Abstract:The Er~(3+)/Yb~(3+) codoped TeO_2-WO_3-ZnO (TWZ) glass samples with same doping concentration and different thickness were prepared. The absorption spectra, 1.5 μm emission spectra and fluorescence lifetimes of Er~(3+), excited by 970 nm, were measured. The absorption cross-section was calculated based on measured absorption spectra at room temperature. The emission cross-sections were calculated by McCumber theory. The effect of radiation trapping on the spectroscopic properties of Er~(3+) in TWZ glass was discussed. Because of the high refractive index of the glass and very large overlapping around 1.5 μm between the absorption cross section and the emission cross section of Er~(3+) in TWZ glass, the radiation trapping in the TWZ glass samples was very strong. The radiation trapping became stronger with the increase of the thickness of samples. Due to the effect of the radiation trapping, the measured fluorescence lifetime was longer than the calculated one, which caused the quantum efficiency large than 100%. The emission spectra were also broadened and the emission peak wavelength shifted to the longer wavelength slightly. When the sample thickness increased from 0.50 mm to 3.15 mm, the fluorescence lifetime increased from 2.60 ms to 3.10 ms and the quantum efficiency increased from 111% to 132%. At the same time, the fluorescence effective line width, Δλ_(eff), increased from 76.2 nm to 91.7 nm and the emission intensity ratio of the main peak to the second peak, I_s/I_p, also increased gradually. The fitting results showed that the Δλ_(eff) increased linearly with the increasing of the ratio value of I_s/I_p. Based on the obtained linear equation for Δλ_(eff) and I_s/I_p, the effective line width in the glass sample without the exis-tence of radiation trapping was deduced, which was 72.1 nm. The value was very close to the Δλ_(eff) calculated from the emission cross-section curve, which was 70.3 nm. So we suggested that the Δλ_(eff) calculated from the emission cross-section curve could be used to determine the Δλ_(eff) of Er~(3+) emission at 1.5 μm without the radiation trapping effect. For the first time, the opinion that the ratio of the I_s/I_p to the σ_(es)/σ_(ep), or the difference between the I_s/I_p and the σ_(es)/σ_(ep) can be used to evaluate the radiation trapping of Er~(3+) at 1.5 μm band. Here the σ_(es) and the σ_(ep) are the emission cross sections at wavelength of the second peak and the strongest peak, respectively, calculated by McCumber theory.

Effect of Radiative Trapping on Measurement of the Spectroscopic Properties of Yb3+: Phosphate Glasses

Effect of Radiation Trapping on Spectroscopic Properties of Yb3+-Doped Phosphate Glasses

Luminescence Properties of Yb2+ Doped NaBaPO4 Phosphate Crystals

Spectroscopic Properties of Yb 3+ doped Phosphate GlassesSupported by Natianal Natural Science Foudation of China under project 69578026.

Spectroscopic Properties of Yb3 + in Phosphate Glass

Effect of Radiation Trapping on Spectroscopic Properties of Er3+/Yb3+ Codoped Tungsten-Tellurite Glasses

Dependence of spectral properties of Yb3+ on [PO3]- content in fluorophosphate glasses

Dependence Of Spectroscopic Properties On Ytterbium Ion Concentration In Glasses

Influence of MF2(M=Mg, Ca, Zn, Sr, Ba) on properties of Yb3+-doped phosphate glasses

Spectroscopic Properties of Ytterbium in Phosphate Glass

Effect of Ce3+ and Cr3+ on the Spectroscopy Properties of Cr3+, Yb3+, Er3+ Co-Doped Phosphate Glasses

Spectroscopic Properties Of Er3+ And Yb3+ Co-Doped Glass Ceramics Containing Srf2 Nanocrystals

Spectroscopic properties of Er<sup>3+</sup>and Yb<sup>3+</sup>co-doped glass ceramics containing SrF<sub>2</sub>nanocrystals

Radiative-trapping and Fluorescence-Concentration Quenching Effects of Yb:YAl_3(BO_3)_4 Crystals

Influence of Rare Earth Elements and Radiation on Spectral Properties and Thermal Conductivity of Yttrium Aluminum Garnets and Phosphate Glasses

Spectroscopic Properties of Yb 3+ -Doped Borate Glasses

Microstructure and Luminescence of Yb3+-doped Fluorosilicate Glass Ceramics

The spectrum and laser properties of ytterbium doped phosphate glass at low temperature

Optical properties of Yb3+ doped Bi2O3-3B2O3 glass

Spectroscopic Properties of Sm3+-Doped Phosphate Glasses

Concentration Effect of Spectroscopic Properties of Yb3+-doped Borate Glasses