Ultraviolet and violet upconversion luminescence in Ho3+-doped Y2O3 ceramic induced by 532-nm CW laser
Feng Qin,Yangdong Zheng,Ying Yu,Zhemin Cheng,Pouran Sadat Tayebi,Wenwu Cao,Zhiguo Zhang
DOI: https://doi.org/10.1016/j.jallcom.2010.09.188
IF: 6.2
2011-01-01
Journal of Alloys and Compounds
Abstract:Ultraviolet and violet upconversion luminescence spectra of holmium-doped Y 2 O 3 were produced under the excitation of a compact continues-wave 532 nm solid-state laser. Emissions around 306, 362, 412, 390 and 428 nm can be assigned to the transitions of 3 D 3 → 5 I J ( J = 8, 7, 6), 5 G 4 → 5 I 8 and 5 G 5 → 5 I 8 , respectively. Power dependence and upconversion dynamics analysis demonstrated that both the energy transfer upconversion (ETU) and the excited state absorption (ESA) processes were involved in the population of 3 D 3 state via the coupled intermediate states 5 S 2 / 5 F 4 . Fluorescence spectra in the visible and infrared ranges showed that 5 G 4 and 5 G 5 states were populated by the ESA process from 5 I 6 and 5 I 7 states, respectively, while the 5 I 6 and 5 I 7 states were radiatively populated from the excited 5 S 2 / 5 F 4 states. Upconversion mechanisms have been evaluated based on a rate equation model. Keywords Holmium Upconversion Ultraviolet 1 Introduction Potential applications in environmental sciences, medicine, photolithography, material processing, and high-density optical data storage have stimulated the development of solid-state lasers working in the ultraviolet (UV) spectral range [1,2] . Frequency upconversion (UC) is one method to produce short wavelength laser, pumped with relatively longer wavelength laser through intrinsic energy level matching of certain rare-earth ions [3] . In UC process, high-lying excited states whose energy exceeds that of the pump photon are populated by multi-photon interaction processes such as excited state absorption (ESA), energy transfer upconversion (ETU) and photon avalanche (PA) [4] . Recently, generation of upconverted fluorescence by infrared (IR) lasers has attracted great interest due to the availability of inexpensive commercial IR diode lasers. However, in order to induce a single UV photon the active ion has to absorb at least three IR photons or even more [5] . Usually, with the increase of photons involved in an upconversion process, the upconversion mechanism becomes more complex and the upconversion efficiency goes down. Therefore, compared with shorter wavelength lasers, low cost IR diode laser is less efficient to induce UV upconversion emissions. Traditional visible lasers, such as argon-krypton lasers, are expensive, bulky and complex in structure. These shortcomings greatly restrict the development of such lasers for practical applications. In recent years, the development of commercial solid state Nd 3+ lasers has made significant progress. High-power and cost-effective compact 532-nm continuous wave (CW) solid state laser is now readily available. More importantly, the energy of such green laser matches well with the energy structures of trivalent holmium ions so that the green laser can resonate with the thermalized 5 S 2 / 5 F 4 states [6] . Trivalent holmium ion (Ho 3+ ) itself is a good candidate for upconversion processes because it has many long-lived intermediate metastable levels, from which excited state absorption (ESA) can take place [7,8] . There are also several high-lying metastable levels that can give rise to transitions at various wavelengths in the visible and UV regions [9] . Most upconversion studies on Ho 3+ -doped materials were mainly focused on infrared and visible regions. There are also a few papers devoted to the studies of UV and violet upconversion fluorescence under IR or red laser excitation [5,7,10,11] . Here we report the generation of blue, violet, and ultraviolet upconversion luminescence spectra in the range of 290–450 nm by the excitation of a compact continues-wave 532 nm green solid-state laser in Y 2 O 3 :Ho 3+ ceramic. The corresponding upconversion mechanisms are analyzed by means of power dependence and temporal evolution curves of upconverted fluorescence spectra in visible and infrared ranges. The proposed upconversion mechanisms are evaluated using proper rate equations. 2 Experimental procedure Yttrium (III) oxide (Y 2 O 3 ) powders doped with Ho 3+ 1 mol% were prepared by the following complex precursor method. Y(NO 3 ) 3 and Ho(NO 3 ) 3 ·6H 2 O with proportional molar ratios of cations were completely dissolved in de-ionized water by constant rate stirring at 80 °C. Subsequently, citric acid was added into the solution with 1:4 molar ratio of (Y + Ho) to citric acid. After complete dissolution, the pH of the solution was adjusted to 6.0 by the addition of ammonium hydroxide. The resulting solution was dried at 180 °C for 24 h and then transformed into a black bulk. This black bulk was calcined at 900 °C for 2 h in air to remove remained organic additives so that the nanocrystals were formed. These nanocrystals were pressed under 10 MPa pressure into a smooth and flat disk, then sintered at 1300 °C for 32 h in air to form ceramic samples. X-ray diffraction showed that the sample is in pure phase with cubic crystal structure. The ceramic sample was excited by a 532-nm laser (CLO Laser DPGL-500L), and the resulting emissions were analyzed using a medium resolution monochromator (Zolix SBP300). Florescence in the UV and visible ranges was detected by a photomultiplier tube (Zolix CR131) and in IR range by a PbS detector (Zolix DPbS2900). These detected signals were amplified and plotted on a chart recorder (Zolix DSC102). To measure the fluorescence lifetime, the CW laser was modulated by an electro-optic modulator (Leysop EM200K) with square wave modulation and the induced time-resolved curves were recorded by a digital phosphor oscilloscope (Tektronix TDS 5052). 