6.2
2021-12-01
Journal of Alloys and Compounds
Abstract:Ni–Mn–Z (Z = In, Sn, and, Sb) metamagnetic shape memory alloys exhibit plenty of state-of-the-art magnetoresponsive effects owing to the magnetic-field-induced reversible martensitic transformation. For this compound, achieving high magnetization difference, large transformation entropy change, strong field dependence of transformation temperature, and low thermal hysteresis is essential to obtain significant magnetoresponsive functional properties. In this work, starting from the Ni45Co5Mn36In14 alloy, the substitution of Cu for In is introduced to optimize these properties simultaneously, giving rise to the substantial improvement in the magnetoresponsive effects. By composition design, a second-phase freed Ni45Co5Mn36In13.2Cu0.8 alloy with the phase temperature just below room temperature was selected. Using the directionally solidified technique, a strong<001>-textured sample is prepared to enhance magnetoresponsive behaviors. Measurements show that the reversible magnetoresistance and magnetic-field-induced strain of the prepared sample reach −79% and 0.24%, respectively. Moreover, a maximum isothermal magnetic entropy change of 16.0 J kg−1 K−1 and the maximum adiabatic temperature change of −3.4 K are measured under a field change of 1.5 T, showing excellent low-field magnetocaloric response. The work is expected to supply a prototype alloy of NiMn-based alloy to promote the development of magnetic shape memory alloy.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering