Abstract:Si3N4/BN laminated ceramics were fabricated via a processing of rolling, coating and hot pressing. Their flexure creep behaviors were examined at 1100similar to1300degreesC in air, and then compared with those of monolithic Si3N4 ceramics. The Si3N4/BN laminated ceramics exhibited a better creep resistance than their monolithic counterparts. It was supposed that the incorporation of BN interlayers improved the creep resistance of the composites by producing incompatible deformation and confining the distribution of glassy phase to planar continuity. Furthermore, the BN interlayers could influence the creep resistance of the composites by "purifying" Si3N4 grain boundaries of Si3N4 layer. Compared to those with (Al2O3+Y2O3+MgO) addition, the composites using (Al2O3+Y2O3+La2O3) system as sintering aids showed an improved creep resistance. On the basis of experimental results, the primary mechanisms of creep deformation could be mainly attributed to viscous flow of the glassy phase and grain boundary sliding.

Flexure Creep Behaviors of Si<sub>3</sub>N<sub>4</sub>/BN Laminated Ceramic Composites Produced by Rolling