3 Results and discussions Fig. 1 is the upconverted emission spectrum of Y 2 O 3 :Ho 3+ ceramic in the range of 290–450 nm under the excitation of a 532 nm green light laser. Five emission bands centered at 306, 362, 390, 412 and 428 nm were generated by intra-4 f electron transitions of Ho 3+ ions. Emissions around 306, 362, and 412 nm can be assigned to the transitions from 3 D 3 state to the ground state 5 I 8 and the first two excited states 5 I 7 and 5 I 6 , respectively, corresponding well to the fluorescence emissions excited by the 288 nm pumping light [9] . Peaks centered at 390 and 428 nm can be assigned to the transitions 5 G 4 → 5 I 8 and 5 G 5 → 5 I 8 of the Ho 3+ ions [5] . The energy level diagram of the Ho 3+ ion and corresponding transitions are indicated in Fig. 2 [12] . The upconversion mechanisms for trivalent holmium ion pumped by the 532-nm laser are proposed as illustrated in Fig. 2 . Ho 3+ ions in the ground state are pumped to the thermalized 5 S 2 / 5 F 4 states by ground state absorption (GSA) process. Subsequently the 3 D 3 state is populated by way of either ETU or ESA process utilizing the 5 S 2 / 5 F 4 states as the intermediate level, which then produces 306, 362, and 412-nm luminescence. The 5 G 4 and 5 G 5 states are populated by ESA processes from the 5 I 6 and 5 I 7 states resulting in the 390 and 428-nm emissions, respectively. In order to identify the ESA processes from low excited states, the population situation of these states needs to be investigated. For this purpose, the fluorescence spectra under the single green laser irradiation are measured. Fig. 3 is the recorded spectrum in the visible range. Emissions peaked at 550 and 760 nm can be assigned to transitions from the thermalized levels 5 S 2 / 5 F 4 to the ground state 5 I 8 and the first excited state 5 I 7 , respectively. The relatively weaker luminescence around 660 nm in the inset of Fig. 3 corresponds to the 5 F 5 → 5 I 8 transition. As illustrated in Fig. 3 , the emission from 5 F 5 level (660 nm) is so weak compared with the 5 S 2 / 5 F 4 → 5 I 7 transition (760 nm) that the population of such level could be neglected. That is to say, the probability of normally radiationless relaxation from the 5 S 2 / 5 F 4 states to 5 F 5 state is greatly decreased due to the resonating nature of the pumping green light with the coupled 5 S 2 / 5 F 4 states in the Y 2 O 3 ceramic. Additionally, the significant luminescence around 760 nm indicates that the 5 I 7 state could be directly populated by the thermalized 5 S 2 / 5 F 4 levels radiatively under the green laser excitation rather than nonradiative relaxation from the 5 F 5 state [13] . Fig. 4 shows the IR fluorescence spectrum. There are three emission bands centered at 1.03, 1.2 and 2.0 μm. The 1.03 μm emission corresponds to the 5 S 2 / 5 F 4 → 5 I 6 transition, while luminescence around 1.2 and 2.0 μm can be assigned to transitions from 5 I 6 and 5 I 7 levels to the ground state 5 I 8 , respectively. That is to say, both 5 I 6 and 5 I 7 states are populated from the excited thermalized level ( 5 S 2 / 5 F 4 ) radiatively. Therefore, considering the long-lived metastable states 5 I 6 and 5 I 7 , it is reasonable to propose that 5 G 4 and 5 G 5 states are populated by ESA processes from 5 I 6 and 5 I 7 states, respectively. To identify which multi-photon process is responsible for these upconversion emissions, the emission intensities were measured as a function of the pumping power. For an unsaturated upconversion process, the upconverted emission intensity ( I em ) depends on the pumping laser power ( I pump ) according to the following relation: (1) I em ∝ I pump n , n = 2,3 , … where n is the number of pumping photons absorbed per short wavelength photon emitted, which can be easily evaluated from the slope of the linear fit. Fig. 5 shows the logarithmic plot of the integrated emission intensities of the upconverted emissions. As illustrated in Fig. 5 , the n values are 2.1, 2.0 and 2.0 for the 306, 362, and 412-nm emission bands, respectively. Therefore, two-photon process was involved in populating the emitting state. Moreover, the same n value of the three emission peaks provides further evidence that these emissions all originate from the same state. However, the n values for the 390 and 428-nm peaks are only 1.5 and 1.2, respectively. Although the n values also suggest that 5 G 4 and 5 G 5 states are both populated by two-photon process, the relatively smaller n indicates that the populating manners for these two states are different. In order to describe the above mentioned processes, differential equations of states are proposed as following: (2a) d n 1 d t = n 3 A 31 − n 1 A 1 − σ 14 ρ n 1 , (2b) d n 2 d t = n 3 A 32 − n 2 A 2 − σ 25 ρ n 2 , (2c) d n 3 d t = σ 03 ρ n 0 − n 3 A 30 − n 3 A 31 − n 3 A 32 , (2d) d n 4 d t = σ 14 ρ n 1 − n 4 A 4 , (2e) d n 5 d t = σ 25 ρ n 2 − n 5 A 5 , where n 0 , n 1 , n 2 , n 3 , n 4 , and n 5 are the population of the 5 I 8 , 5 I 7 , 5 I 6 , 5 S 2 / 5 F 4 , 5 G 5 and 5 G 4 levels, respectively, σ ik is the absorption across section between the i and k states, ρ is the pumping energy density, and A ik is the radiative transition probability. Here we assume that linear decay dominates the 5 S 2 / 5 F 4 states, therefore, the upconversion term in Eq. (2c) is negligible. For the 5 G 5 state, under the steady-state excitation, we have (3) n 4 A 4 = n 0 σ 03 σ 14 A 31 A 30 + A 31 + A 32 ρ 2 A 1 + σ 14 ρ . When A 1 ≫ σ 14 ρ , that is to say, the main depletion mechanism for 5 I 7 state is a linear decay, n 4 A 4 ∝ ρ 2 . When A 1 ≪ σ 14 ρ , which means upconversion is dominant for 5 I 7 state, n 4 A 4 ∝ ρ . Therefore, for the 5 I 7 state, upconversion is a dominant depletion mechanism compared with the linear decay [14] . Similarly, for the 5 G 4 state, we have (4) n 5 A 5 = n 0 σ 03 σ 25 A 32 A 30 + A 31 + A 32 ρ 2 A 2 + σ 25 ρ . According to the above discussion, for the 5 I 6 state, upconversion is a depletion mechanism comparable with linear decay [14] . Such explanation is reasonable considering the long lifetimes of the 5 I 7 and 5 I 6 states which are in the order of tens of milliseconds [13] . There are two possible approaches to populate the 3 D 3 state, i.e., either ETU or ESA process utilizing the intermediate 5 S 2 / 5 F 4 states. To identify which one is the actual physical mechanism, fluorescence decays from concerned levels were measured. Typical decay curves are plotted in Fig. 6 in logarithmic scale. For the 3 D 3 state, the decay curves have been fitted to two-exponential decay law and the estimated decay times are obtained: τ 1 = 15 ± 2, τ 2 = 57 ± 3 μs for the 362 nm emission and τ 1 = 15 ± 2, τ 2 = 58 ± 3 μs for the 414 nm emission. Such results indicate that an energy transfer upconversion process is involved in populating the 3 D 3 level although the excited state absorption process cannot be ruled out. Decay curves for the emissions from 5 S 2 / 5 F 4 states are fitted to single-exponential decay law and the decay times are fitted to be 113 ± 3 and 115 ± 3 μs for the 550 and 760 nm emissions, respectively. These results confirmed that the luminescence peaked at 550 and 760 nm originate from the same excited state. In order to describe the physical mechanism of the 3 D 3 state, differential equations of corresponding states are proposed as follow: (5a) d n 3 d t = σ 03 ρ n 0 − A 3 n 3 , (5b) d n D d t = σ 3 D ρ n 3 + W n 3 2 − A D n D , where n D is the population of the 3 D 3 level, σ ik is the absorption across section between the i and k states, ρ is the pumping energy density, W is the corresponding parameter of ETU process, and A i is the radiative transition probability. We neglected the upconversion decay term for 5 S 2 / 5 F 4 states. Under steady-state excitation, stationary solutions are deduced so that (6a) n 30 = σ 03 ρ n 0 A 3 , (6b) n D 0 = σ 03 ρ 2 n 0 A D A 3 σ 3 D + W σ 03 n 0 A 3 . For decay processes, there are no pump terms in the above equations, thus we could get the following solutions from Eq. (5): (7a) n 3 = n 30 exp ( − A 3 t ) , (7b) n D = C 1 exp ( − A D t ) + C 2 exp ( − 2 A 3 t ) , with the initial conditions n 3 ( t = 0) = n 30 and n D ( t = 0) = n D 0 . Here the integral parameters are calculated to be C 1 = ( σ 01 ρ 2 n 0 / A 3 A D )( σ 12 − (2 Wσ 01 n 0 /( A D − 2 A 3 ))) and C 2 = ( W σ 01 2 ρ 2 n 0 2 / A 3 2 ( A D − 2 A 3 ) ) , respectively. According to above analyses, the two-exponential decay curves of 3 D 3 state can be interpreted as follows: the fast decay ( τ 1 ) corresponds to the radiative lifetime of 3 D 3 state, i.e., τ D 1 = 1/ A D = τ D ; the slow decay ( τ 2 ) is caused by the energy transfer upconversion process from the pumped thermalized levels 5 S 2 / 5 F 4 , whose decay time is twice of the slow decay time ( τ 2 ), i.e., τ D 2 = 1/2 A 3 = τ 3 /2. This means that the 3 D 3 state could be populated by the ETU process. However, the ESA process cannot be ruled out because the signs of C 1 and C 2 are both positive. If there is no ESA process, the σ 12 term will not exist so that the sign of C 1 should be opposite to that of C 2 , and this does not agree with our experiment results. Based on the arguments above, we propose the following upconversion mechanisms for trivalent holmium ion pumped by a 532-nm laser: Ho 3+ ion in the ground state is pumped to the 5 S 2 / 5 F 4 states by the GSA process. Then, the excited 5 S 2 / 5 F 4 states populate the 5 I 6 and 5 I 7 states radiatively, and subsequently, the ESA processes take place from these two levels, resulting in the population of the 5 G 4 and 5 G 5 states, which are responsible for the 390 and 428-nm emissions, respectively. Meanwhile, the 3 D 3 state of Ho 3+ ion, which is responsible for the 306, 362, and 412-nm luminescence, is populated by both the ETU and ESA processes, using the thermalized 5 S 2 / 5 F 4 states as the intermediate state. 4 Conclusion In this paper, we report the observation of ultraviolet and violet upconversion luminescence in Y 2 O 3 :Ho 3+ (1 mol%) ceramic under the excitation of a 532 nm CW green laser. The emissions peaked at 390 and 428 nm are originated from the 5 G 4 and 5 G 5 states, which are populated by ESA processes from two long-lived low excited states. This process is identified experimentally by power dependent curves and explained by a steady state rate equation model. The luminescence spectra around 306, 362, and 412 nm are originated from the 3 D 3 state, which is populated by both the ETU and ESA processes. Such populating approaches are identified based on fluorescence decay curves and analyzed by a time dependent rate equation model. Acknowledgment This work was financially supported by the 863 Hi-Tech Research and Development Program of the People's Republic of China. References [1] X. Zhang C. Serrano E. Daran F. Lahoz G. Lacoste A. Muñoz-Yagüe Phys. Rev. B 62 2000 4446 [2] C.L. Pope B.R. Reddy S.K. Nash-Stevenson Opt. Lett. 22 1997 295 [3] L.F. Johnson H.J. Guggenheim Appl. Phys. Lett. 19 1971 44 [4] M.-F. Joubert Opt. Mater. 11 1999 181 [5] X.X. Luo W.H. Cao Mater. Lett. 61 2007 3696 [6] K.L. Nash R.C. Dennis N.J. Ray J.B. Gruber D.K. Sardar J. Appl. Phys. 106 2009 [7] F. Lahoz I.R. Martin J.M. Calvilla-Quintero Appl. Phys. Lett. 86 2005 [8] M. Malinowski A. Wnuk Z. Frukacz G. Chadeyron R. Mahiou S. Guy M.F. Joubert J. Alloys Compd. 323 2001 731 [9] M. Malinowski M. Kaczkan A. Wnuk M. Szuflinska J. Lumin. 106 2004 269 [10] D.Y. Wang Y. Min W.P. Zhang D. Ning Y.S. Zhang S.D. Xia J. Alloys Compd. 361 2003 1 [11] M. Kaczkan M. Malinowski J. Alloys Compd. 380 2004 201 [12] M. Malinowski R. Piramidowicz Z. Frukacz G. Chadeyron R. Mahiou M.-F. Joubert Opt. Mater. 12 1999 409 [13] M. Malinowski Z. Frukacz M. Szuflinska A. Wnuk M. Kaczkan J. Alloys Compd. 300 2000 389 [14] M. Pollnau D.R. Gamelin S.R. Lüthi H.U. Güdel Phys. Rev. B 61 2000 3337
What problem does this paper attempt to address?
-
Strong Dependence of Upconversion Luminescence on Doping Concentration in Holmium and Ytterbium Co-Doped Y 2 O 3 Phosphor
Wei Xiantao,Li Yong,Cheng Xuerui,Chen Yonghu,Yin Min
DOI: https://doi.org/10.1016/s1002-0721(10)60493-0
2011-01-01
Abstract:Under the excitation of 980 nm diode laser, intense green emission (5F4+5S2-5I8) of Ho3+ was observed in Ho3+ and Yb3+ co-doped cubic Y2O3. The doping concentration and laser power dependence of the upconverted emission were studied. The decay curves of 5F4+5S2 emission of Ho3+ under the excitation of 355 nm pulse laser were measured to investigate the energy transfer process between Ho3+ and Yb3+. The results indicated that two-photon process was responsible for the upconversion (UC) emission. The Ho3+ concentration of 0.04 mol.% and the Yb3+ concentration of 5 mol.% were determined to be the best value for the strongest Ho3+ emission under the excitation of 980 nm light. The cross-relaxation between two neighboring Ho3+ ions and the back energy transfer from Ho3+ to Yb3+ were important factors for determin- ing the optimal doping concentration. This material was a promising candidate for the application in biomedical fluorescent labels for the intense green emission upon excitation of near-infrared (NIR) light.
-
Fabrication and luminescent properties of holmium doped Y2Zr2O7 transparent ceramics as new type laser material
Yucheng Ye,Zhe Tang,Zhuang Ji,Hongyi Xiao,Yurong Liu,Yichu Qin,Lexing Liang,Jianqi Qi,Tiecheng Lu
DOI: https://doi.org/10.1016/j.optmat.2021.111643
IF: 3.754
2021-11-01
Optical Materials
Abstract:Via a vacuum sintering method, highly transparent Ho: Y2Zr2O7 ceramics with different holmium doping concentrations were successfully fabricated for the first time. Y1.99Ho0.01Zr2O7 and Y1.98Ho0.02Zr2O7 transparent ceramics exhibit the highest in-line transmittance at 72% in the visible (Vis) region and over 75% in the near infrared (NIR) region. The microstructure and crystal structure of Ho: Y2Zr2O7 transparent ceramics were fully investigated by SEM and XRD measurements. Photoluminescence spectra demonstrated that Ho: Y2Zr2O7 ceramics can be effectively excited at 376 nm and 460 nm. Strong green (centered at 551 nm) and NIR (centered at 1111 nm) emissions were observed in the downshifting (DS) luminescence. Meanwhile, same green emissions have been observed in the upconversion (UC) luminescence. The luminescence decay curves have also been studied, demonstrating that the longest average fluorescence lifetime of Ho: Y2Zr2O7 transparent ceramics reaches 48 μs. Combined with the high temperature resistance and good mechanical strength of Y2Zr2O7 transparent ceramics, these results suggest that Ho3+: Y2Zr2O7 transparent ceramics are able to generates both down and up converted fluorescence.
materials science, multidisciplinary,optics
-
Ultraviolet and visible upconversion luminescence of Tm(0.1)Yb(5):FOV oxyfluoride nanophase vitroceramics
XiaoBo Chen,ZengFu Song,JinGuang Wu,N. Sawanoboi,M. Ohtsuka,YongLiang Li,Jing Zhou,Ce Wang,JinYing Liu,Qiang Tian,Ping Sun,HongMei Jing
DOI: https://doi.org/10.1007/s11433-008-0183-6
2008-01-01
Abstract:The ultraviolet upconversion luminescence of Tm 3+ ions sensitized by Yb 3+ ions in oxyfluoride nanophase vitroceramics when excited by a 975 nm diode laser was studied. An ultraviolet upconversion luminescence line positioned at 363.6 nm was found. It was attributed to the fluorescence transition of 1 D 2 → 3 H 6 of Tm 3+ ion. Several visible upconversion luminescence lines at 450.7 nm, (477.0 nm, 462.5 nm), 648.5 nm, (680.5 nm, 699.5 nm) and (777.2 nm, 800.7 nm) were also found, which result respectively from the fluorescence transitions of 1 D 2 → 3 F 4 , 1 G 4 → 3 H 6 , 1 G 4 → 3 F 4 , 3 F 3 → 3 H 6 and 3 H 4 → 3 H 6 of Tm 3+ ion. The careful measurement and analysis of the variation of upconversion luminescence intensity F as a function of the 975 nm pumping laser power P prove that the upconversion luminescence of 1 D 2 state is partly a five-photon upconversion luminescence, and the upconversion luminescence of 1 G 4 state and 3 H 4 state are respectively the three-photon and two-photon upconversion luminescence. The theoretical analysis suggested that the upconversion mechanism of the 363.6 nm 1 D 2 → 3 H 6 upconversion luminescence is partly the cross energy transfer of { 3 H 4 (Tm 3+ ), 3 F 4 (Tm 3+ ), 1 G 4 (Tm 3+ )→ 1 D 2 (Tm 3+ )} and { 1 G 4 (Tm 3+ )→ 3 F 4 (Tm 3+ ), 3 H 4 (Tm 3+ )→ 1 D 2 (Tm 3+ )} between Tm 3+ ions. In addition, the upconversion luminescence of 1 G 4 and 3 H 4 state results respectively from the sequential energy transfer { 2 F 5/2 (Yb 3+ )→ 2 F 7/2 (Yb 3+ ), 3 H 4 (Tm 3+ )→ 1 G 4 (Tm 3+ )} and { 2 F 5/2 (Yb 3+ ) → 2 F 7/2 (Yb 3+ ), 3 F 4 (Tm 3+ )→ 3 F 2 (Tm 3+ )} from Yb 3+ ions to Tm 3+ ions.
-
Yb3+ion Cooperative Upconversion Luminescence of Oxyfluoride Vitroceramics
XB Chen,MX Li,ZF Song,GW Wang,ZC Ying
DOI: https://doi.org/10.1117/12.461658
2002-01-01
Abstract:Upconversion luminescence of Yb3+-doped and Yb3+HO3+-Codoped oxyfluoride vitroceramics when excited by a diode laser operating at a wavelength of 960 nm is investigated. A strong 479-nm upconversion cooperative radiation luminescence, attributed to the coupled states of Yb 3'Yb 31CIUSters, is discovered. This result suggests an interesting and effective path to achieve compact blue upconversion luminescence. The presence of holmium in the Yb3+HO3+-codoped oxyfluoride vitroceramics substantially reduces intensity of the cooperative upconversion luminescence.
-
Down conversion and efficient NIR to visible up-conversion emission analysis in Ho3+/Yb3+ co-doped tellurite glasses
Sharafudeen Kaniyarakkal,Rajesh Dagupati,Yang Li,Zhi Chen,Vijayakumar Sadasivan Nair,Shiju Edappadikkunnummal,Kesavulu Culala Rajasekharaudayar
DOI: https://doi.org/10.1016/j.bsecv.2023.01.002
IF: 3.483
2023-01-01
Boletín de la Sociedad Española de Cerámica y Vidrio
Abstract:A series of glasses with chemical composition (50−x−y) TeO2–30ZnO–10YF3–10NaF–xHo2O3–yYb2O3 (x =0.5 and y =0.5, 1.0, 3.0, 5.0mol%) were prepared by melt-quenching procedure. The absorption spectra, excitation, down conversion emission spectra, up-conversion (UC) emission spectra and decay time measurements were analyzed. In down conversion visible emission transition intensity, associated with 5F4 → 5I8 (547nm), 5F5 → 5I8 (657nm), and 5F4 → 5I7 (755nm) of Ho3+ ions decreased with Yb3+ concentration since energy transfer (ET) process from Ho3+ to Yb3+ ions. In up-conversion, on exciting with 980nm diode laser beam, we observed a strong green (543nm) and red (657nm) UC emissions, that refers to the energy level transitions; 5F4 (5S2)→ 5I8 and 5F5 → 5I8 of Ho3+.The influence of excitation power on UC intensities studies, shown that the population at 5F4 (5S2) and 5F5 levels of Ho3+ ion occurs due to two-photon absorption process associated energy transfer from Yb3+ to Ho3+. The influence of Yb3+ doped concentration on UC was studied, and it is observed that both the green and red UC intensities improved significantly on increasing Yb3+ doped concentration.
materials science, ceramics
-
[Upconversion and Mid-Infrared Fluorescence Properties of Ho3+/Yb3+ Co-Doped 50Sio2-50Pbf2 Glass Ceramic].
