Biodegradable Copolyesters with Unexpected Highly Blocky Microstructures and Enhanced Thermal Properties
Xu Zhang,Yong Chen,Mengting Ye,Jing Wu,Huaping Wang
DOI: https://doi.org/10.1021/acssuschemeng.1c07993
2022-04-01
Abstract:To synthesize novel biodegradable polyesters with high heat resistance and good crystallization capability, we designed a series of aliphatic-aromatic copolyesters, i.e., poly(isoidide-2,5-dimethylene adipate-co-terephthalate)s (PIATs) based on isoidide-2,5-dimethanol (IIDML), a rigid carbohydrate-based building block. The Mn values and intrinsic viscosities of PIAT copolyesters containing up to 40 mol % aromatic moieties are in the range of 6 000–19 000 g·mol–1 and 0.5–0.87 dL·g–1, respectively. Interestingly, the products were obtained as blocky copolymers after the one-pot melt polycondensation process because of the thermodynamic equilibrium of IIDML moieties driven by the insufficient thermal stability of the IIDML moieties. In addition, all the copolyesters are semicrystalline with crystallinity from 28% to 55% and tunable Tm values ranging from 88 °C to a remarkable 189 °C. They exhibit better (bio)degradability than the same type of polyesters. This work shows that this green monomer plays a key role in balancing thermal properties (especially Tg) and (bio)degradability, and these polyesters potentially broaden the application toward, for example, fibers.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssuschemeng.1c07993.Detailed synthesis experimental conditions, 1H NMR and 13C NMR spectra of PIAT copolyesters, DSC curves of the first heating of PIAT copolyesters, PIAT50 and PIAT60 copolyesters, synthesis procedures and DSC curves of PBAT copolyesters, and 1H NMR spectra of PIAT copolyesters during the degradation test (PDF)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology