Abstract:Uniform CeO(2) nanoflowers were synthesized by rapid thermolysis of (NH(4))(2)Ce(NO(3))(6) in oleic acid (OA)/oleylamine (OM), by a unique 3D oriented-attachment mechanism. CeO(2) nanoflowers with controlled shape (cubic, four-petaled, and starlike) and tunable size (10-40 nm) were obtained by adjusting the reaction conditions including solvent composition, precursor concentration, reaction temperature, and reaction time. The nanoflower growth mechanism was investigated by in situ electrical conductance measurements, transmission electron microscopy, and UV/Vis spectroscopy. The CeO(2) nanoflowers are likely formed in two major steps, that is, initial formation of ceria cluster particles capped with various ligands (e.g., OA, OM, and NO(3) (-)) via hydrolysis of (NH(4))(2)Ce(NO(3))(6) at temperatures in the range 140-220 degrees C, and subsequent spontaneous organization of the primary particles into nanoflowers by 3D oriented attachment, due to a rapid decrease in surface ligand coverage caused by sudden decomposition of the precursor at temperatures above 220 degrees C in a strong redox reaction. After calcination at 400 degrees C for 4 h the 33.8 nm CeO(2) nanoflowers have a specific surface area as large as 156 m(2) g(-1) with high porosity, and they are highly active for conversion of CO to CO(2) in the low temperature range of 200-400 degrees C. The present approach has also been extended to the preparation of other transition metal oxide (CoO, NiO, and CuO(x)) nanoflowers.

Cupric Oxide Nanoflowers Synthesized with a Simple Solution Route and Their Field Emission

Facile Synthesis of Leaf-like Cu(OH)2 and Its Conversion into CuO with Nanopores

Growth of Cu2o Flower/Grass-Like Nanoarchitectures and Their Photovoltaic Effects

One-Pot Fast Synthesis of Leaf-Like CuO Nanostructures and CuO/Ag Microspheres with Photocatalytic Application

Self-Assembled Synthesis and Characterization of Dandelion-Like and Flower-Like Cupric Oxide Nanostructures

Synthesis of Highly Monodisperse Cu2O Nanocrystals and Their Applications as Hole-Transporting Layers in Solution-Processed Light-Emitting Diodes.

Field Electron Emission from Cupric Oxide-Nanobelt Films

Synthesis of flower-like CuO nanostructures as a sensitive sensor for catalysis

Innovative Multiphase Ultrasonic-Assisted Method for High-Purity, Stable, and Cost-Effective Copper Nanowire Synthesis

One-step synthesis of copper compounds on copper foil and their supercapacitive performance

Preparation of Novel Cuprous Oxide-Fullerene[60] Core-Shell Nanowires and Nanoparticles Via A Copper(I)-Assisted Fullerene-Polymerization Reaction

Fabrication of Nanowire-Like Cuprous Oxide in Aqueous Solutions of a Triblock Copolymer

Controlled growth of CuO nanowires on Cu grid via thermal oxidation process with enhanced field electron emission properties

Growth of Novel Nanostructured Copper Oxide (cuo) Films on Copper Foil

A novel wet-chemical method of preparing highly monodispersed Cu2O nanoparticles

Copper Nanoflower Assembled by Sub-2 Nm Rough Nanowires for Efficient Oxygen Reduction Reaction: High Stability and Poison Resistance and Density Functional Calculations.

Preparation of Cuo Nanowire Field Emitter Arrays by Thermal Oxidation in Water Vapor Containing Environments and Their Field Emission Properties

Copper Hydroxide Nanoneedle And Nanotube Arrays Fabricated By Anodization Of Copper

Polyol synthesis and chemical conversion of Cu 2 O nanospheres

Spontaneous Organization of Uniform CeO2 Nanoflowers by 3D Oriented Attachment in Hot Surfactant Solutions Monitored with an in Situ Electrical Conductance Technique

The in Situ Preparation of Novel Α-Fe2o3 Nanorods/cnts Composites and Their Greatly Enhanced Field Emission Properties