Zhang Xiao-guang,Ren Guo-zhong,Yang Huai
DOI: https://doi.org/10.3964/j.issn.1000-0593(2014)08-2060-05
2014-01-01
Spectroscopy and spectral analysis
Abstract:In the present paper, the upconversion and mid-infrared fluorescence properties of Ho3+/Yb3+ co-doped 50SiO2- 50PbF2 glass ceramic (GC) were studied. The GC has the following composition (in mol%): 50SiO2-50PbF2-1YbF3-0. 5HoF3. The mixtures of about 10 g were placed in a corundum crucible and melted at 1000 degrees C for 15 min in a SiC electric furnace in air and then poured on a brass plate. The GCs were obtained just by heat treatment at 450 degrees C. The X-ray diffraction pattern of the GC indicates that very small size crystals were precipitated in the precursor glass by heat treatment. The GCs have as high transmittance as glasses. The GCs have higher absorption cross section and narrower absorption peaks compared to the corresponding glasses, indicating that fluoride is doped with Ho ions. The Judd-Ofelt intensity parameters were determined from the absorption spectrum and Judd-Ofelt theory. The omega2 value is 0.17 x 10(-20) cm2 lower than that of fluoride glass ZBLA (2.28 x 10(-20) cm2), because of Ho3+ doping in PbF2 microcrystal. The intense green upconversion light was observed in Ho3+/Yb3+ co-doped 50SiO2-50PbF2 GCs excited by 980 nm laser diode. A main emission band centered around 540 nm (green), and three week emission bands centered around 420 nm(violet), 480 nm (blue), and 650 nm (red) which correspond to the Ho3+ : ((5)F4-->(5)I8) ((5)G-->(5)I8), ((8)K3--(5)I8) and ((5)F5-->(5)I8) transitions, respectively, were simultaneously observed in GCs. Compared with the glass sample, GCs have significantly intension in the green and blue upconversion fluorescence, and not significant change in the red upconversion fluorescence. Those changes are because that Ho ion in GCs locates in lower phonon energy environment than in glasses. Lower phonon energy can make the nonradiative relaxation rate reduce, which improves the green light upconversion efficiency, at the same time reduces the population of the intermediate energy level ((5)I7) of the red light radiation. The 2.9 microm mid-infrared light was observed in GC sample, but not in glass precursor excited by 980 nm laser diode.
-
Optical, vibrational, and photoluminescence properties of holmium‐doped boro‐bismuth‐germanate glasses
Mamilla Rathaiah,Rallapalli Ravanamma,Nirlakalla Ravi,Kummara Venkata Krishnaiah,Kagola Upendra Kumar,Nallabala Nanda Kumar Reddy,Bangaram Naga Kiran,Chinnappa
DOI: https://doi.org/10.1002/bio.4822
IF: 2.613
2024-07-19
Luminescence
Abstract:The optical, vibrational, and photoluminescence properties of Ho3+‐doped boro‐bismuth‐germanate glasses were studied. Upon 450 nm excitation, intense green emission around 550 nm was observed in low Ho3+‐doped glasses, whereas high Ho3+ doping leads to the concentration quenching effect; the reasons behind the quenching of emission intensity and decay time of 5S2 + 5F4 (Ho3+) level have been discussed. The studied glasses could be a good choice for display devices and green emission applications. Holmium (Ho3+)‐doped boro‐bismuth‐germanate glasses having the chemical composition (30‐x)B2O3 + 20GeO2 + 20Bi2O3 + 20Na2O + 10Y2O3 + xHo2O3, where x = 0.1, 0.5, 1.0, and 2.0 mol% were prepared by melt‐quenching technique. The prepared glasses were examined for thermal, optical, vibrational, and photoluminescent properties. The prepared glasses were found to be thermally very stable. The optical bandgap and Urbach energies of 0.1 mol% Ho2O3‐doped boro‐bismuth‐germanate glass were calculated to be 3.3 eV and 377 MeV, respectively, using the absorption spectrum. The Judd–Ofelt analysis was performed on the 0.1 mol% Ho2O3‐doped glass and compared the obtained parameters with literature. The branching ratio (β) and emission cross‐section (σem) of the green band were determined to be 0.7 and 0.24 × 10−20 cm2, respectively. Under 450 nm excitation, a strong green emission around 550 nm was observed and assigned to the (5S2 + 5F4) → 5I8 (Ho3+) transition. Upon an increase of Ho2O3 content from 0.1 to 2.0 mol%, the intensities of all observed emission bands as well as decay time of the (5S2 + 5F4) → 5I8 transition have been decreased gradually. The reasons behind the decrease in emission intensity and decay time were discussed. The strong green emission suggests that these glasses may be a better option for display devices and green emission applications.
chemistry, analytical
-
Enhanced Upconversion in Ho3+-doped Transparent Glass Ceramics Containing BaYbF5 Nanocrystals
Sha Jiang,Hai Guo,Xiantao Wei,Changkui Duan,Min Yin
DOI: https://doi.org/10.1016/j.jlumin.2013.11.030
IF: 3.6
2014-01-01
Journal of Luminescence
Abstract:Novel Ho3+-doped transparent oxyfluoride SiO2–Al2O3–Na2CO3–CaO–BaF2–YbF3 glass ceramics (GC) containing BaYbF5 nanocrystals were fabricated via melt-quenching technique with subsequent heat treatment. The formation of crystalline fluoride phase was confirmed by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Compared to precursor glasses, the greatly enhanced green emission (40-fold), new emission band at ultraviolet-blue region and stark splittings of emission in GC, indicate that Ho3+ enters into BaYbF5 nanocrystals with low phonon energy. Besides, the origin of the previously unconfirmed emission band at 440–460nm is clearly identified by measuring spectra from thermally coupled luminescent levels at various temperatures. The outstanding upconversion properties of Ho3+ in GC may present potential application in all-solid-state upconversion lasers operating in the visible and ultraviolet range.
-
Highly efficient ultraviolet and visible light emissions from upconversion transitions in Ho/Tm/Yb co-doped lutecia-stabilized zirconia single crystals excited by a 980 nm laser
Kan Lu,Qifan Zhang,Juan Kong,Yan Hao,Wenxia Wu,Yazhao Wang,Haibo Lin,Shoulei Xu,Wen Deng
DOI: https://doi.org/10.1039/d4ce00844h
IF: 3.756
2024-10-04
CrystEngComm
Abstract:High-quality transparent cubic lutecia-stabilized zirconia (LSZ) and LSZ:Yb 0.25 Tm 0.5 Ho 0.03 single crystals were fabricated by the OFZ (optical floating zone) method for the first time. For comparison, YSZ and YSZ:Yb 0.25 Tm 0.5 Ho 0.03 single crystals were also fabricated. The transmittance of the LSZ single crystal (80.7%) is slightly lower than that of the YSZ single crystal (86.3%) in the visible light region, which is attributed to the LSZ single crystal with a higher density (6.604 g cm −3 ) in comparison with that of the YSZ single crystal (5.973 g cm −3 ). No absorption peaks were observed in the transmission and absorption spectra of LSZ and YSZ within 200–1100 nm, indicating that both crystals are excellent host crystals. The density of LSZ:Yb 0.25 Tm 0.5 Ho 0.03 single crystals (6.596 g cm −3 ) is also higher than that of YSZ:Yb 0.25 Tm 0.5 Ho 0.03 single crystals (6.005 g cm −3 ). The absorption spectra of LSZ:Yb 0.25 Tm 0.5 Ho 0.03 and YSZ:Yb 0.25 Tm 0.5 Ho 0.03 single crystals exhibited several absorption peaks at 363, 453, 678, and 785 nm and a strong broad absorption band within 850–1000 nm. The upconversion photoluminescence (UCPL) spectrum of the LSZ:Yb 0.25 Tm 0.5 Ho 0.03 single crystal excited at 980 nm exhibited several emission peaks at 308, 373, 488, 540, 550, 655 and 794 nm; similar emission peaks were observed in the UCPL spectrum of the YSZ:Yb 0.25 Tm 0.5 Ho 0.03 single crystal. The intensities of the emission peaks of the former are higher than those of the corresponding peaks of the latter, which is due to the former having a higher density and lower phonon energy in comparison with the latter. Power curves indicated that the 308 and 373 nm emissions are 4-photon upconversion processes, the 488 nm emission is a 3-photon process, and the 540 nm and 655 nm emissions are 2-photon processes. These results indicate that under the excitation at 980 nm, the LSZ:Yb 0.25 Tm 0.5 Ho 0.03 single crystal has high efficiency over the YSZ:Yb 0.25 Tm 0.5 Ho 0.03 single crystal in ultraviolet and visible light emissions.
