Nanocomposites As Anode for Lithium-Ion Battery
Xiangcheng Sun,Manu Hegde,Yuefei Zhang,Min He,Lin Gu,Yongqing Wang,Jie Shu,Pavle V. Radovanovic,Bo Cui
DOI: https://doi.org/10.1016/s1452-3981(23)07875-6
IF: 1.541
2014-01-01
International Journal of Electrochemical Science
Abstract:Nanocomposite particles of amorphous carbon-Li4Ti5O12 (C-LTO) and carbon nanotube-Li4Ti5O12 (CNT-LTO) were synthesized by solvothermal method and subsequent high-temperature calcination. X-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HR-TEM), and selected area electron diffraction (SAED) were applied to characterize the phase structure, particle morphology, and the coating structure. XRD analysis, TEM micrographs, HR-TEM images and SAED analysis revealed that both LTO particles exhibited a well- developed spinel nanocrystal structure with average sizes between 20-70 nm. The C-LTO particles exhibited roughly spherical shape coated by an amorphous carbon layer up to 10 nm in thickness. The CNT-LTO samples showed uniform square nanocrystals with edge length around 20 nm and nanoscale graphitic layers covering the surface, revealing the carbon nanotubes interconnection networks among the particle assemblies. Electrochemical studies of lithium insertion/extraction performance are evaluated by the galvanostatic charge/discharge tests, cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). Both LTO particles showed the superior initial discharge capacity of more than 200 mAh/g at 1/10C rate. The irreversible capacity of the C-LTO particles at more cycles was due to large polarization resulted from excessive carbon and possible residual precursors. The CNT-LTO particles show larger reversible capacity and enhanced electrochemical Li+ insertion/extraction kinetics at different cycling rates. The comparative structural and electrochemical analyses demonstrated that both nanoscale graphitic covering layers and the CNT interconnection networks increase the electronic conductivity and improve the kinetics rates of lithium insertion/extraction in the CNT-LTO particles.