Effects of Different Pretreatments on Fiber Component Characteristics of Corn Straw
Ling ZHAO,Sen LI,Cong WANG,Min ZHANG,Shi-yan GU,Qing-yu LIU
DOI: https://doi.org/10.3969/j.issn.1000-1700.2017.02.017
2017-01-01
Abstract:In order to study the effects of 3 kinds of different pretreatment materials (biogas slurry, combined alkali and white rot fungi) on the contents and crystal structures of corn straw fiber components (cellulose, hemicellulose and lignin), the biogas slurry and corn straw were mixed by 5:2 ratio for 5d pretreatment, combined alkali (sodium hydroxide and calcium hydroxide mass ratio of 2:1) were added by the solid-liquid ratio of 1:5 for 5d pretreatment, and the proportion of 5% white rot fungus was used for the pretreatment in 10d. The structure characteristics of straw fiber before and after pretreatments were measured by using Soest (Van) fiber measurement, Fourier transform infrared spectroscopy (FTIR) and X ray diffraction (XRD). The results showed that the corn straw fiber contents decreased after each of the 3 kinds of pretreatment, the destruction degree of lignin structure of corn straw was more significant than that of biogas slurry and white rot fungus pretreatment, and the transformation of cellulose, the lignin contents were decreased by 7.73%, 16.79% and 6.92%, respectively. After different pretreatments, the crystalline structures of cellulose in corn straw were damaged to a certain degree, and crystallinity decreased by 9.3%, 12.4% and 10.9%, respectively, the cellulose crystallinity of corn straw decreased the most under combined alkali pretreatment, which was beneficial to increase the accessibility of cellulase and improve the hydrolysis efficiency of cellulose. The result of FTIR showed that there had the greatest damage to the structure of corn straw fiber components under combined alkali pretreatment methods. Thus, this research could provide a theoretical basis for more efficient and reasonable regulating pretreatment of straw biogas project.