chemistry, multidisciplinary,crystallography
-
Research on the Photoluminescence and Up-Conversion Luminescence Properties of Y2Mo4O15: Yb, Ho under 454 and 980 Nm Excitation
Tao Jiang,Ying Tian,Mingming Xing,Yao Fu,Xiumei Yin,Hong Wang,Xin Feng,Xixian Luo
DOI: https://doi.org/10.1016/j.materresbull.2017.09.025
IF: 5.6
2017-01-01
Materials Research Bulletin
Abstract:Y1.8-xYb0.2HoxMo4O15 (x = 0.005, 0.01, 0.02, 0.04, 0.08, 0.16, 0.32, 0.64) phosphors were synthesised at 700 degrees C by using a solid-state reaction method. The samples were characterised by X-ray diffraction, diffuse reflectance spectra, photoluminescence and up-conversion emission spectra. The photoluminescence spectra of Y2Mo4O15:Yb, Ho shows extremely strong green down-shift luminescence corresponding to the F-5(4), S-5(2) -> I-5(8) transition of Ho3+ ions with I-g/I-r > 20 under 454 nm excitation. While at 980 nm excitation, Y2Mo4O15:Yb, Ho sample exhibits unusual red up-conversion luminescence along with a very weak green emission (I-r/I-g = 6.4), which is resulted from the severe non-radiative relaxation (I-5(6) -> I-5(7)) process due to the very short decay time of I-5(6) states of Ho3+ ions. The mechanism of down-shift luminescence is the electrical dipole - dipole transitions. The quenching concentration for down-shift luminescence is higher than that for up-conversion luminescence, which results from the effects of different luminescence processes and large distance between doped rare earth ions in Y2Mo4IO15. The different luminescence mechanism and color performance are also studied.
-
Luminescence properties and temperature characteristics of Yb3+/Nd3+/Ho3+ triple doped BaGeTeO6 up-conversion phosphors under 980 nm excitation
Shengyi Liu,Duan Gao,Li Wang,Wenbin Song,Zhiliang Zhang,Peilin Du,Ying Zhu,Peijia Xiao,Qi Zhang
DOI: https://doi.org/10.1007/s10043-024-00911-6
IF: 1.2
2024-08-26
Optical Review
Abstract:BaGeTeO 6 : Nd 3+ /Yb 3+ /Ho 3+ green up-conversion phosphors were synthesized using the high-temperature solid-state reaction method. The optimal doping concentrations for the three dopant ions Nd 3+ , Yb 3+ , and Ho 3+ were determined to be 1 mol%, 6 mol%, and 0.8 mol%, respectively, through the method of controlling variables. By analyzing the dependence of the up-conversion luminescence intensity on the pump current of the 980 nm laser, it was found that the green and red up-conversion emissions of Ho 3+ ions under 980 nm laser excitation were both two-photon processes. Furthermore, the influence of temperature on the up-conversion luminescent properties of BaGeTeO 6 : Nd 3+ /Yb 3+ /Ho 3+ green up-conversion phosphors under 980 nm laser excitation was investigated, and the temperature sensing properties of Ho 3+ ions were discussed. The results indicated that, at room temperature and higher temperatures, both the red and green up-conversion emissions of the sample were two-photon processes. Within the range of excitation current used in the experiment, the ratio of red to green up-conversion luminescence intensity of Ho 3+ ions was independent of the laser excitation current but correlated with the sample temperature. In the temperature range of 303–723 K, the ratio of red to green up-conversion luminescence intensity of Ho 3+ ions exhibited a nonlinear relationship with temperature. Comparing the temperature sensing sensitivity of Ho 3+ in different matrices, the results indicated that the sample possessed high temperature sensing sensitivity.
optics
-
Optical spectroscopy of Ho3+,Pr3+ co-doped YScO3 crystal
Chuang Yang,Jian Liu,Peng Chen,Qingsong Song,Jie Xu,Peng Liu,Yanyan Xue,Xiaodong Xu,Kheirreddine Lebbou,Ivan Buchvarov,Jun Xu
DOI: https://doi.org/10.1016/j.jlumin.2023.120151
IF: 3.6
2023-08-01
Journal of Luminescence
Abstract:YScO3 single crystal co-doped with Ho3+ and Pr3+ ions has been successfully grown by the Czochralaki method. The absorption spectrum, fluorescence spectrum and fluorescence decay curve were measured at room temperature. The absorption cross section of Ho,Pr:YScO3 at 649 nm and 1130 nm was calculated to be 0.93 × 10−20 cm2 and 0.32 × 10−20 cm2, respectively. Judd-Ofelt (J-O) theory was performed to evaluate the spontaneous emission probabilities and the radiative lifetimes. Ho,Pr:YScO3 exhibited strong emission at 2040 nm and 2890 nm with a emission cross section of 0.80 × 10−21 cm2 and 1.22 × 10−20 cm2, respectively. The fluorescence lifetime of the Ho3+:5I6 and 5I7 levels were calculated to be 0.31 ms and 5.89 ms, respectively. All the results indicate that the Ho,Pr:YScO3 crystal could be a potential laser material for 2.9 μm laser operation.
optics
-
The role of thickness on the structural and luminescence properties of Y2O3:Ho3+, Yb3+ upconversion films
Vhahangwele Makumbane,Robin E. Kroon,Mubarak Y. A. Yagoub,Lucas J. B. Erasmus,E. Coetsee,Hendrik C. Swart
DOI: https://doi.org/10.1038/s41598-024-68367-x
IF: 4.6
2024-08-03
Scientific Reports
Abstract:The structural, surface, and upconversion (UC) luminescence properties of Y 2 O 3 :Ho 3+ ,Yb 3+ films grown by pulsed laser deposition, for different numbers of laser pulses, were studied. The crystallinity, surface, and UC luminescence properties of the thin films were found to be highly dependent on the number of laser pulses. The X-ray powder diffraction analysis revealed that Y 2 O 3 :Ho 3+ ,Yb 3+ films were formed in a cubic structure phase with an Ia space group. The thicknesses of the films were estimated by using cross-sectional scanning electron microscopy, depth profiles using X-ray photoelectron spectroscopy (XPS), and the Swanepoel method. The high-resolution XPS was used to determine the chemical composition and oxidation states of the prepared films. The UC emissions were observed at 538, 550, 666, and 756 nm, assigned to the 5 F 4 → 5 I 8 , 5 S 2 → 5 I 8 , 5 F 5 → 5 I 8 , and 5 S 2 → 5 I 7 transitions of the Ho 3+ ions. The power dependence measurements confirmed the involvement of a two-photon process in the UC process. The color purity estimated from the Commission International de I'Eclairage coordinates confirmed strong green UC emission. The results suggested that the Y 2 O 3 :Ho 3+ ,Yb 3+ UC transparent films are good candidates for various applications, including solar cell applications.
