Abstract:Pt-based catalysts play a significant role in the advancement of direct methanol fuel cells (DMFCs). However, their inefficient reaction kinetics, low resistance to CO poisoning, and unstable performance hinder the commercialization of DMFCs. To address these issues and enhance both the catalytic efficiency and stability of Pt-based catalysts for the methanol oxidation reaction (MOR), the MnO-Co@Pt nanocomposites by encapsulating them into N-doped porous carbon (NPC), confirmed through physicochemical characterizations, such as HR-TEM, XRD, XPS, were prepared in this paper. The catalyst structures were controllable synthesized by adjusted calcination, and reaction time of galvanic replacement. MnO-Co@Pt NPCs demonstrated significantly improved performance compared to Pt/C catalysts for MOR. The mass activity of 925.72 mA mgPt-1 and current density after an 3600s I-t test of MnO-Co@Pt NPCs 800 15 min 15% were 3.3 times and 3.8 times higher than that of Pt/C catalyst, respectively. The peak potential of CO electrooxidation exhibited a negative shift of 73 mV when compared with Pt/C catalyst. The exceptional MOR performance of MnO-Co@Pt NPCs can be attributed to the binding, and encapsulation effects of the NPCs, which facilitate the isolation, preventing the sintering and expansion of MnO-Co@Pt nanoparticles. This study not only presents a simple method for developing low Pt nanostructures but also offers possibilities for designing nanocomposites with carbon protection layers and coated catalysts incorporating different transition metals. These advancements significantly improve the performance of Pt-based electrocatalysts for the MOR process.

Effect of over-oxidation treatment of Pt–Co/polypyrrole-carbon nanotube catalysts on methanol oxidation

Highly Active Nanoporous Pt-based Alloy As Anode and Cathode Catalyst for Direct Methanol Fuel Cells

Pt-Co Supported On Polypyrrole-Multiwalled Carbon Nanotubes As An Anode Catalyst For Direct Methanol Fuel Cells

Synthesis and characterization of bimetallic Pt–Fe/polypyrrole–carbon catalyst as DMFC anode catalyst

A study of different polyphosphazene-coated carbon nanotubes as a Pt-Co catalyst support for methanol oxidation fuel cell

Ptco/polypyrrole-multiwalled carbon nanotube complex cathode catalyst containing two types of oxygen reduction active sites used in direct methanol fuel cells

Role of Pt-Pyridinic Nitrogen Sites in Methanol Oxidation on Pt/Polypyrrole-Carbon Black Catalyst

Development of Composite Anode Electrocatalyst for Direct Methanol Fuel Cells

Enhanced Electrocatalytic Performance of the FePt/PPy-C Composite toward Methanol Oxidation

A highly active, stable and synergistic Pt nanoparticles/Mo 2 C nanotube catalyst for methanol electro-oxidation

Evaluation of the Performance of Carbon Supported Pt-Ru-Ni-P as Anode Catalyst for Methanol Electrooxidation

Pt–Co supported on single-walled carbon nanotubes as an anode catalyst for direct methanol fuel cells

Co-catalytic effect of Ni in the methanol electro-oxidation on Pt–Ru/C catalyst for direct methanol fuel cell

Methanol Oxidation over Tio2-Modified Multi-Walled Carbon Nanotubes Supported Pt-Mo Electrocatalyst

Pt supported on phosphorus-doped carbon nanotube as an anode catalyst for direct methanol fuel cells

Core–Shell Structured PtRuCo x Nanoparticles on Carbon Nanotubes as Highly Active and Durable Electrocatalysts for Direct Methanol Fuel Cells

Different polyaniline/carbon nanotube composites as Pt catalyst supports for methanol electro-oxidation

MnO-Co@Pt nanowires encapsulated in N-doped porous carbon derived from MOFs for efficient electrocatalytic methanol oxidation reaction

Nanostructured Polypyrrole/Carbon Composite As Pt Catalyst Support for Fuel Cell Applications

Facile Fabrication of Platinum-Cobalt Alloy Nanoparticles with Enhanced Electrocatalytic Activity for a Methanol Oxidation Reaction

Facile Synthesis of PtP2 Nanocrystals As Highly Active Electrocatalysts for Methanol Oxidation.