Abstract:The effects of Ca substitution for Y on the electrical transport and thermoelectric properties of Y1-xCaxCoO3 (0 <= x <= 0.1), prepared by using the sol-gel process, were investigated in the temperature range from 300 to 780 K. The results indicated that direct current electrical resistivity rho of Y1-xCaxCoO3 decreased remarkably with increasing Ca content x as x <= 0.01, which could mainly be attributed to the increase of hole concentration due to substitution of Ca2+ for Y3+. The temperature dependences of the resistivity for Y1-xCaxCoO3 were all found to be basically consistent with small-polaron hopping conduction model. Although Seebeck coefficient S of Y1-xCaxCoO3 at low temperatures T <similar to 550 K decreased remarkably with increasing x, it approached a limit value similar to 150 mu V/K at similar to 800 K for all the samples with different x, which was consistent well with the thermopower resulting from the degeneracy of electron configuration estimated from Heikes formula by assuming that Co3+ and Co4+ exist in low spin state. Experiments showed that thermal conductivity kappa of Y1-xCaxCoO3 came mainly from its lattice component, whose decrease with increasing x could be chiefly ascribed to impurity-scattering effect due to Ca doping. The thermoelectric figure of merit ZT (=(ST)-T-2/rho kappa) of Y1-xCaxCoO3 changed nonmonotonously with increasing doping content of Ca, and Y0.95Ca0.05CoO3 was found to have optimum thermoelectric properties with ZT=0.019 at 660 K, which was about ten-fold greater than that of YCoO3, indicating that its thermoelectric properties could be improved effectively by appropriate substitution of Ca for Y in this compound. (c) 2007 American Institute of Physics.

Thermoelectric Properties of Sol–gel Derived Cobaltite Bi2Ca2.4Co2Oy

Intrinsically Modified Thermoelectric Performance of Alkaline-Earth Isovalently Substituted [bi2ae2o4][coo2]y Single Crystals

Evolution of the Thermoelectric Performance in Low Ca-doped Layered Cobaltite Bi2Sr2Co2Oy

Thermoelectric properties of La-doped Ca–Co–O misfit cobaltites

Thermoelectric Properties of Bi3+ Substituted Co-based Misfit-Layered Oxides

Synthesis and Thermoelectric Properties of Ca2.6Nd0.4Co4O9 Compound

Intergrowth and thermoelectric properties in the Bi–Ca–Co–O system

Scaling behavior in thermoelectric misfit cobalt oxides

Cobalt Substitution Effects in the Spin Ladder Compound Sr14-Xcaxcu24-Ycoyo41

Thermoelectric Properties and Electronic Structure of Ca 3 Co 2 O 6

Research on Properties of Ca<sub>3-x</sub> La <sub>x</sub>Co<sub>4</sub>O<sub>9</sub> Thermoelectric Material with Adding La

Enhanced Thermoelectric Performance of Heavy-Metals (M: Ba, Pb) Doped Misfit-Layered Ceramics: (ca2−xmxcoo3)0.62 (Coo2)

Thermoelectric Properties of the Ca3Co4O9 Ceramics by K+ Substitution

Anisotropic Thermopower and Magnetothermopower in a Misfit-Layered Calcium Cobaltite

Strongly correlated properties of the thermoelectric cobalt oxide Ca3Co4O9

Magnetic field enhanced thermal conductivity and origin of large thermopower in layered cobaltates

Electro-Thermo-Magnetic Effect-Induced Large Thermoelectric Performance of Calcium Cobaltite Nanocomposites

Synthesis and Thermoelectric Properties of (naxca1−x)3co4o9 Ceramics

Electrical Transport and Thermoelectric Properties of Y1−xCaxCoO3 (⩽x⩽0.1) at High Temperatures

Enhancement Of Thermoelectric Performance In Cd-Doped Ca3co4o9 Via Spin Entropy, Defect Chemistry And Phonon Scattering

Thermoelectric Properties Of Ca3co4o9+Delta-Based Polycrystalline Oxides