multidisciplinary sciences
-
Modulation of phosphor luminescence performance by high concentration self-sensitization of Er and Ho-Yb ions co-doping under 1550 nm excitation
Lei Bohan,Liping Lu,Haiying Sun
DOI: https://doi.org/10.1039/d4tc00859f
IF: 6.4
2024-05-31
Journal of Materials Chemistry C
Abstract:In this paper, upconversion fluoride phosphors NaY1-x-y-zF4:Er3+x, Ho3+y, Yb3+z were synthesized by the low-temperature combustion method. And the optimal ratio of lanthanide ion doping in the matrix lattice was determined by the control variable method. First of all, the experimental results show that some Er3+-2 ions may be present in the samples doped with a high concentration of Er3+ ions, and the energy carried by the 1550 nm photons is absorbed by them and transferred to the remaining Er3+-1 ions in the form of sensitizers, it leads to saturation excitation of these Er3+ -1 ions. Thus, the upconversion luminescence intensity of the Er3+ ions-doped samples was dramatically increased. Secondly, it was found that the singly doped Ho3+ ions samples also showed significant absorption of 1550 nm photons. In contrast, doping Yb3+ ions in samples singly doped with Ho3+ ions produces the opposite effect of Er3+ ions. The upconversion luminescence intensity of the Ho3+ ions-doped samples being significantly quenched. According to the above experimental phenomena, when a small amount of Ho3+ ions are doped into the matrix lattice of the sample doped with a high concentration of Er3+ ions. Firstly, these Ho3+ ions can act as transient energy transition centers in the lattice. Secondly, they can also play the role of another self-absorption activation center in the matrix lattice. The upconversion luminescence performance of the Er3+-Ho3+ ions co-doped samples is significantly enhanced, so the characteristic emissions of Er3+ and Ho3+ ions are highly overlapped in the visible region. A small amount of Yb3+ ions continue to be doped into the Er3+-Ho3+ ions co-doped system, due to the significant quenching effect of the Yb3+ ions on the luminescence of the Ho3+ ions. The Yb3+ ions mainly play the role of reverse energy transfer centers between the Er3+-Yb3+ ions in the crystal lattice.
materials science, multidisciplinary,physics, applied
-
Investigation of up/down-converted luminescence and related mechanisms in Ho3+/Yb3+ co-doped Y2Zr2O7 highly transparent ceramics as phosphor material
Yilong Li,Yucheng Ye,Weike Quan,Yichu Qin,Wenhan Han,Yao Chen,Wenlong Liao,Yucheng Wu,Jun Wang,Jianqi Qi
DOI: https://doi.org/10.1016/j.jlumin.2022.119255
IF: 3.6
2022-11-01
Journal of Luminescence
Abstract:Via solid state reaction, Ho3+/Yb3+ co-doped Y2Zr2O7 (YZO) transparent ceramics with different ytterbium concentration were successfully prepared. Highest in-line transmittance of samples reaches over 75% in both visible and near-infrared region. The homogeneity and microstructure of powders and ceramics were investigated through XRD and SEM characterizations. The luminescence results show that under excitation at ultraviolet (UV) and near-infrared (NIR) source, strong green emission peaks were observed and corresponding energy-conversion mechanism such as cooperative energy transfer (CET) were applied to explain the transition mechanism. Combined with the excellent optical properties and high temperature resistance, these results suggest that Ho3+/Yb3+ co-doped Y2Zr2O7 (YZO) transparent ceramics are promising novel phosphor material under different circumstance.
optics
-
UVB upconversion of LiYO2:Ho3+,Gd3+ for application in luminescence thermometry
Shanshan Zhao,Benchun Li,Tiantian Shen,Fang Fang,Songlin Zhuang,Dawei Zhang,Dechao Yu
DOI: https://doi.org/10.1039/d3dt01690k
IF: 4
2023-09-08
Dalton Transactions
Abstract:Development of novel ultraviolet (UV) upconverting materials has been emerging as hot research topic for application in tunable UV laser, photocatalysis, sterilization, tagging, and most recently luminescence thermometry. We readily synthesized a series of Ho3+/Gd3+ co-doped LiYO2 upconverting phosphors by a traditional high-temperature reaction. Under excitation of a blue ~ 445 nm laser, the LiYO2:Ho3+,Gd3+ polycrystalline powders yield intense sharp ultraviolet B (UVB) upconversion luminescence from Gd3+ 6Pj (j = 7/2, 5/2, 3/2) excited states. By means of steady and dynamic photoluminescence spectra, we systematically investigated the involved two-photon absorption upconversion as well as the accompanying energy transfer processes between Ho3+ and Gd3+ ions in LiYO2 host lattice. Interestingly, the distinguishable UVB luminescence constituents from Gd3+ 6Pj excited states behave sensitive temperature dependence in 353-673 K. Sheding light onto thermal equilibriums between Gd3+ 6Pj UV-emitting levels, their luminescence intensity ratios follow Boltzmann statistics for application of new luminescence thermometry. For the scheme of 6P3/2-6P5/2 thermally coupled levels, it works over temperature range of 373-673 K with a maximum relative sensitivity (Sr) about 1.08% at 373 K, and the 6P7/2-6P5/2 counterpart works over 353-533 K with a maximum Sr about 0.80% at 353 K. Overall, our study provides new pathway to develop UV upconverting materials, and promotes application of Gd3+-related UV luminescence constituents in sensitive temperature sensing over a wide temperature range.
