MOLECULAR STRUCTURE EFFECT ON MELT GRAFTING OF ACRYLATES ONTO LLDPE
Jia-lin Li,Zhi-qiang Duan,Cheng Gong,Xu-ming Xie
DOI: https://doi.org/10.3724/sp.j.1105.2012.12093
2012-01-01
Acta Polymerica Sinica
Abstract:The melt grafting of acrylates onto LLDPE was investigated for monomers of GMA,HPMA, HEMA, EMA, MMA and HEA by Haake mixer. It is found that, the depolymerization would occur during the melt grafting process for the grafted acrylate oligomer chains when the temperature was higher than the ceiling temperature (T-c) of the grafted acrylate polymers, which induced the decrease in the grafting ratio of the acrylates. T-c varied with different molecular structures of acrylate monomers. The influence of the steric hindrance and the special interactions between monomers was discussed. For the monomers with hydroxyl groups (GMA,HPMA, HEMA, HEA), the larger the steric hindrance is, the lower the reaction heat, which results in the lower ceiling temperature. The monomers of MMA and EMA have no hydroxyl groups, so the reaction heat is much lower, which results in the relatively low ceiling temperature than that with hydroxyl groups. The order of the ceiling temperatures was finally suggested: T-c(HEA) > T-c(HEMA) > T-c(HPMA) approximate to T-c(GMA) > T-c(EMA, MMA). The solution polymerization in dichlorobenzene of the acrylate monomers was carried out respectively and the ceiling temperature ranges of different acrylate monomers were identified, which agreed well with the results of melt grafting. The styrene (St) was added as co-monomer to assist the grafting of acrylate monomers onto LLDPE, and the effect could be predicted by the Q-e rule. The grafting ratio of GMA,HPMA,MMA and EMA could be improved by adding St because they can copolymerize with St well and the depolymerization in melt grafting could be depressed even at high temperatures.