Preparation and Properties of Superhydrophilic Polyvinylidene Fluoride Hollow Fiber Membrane
Cheng Jifeng,Jiang Tuanhui,Zhan Xiaomei,Qi Yating,Yang Yuanyuan,Kang Xun,Qin Shuhao
DOI: https://doi.org/10.7503/cjcu20190374
2020-01-01
Abstract:PVDF-g-GMA membrane was prepared by grafting glycidyl methacrylate( GMA ) onto the surface of polyvinylidene fluoride ( PVDF) membrane by ultrasonic assisted graft polymerization. A modified membrane with zwitterionic structure surface ( PVDF-g-GMA-Thr ) was prepared by grafting threonine ( Thr ) onto the surface of the PVDF membrane through the ring opening reaction of epoxy groups induced by amino group. The chemical composition, wettability, , surface morphology and antifouling performance of PVDF membrane before and after modification were systematically studied by Attenuated total reflection Fourier infrared spectroscopy ( ATR-FTIR) , X-ray photoelectron spectroscopy ( XPS) , contact angle analyzer, scanning electron microscopy ( SEM ) and bovine serum albumin ( BSA) filtration experiments. The results show that with the increase of PVDF-g-GMA grafted threonine reaction time, the hydrophilicity of the prepared modified membrane with zwitterionic structure surface is obviously improved , and the contact angle is reduced from 90 degrees to 0 degrees , showing the superhydrophilicity. At the same time , the water flux of the modified membrane is obviously improved , when the threonine induces the ring opening reaction 14 12 h , the modified membrane has the highest water flux as high as 686 L/( m(2). h) , it increased by 204. 5%. In addition , in the filtration test of BSA , the modified membrane exhibited good anti-fouling performance and retention performance. BSA rejection ratio is increased from 42% to 84% for the modified membranes. Moreover, compared with PVDF original membrane, the water flux recovery rate of the modified membrane increased from 53% to 87% and the irreversible fouling decreased from 47% to 12% , which indicated that the membrane fkmling can be effectively reduced by grafting threonine to construct zwitterionic structure surface on the PVDF membrane.