chemistry, inorganic & nuclear
-
Investigation of the Energy-Transfer Mechanism in Ho3+- and Yb3+-Codoped Lu2O3 Phosphor with Efficient Near-Infrared Downconversion
Guotao Xiang,Yan Ma,Xianju Zhou,Sha Jiang,Li Li,Xiaobing Luo,Zhendong Hao,Xia Zhang,Guo-Hui Pan,Yongshi Luo,Jiahua Zhang
DOI: https://doi.org/10.1021/acs.inorgchem.6b02600
2017-02-06
Abstract:A high-temperature solid-state method was used to synthesize the Ho3+- and Yb3+-codoped cubic Lu2O3 powders. The crystal structures of the as-prepared powders were characterized by X-ray diffraction. The energy-transfer (ET) phenomenon between Ho3+ ions and Yb3+ ions was verified by the steady-state spectra including visible and near-infrared (NIR) regions. Beyond that, the decay curves were also measured to certify the existence of the ET process. The downconversion phenomena appeared when the samples were excited by 446 nm wavelength corresponding to the transition of Ho3+: 5I8→5G6/5F1. On the basis of the analysis of the relationship between the initial transfer rate of Ho3+: 5F3 level and the Yb3+ doping concentration, it indicates that the ET from 5F3 state of Ho3+ ions to 2F5/2 state of Yb3+ ions is mainly through a two-step ET process, not the long-accepted cooperative ET process. In addition, a 62% ET efficiency can be achieved in Lu2O3: 1% Ho3+/30% Yb3+. Unlike the common situations in which the NIR photons are all emitted by the acceptors Yb3+, the sensitizers Ho3+ also make contributions to the NIR emission upon 446 nm wavelength excitation. Meanwhile, the 5I5→5I8 transition and 5F4/5S2→5I6 transition of Ho3+ as well as the 2F5/2→2F7/2 transition of Yb3+ match well with the optimal spectral response of crystalline silicon solar cells. The current research indicates that Lu2O3: Ho3+/Yb3+ is a promising material to improve conversion efficiency of crystalline silicon solar cell.
-
Impact of high sensitizer doping on the transient multiband upconversion luminescence in β-NaYF 4 :Yb/Ho microcrystals
Mingchen Li,Maohui Yuan,Wenda Cui,Hao Liu,Hanchang Huang,Zhongyang Xing,Chuan Guo,Kai Han
DOI: https://doi.org/10.1016/j.optmat.2024.115993
IF: 3.754
2024-08-23
Optical Materials
Abstract:Under intense near-infrared light excitation, upconversion luminescence (UCL) nanomaterials exhibit multiband emission and high sensitizer quenching concentration, indicating the potential to enhance upconversion (UC) quantum efficiency. In comparison to other common activator ions (e.g. Er 3+ , Tm 3+ , Ho 3+ ), Ho 3+ possesses abundant energy levels. However, previous studies mostly focused on the red (Ho 3+ : 5 F 5 → 5 I 8 ) and green (Ho 3+ : 5 F 4 , 5 S 2 → 5 I 8 ) emissions. In this paper, we have examined the transient UCL characteristics of β-NaYF 4 :Yb/Ho microcrystals (MCs) excited by a high-power 976 nm ns pulsed laser (∼0.32 GW/cm 2 ). The energy transfer (ET) pathways with varying Yb 3+ doping (20–98 mol%) are determined by the time evolution spectra. In high Yb 3+ doping system (98 mol%), the electron population of Ho 3+ accelerates, and the multiband UC rise is shortened by 6 times (from ∼3 μs to ∼500 ns). We identified a new pathway for electron populating with higher Yb 3+ doping ( ≥ 40 mol%), which is Yb 3+ : 2 F 5/2 + Ho 3+ : 3 L 9 → Yb 3+ : 2 F 7/2 + Ho 3+ : 3 M 9 . As Yb 3+ concentration increases, the varying lifetime and intensity distribution of UCL leads to variations in the luminescence color evolution. Our result shows that altering the Yb 3+ doping concentration provides a way to control the energy flow between energy levels of Ho 3+ , which can modulate the rise time and color evolution of Yb–Ho co-doped UC MCs. This study is expected to promote the advancement of fast-respond optoelectronic devices, UC displays, and micro-nano lasers. Kewords multiband upconversion luminescence; high-power excitation; upconversion luminescence dynamics; high sensitizer concentration; upconversion pathways.
materials science, multidisciplinary,optics
-
Enhanced Optical Temperature Sensing Performance Based on Dual Emission Centers of Y2O3: Yb3+, Tm3+, Ho3+ Upconversion Phosphor
Jian Wang,Huili Zhou,Kesong Zhu,Linhua Ye,Xuegong Yu,Junxiang Zhang,Li-Gang Wang
DOI: https://doi.org/10.1016/j.ceramint.2024.07.025
IF: 5.532
2024-01-01
Ceramics International
Abstract:Y2O3: 5%Yb3+, 0.5%Tm3+, z%Ho3+ (z = 0, 0.1, 0.5, 1.0) upconversion luminescent materials were synthesized by CO2 laser zone melting method. The upconversion luminescence (UCL) spectra of the samples were recorded with the excitation of 980 nm laser, and the energy transfer processes among doped rare earth (RE) ions were analyzed. The introduction of Ho3+ ions into Y2O3: 5%Yb3+, 0.5%Tm3+ gave the samples four distinct UCL bands, including blue, green, red, and infrared emission bands. The temperature sensing characteristics based on the fluorescence intensity ratio (FIR) of non-thermally coupled levels (NTCLs) of Tm3+ and Ho3+ ions were studied, and the derived maximum relative sensitivity (SR) reached impressive value of 0.0138 K-1 (298 K). Compared to the materials doped with single emission center of either Tm3+ or Ho3+ ions, the luminescent material co-doped with both Tm3+ and Ho3+ ions exhibited higher sensitivity while maintaining a wide temperature measurement range. The research results indicate that Y2O3: Yb3+, Tm3+, Ho3+ upconversion phosphor promises broad application prospects in optical temperature measurement.
-
The upconversion luminescence properties of the Yb<sup>3+</sup>–Ho<sup>3+</sup> system in nanocrystalline Y<sub>2</sub>O<sub>2</sub>S
Yao Fu,Wanghe Cao,Yong Peng,Xixian Luo,Mingming Xing
DOI: https://doi.org/10.1007/s10853-010-4744-5
IF: 4.5
2010-01-01
Journal of Materials Science
Abstract:Near-spherical Y2O2S:Yb3+,Ho3+ nanocrystals (NCs) with an average particle size of 40 nm were synthesized by the coprecipitation method followed by a solid-gas sulfuration technique. The effects of the Ho3+ ion doping concentration on the upconversion luminescence (UCL) property of the NCs was studied through the UCL spectra. Results show that the UCL intensity of Y2O2S:Yb3+,Ho3+ NCs markedly changes with Ho3+ ion concentration, and that the Ho3+ ion concentration quench is observed at 0.25 mol%. This value is only half as much as that in micron Y2O2S prepared by a solid state reaction, which can be attributed to the distinct diffusion mechanism of activator ions in the coprecipitation process. In addition, strong red emissions can be observed in Y2O2S:Yb3+,Ho3+ NCs throughout all Ho3+ doping concentrations used. However, the Ho3+ in micron Y2O2S usually exhibits weak red UCL. Infrared spectra confirm that this result is related to the large vibrational quanta produced by OH- and CO3 (2-) groups adsorbed onto the surface of NCs. These large vibrational quanta can remarkably increase the probability of S-5(2)-F-5(5) and I-5(6)-I-5(7) multiphonon relaxation, leading to the enhancement of red emissions arising from F-5(5) -> I-5(8) transitions. The UCL mechanism of the Yb3+-Ho3+ system in nano- and microsized Y2O2S is also discussed.