Transparent Ni2+-doped lithium aluminosilicate glass–ceramics with broadband infrared luminescence

Gaofeng Feng,Shifeng Zhou,Jiaxing Bao,Xi Wang,Shiqing Xu,Jianrong Qiu

DOI: https://doi.org/10.1016/j.jallcom.2007.03.034

IF: 6.2

2008-01-01

Journal of Alloys and Compounds

Abstract:Transparent Ni2+-doped Li2O–Al2O3–SiO2 glass–ceramics were prepared. β-Eucryptite nanocrystals were precipitated from the glass matrix after heat-treatment. X-ray diffraction analysis revealed that the crystallite sizes were 30–40nm, and the average size increased with increasing temperature. Broadband infrared luminescence centered at around 1300nm with full width at half maximum (FWHM) of more than 300nm was observed from the Ni2+-doped glass–ceramic heat-treated at 650°C for 2h. Optical absorption spectra indicated that Ni2+ ions moved from trigonal bipyramid five-fold sites in the as-made glass to octahedral sites in the glass–ceramics at first, and then to distorted octahedral sites with increasing temperature. The blue-shift of the peak position and the intensity decrease of the infrared luminescence could be attributed to the sites change of Ni2+ ions in the glass–ceramics.