Research of detonation products of RDX/Al from the perspective of composition
Xing-han Li,Zhi-cong Yi,Qi-jun Liu,Fu-sheng Liu,Ze-teng Zhang,Shen-yuan Hou,Xian-xu Zheng,Xu Zhang,Hong-bo Pei
DOI: https://doi.org/10.1016/j.dt.2022.11.016
IF: 4.035
2022-12-16
Defence Technology
Abstract:Aluminized explosives have excellent performance as the secondary reaction of aluminum (Al) powders will enhance pressure and temperature of detonation products. However, the equation of state (EOS) of detonation products is not well understood at present. We carried out long-time tests (about 1 ms) of a metal rod driven by detonation products of RDX, RDX/LiF and RDX/Al, and laser velocimetry (PDV) was used to record the free surface velocity of the rod. Thermochemical code DLCHEQ was successfully applied into hydrodynamic program SSS to calculate the rod driven test, and a new method was established to study EOS of detonation products and the secondary reaction of Al powders from the perspective of composition. The reliability of DLCEHQ was verified by the small deviation between the experimental rod free-surface velocity of RDX and the calculated results (<10%), which was far less than that of JWL EOS and ideal gas EOS. Endothermic process and the secondary reaction of Al powders were calibrated by calculating the rod free-surface velocity of RDX/LiF and RDX/Al, respectively. The paper showed a significant effect of the thermodynamic state of Al powders on EOS of aluminized detonation products, and conclusions different from previous studies were obtained. Firstly, temperature equilibrium between Al powders and ambient CHNO products is not always achieved due to the high vaporization enthalpy of Al. Secondly, the secondary reaction of Al in RDX/Al is complicated ( Al+H2O+NO+CO2→CO+H2+N2+Al2O3 ), which is controlled by Al content, Al reaction rate and Al heat absorption rate. Finally, endothermic process of Al powders should be a key factor to weaken the capacity of RDX/Al to do work, rather than the gas-consumption mechanism of Al reaction. The heat absorbed by Al powders is about more than half of its reaction heat, while the reaction consumes little gas.
engineering, multidisciplinary