Abstract:Supported metal catalysts are widely applied in electrocatalysis and heterogeneous catalysis. However, the agglomeration and/or sintering of metal nanoparticles is still a big problem, which usually causes the deactivation of these catalysts. Moreover, the inhomogeneity of the exposed facets of metal nanoparticles hinders the establishment of the structure-activity relationship of catalysts. Thus, it is crucial to develop new strategies to prepare supported metal catalysts with exposed specific metal facets that remarkably decrease the agglomeration of metal nanoparticles and achieve superior metal dispersion, especially in situations of high metal loading. In this manuscript, an ultrathin palladium layer exposed to a Pd{111} facet with an average thickness of 0.9 nm is grown on {001}-faceted anatase TiO2 nanosheets to form the TiO2(001)@Pd(111) facet composite catalyst by precise control of the reduction of palladium precursors in the presence of CO at ambient temperature under mild conditions. On one hand, well-dispersed ultrathin Pd metal with a high metal loading of similar to 31 wt % is achieved, which leads to a much larger active surface area and improved atom utilization efficiency as compared to the supported Pd nanoparticle catalyst, Pd/TiO2(001), prepared by the conventional impregnation method. On the other hand, the maximized interface contact between the ultrathin Pd layer and the TiO2 nanosheet improves the stability of the ultrathin palladium layer and downshifts the Pd d-band center. Therefore, the TiO2(001)@Pd(111) catalyst shows much higher activity, stability, and CO tolerance as compared to Pd/TiO2(001) and commercial Pd/C(Aldrich) catalysts with similar palladium loadings in the formic acid electro-oxidation reaction. This work opens up an effective strategy to synthesize highly stable and active supported ultrathin metal catalysts with exposed specific facets, which also sheds light on enhancing the stability and activity of Pd anodic catalysts in formic acid electro-oxidation.

Synthesis, characterization and catalytic activity of an ultrafine Pd/C catalyst for formic acid electrooxidation

Enhanced Electro-Oxidation of Formic Acid by a PdPt Bimetallic Catalyst on a CeO_2-modified Carbon Support

Structural Design and Facile Synthesis of a Highly Efficient Catalyst for Formic Acid Electrooxidation.

Efficient synthesis of ultrafine Pd nanoparticles on an activated N-doping carbon for the decomposition of formic acid

Pd Nanoparticles Supported on Carbon-Modified Rutile TiO2 As a Highly Efficient Catalyst for Formic Acid Electrooxidation

Carbon-Supported Pd−Pt Nanoalloy with Low Pt Content and Superior Catalysis for Formic Acid Electro-oxidation

Catalytic Performance of Pd/MWCNT on Electrochemical-oxidation of Formic Acid

Facile Synthesis of the TiO<sub>2</sub>-Supported Ultrathin Palladium Facet Composite Catalyst with Superior Metal Dispersion and Enhanced Catalytic Performance in Formic Acid Electro-Oxidation

Synthesis of Ultrathin PdCu Alloy Nanosheets Used as a Highly Efficient Electrocatalyst for Formic Acid Oxidation.

In situ synthesis of C–SiO2 enhanced Pd nanoparticles for catalytic dehydrogenation of formic acid

Synthesis and Electrocatalytic Performances for Formic Acid Electrooxidation of Hollow Pd/C catalyst

Catalytic Pd-on-Au Nanostructures with Improved Pd Activity for Formic Acid Electro-Oxidation

Clean Electrochemical Synthesis of Pd–Pt Bimetallic Dendrites with High Electrocatalytic Performance for the Oxidation of Formic Acid

Carbon Supported Pd-Pt-Cu Nanocatalysts for Formic Acid Electrooxidation: Synthetic Screening and Componential Functions

Electrocatalytic Performance of PdCo–C Catalyst for Formic Acid Oxidation

Ultrasonic-assisted Synthesis of Pd–Ni Alloy Catalysts Supported on Multi-Walled Carbon Nanotubes for Formic Acid Electrooxidation

Pd–Cu/C Electrocatalysts Synthesized by One-Pot Polyol Reduction Toward Formic Acid Oxidation: Structural Characterization and Electrocatalytic Performance

Designing Nanoporous Pd Catalyst with Dual Enhancement of Thermodynamics and Kinetics for Formic Acid Oxidation Reaction

Constructing poison-resistant Au-Pd single-atom alloy electrocatalyst on Pd nanocrystals for formic acid electrooxidation

The Influence of the Crystal Structure of TiO2 Support Material on Pd Catalysts for Formic Acid Electrooxidation

Electrocatalytic Oxidation of Formic Acid on the Carbon Supported Pd-Ni Alloy Nanoparticles