Abstract:Dating back to the late 1980s, bulk metallic glasses (BMGs) are relatively new materials that exhibit exceptional mechanical properties (strength, hardness, fracture toughness, stored elastic energy …), compared to those of most crystalline metallic alloys. Their apparent brittleness under uniaxial loading, however, is still a major obstacle to their industrialization. Moreover, BMGs often contain crystalline defects developed, intentionally or not, during their complex and delicate elaboration. These flaws are known to affect their fracture toughness and their plastic behavior. This paper reviews twenty years of works about this subject on Zr-based BMGs that may contain a low volume fraction of crystalline defects of different natures, e.g. dendrites or spherulites, depending on the synthesis method. Dedicated experimental set-ups, mainly bending tests on notched beams, were developed to create in the specimen a proper pre-crack by fatigue and then load it monotonically up to fracture. The measured fracture toughness and the fractographic observations allow to conclude that these crystalline defects facilitate pre-cracking, but result in an embrittlement that is more or less significant depending on their type. The loading mode of the crack - mode I, II or mixed - as well as the temperature were shown to play a key role in crack initiation and propagation, whether steadily or catastrophically, in the BMG. By means of finite element computations analyses, explanations on how the crystalline flaws presence can affect fracture toughness and perturbate crack growth, under mode I and mode II, were proposed. Finally, the relevance of these experimental techniques as well as the link between crystalline defects, fracture toughness and their consequences on the ductility of a structural component are discussed.

Relationship Between Fracture Toughness and Stretched Zone Width, Shear Band Length and Crack Tip Opening Displacement on Specimen Surface in Bulk Metallic Glasses

Locating bulk metallic glasses with high fracture toughness: Chemical effects and composition optimization

Tension-Tension Fatigue Behavior of High-Toughness Zr61Ti2Cu25Al12 Bulk Metallic Glass

Temperature Effect on Fracture of a Zr-Based Bulk Metallic Glass

Fracture and fatigue behaviour of a laser additive manufactured Zr-based bulk metallic glass

Pure mode II dynamic fracture characteristics and failure mechanism of Zr41.2Ti13.8Cu12.5Ni10Be22.5 bulk metallic glass

Effect of chemical composition on the fracture toughness of bulk metallic glasses

Crystalline defects in bulk metallic glasses: consequences on fracture toughness determination and ductility

Shear banding and serrated flow behaviors of high toughness Zr61Ti2Cu25Al12 bulk metallic glass under bending

Mechanical Properties of Monolithic Zr62Al8Ni13Cu17 Bulk Metallic Glass

Test sample geometry for fracture toughness measurements of bulk metallic glasses

Fatigue and fracture behavior of bulk metallic glass

Mechanical Properties,Damage and Fracture Mechanisms of Bulk Metallic Glass Materials

Tensile fracture morphologies of bulk metallic glass

Size dependence of ductile to brittle transition of Zr-based metallic glasses under multiaxial loading

Quasi-static and dynamic compressive behavior of Zr-based bulk metallic glass with yttrium addition

Compressive fracture morphology and mechanism of metallic glass

Ductile Fracture of Bulk Metallic Glass Zr 50 Cu 40 Al 10 under High Strain-Rate Loading

Enhanced mechanical properties of Zr65Cu15Ni10Al10 bulk metallic glass by simultaneously introducing surface grooves and multiple shear bands

The fracture of bulk metallic glasses

Flaw-insensitive fracture of a micrometer-sized brittle metallic glass