Abstract:Zinc oxide (ZnO) has a wide direct band gap of 3.37 eV at room temperature and a large excitonic binding energy of 60 meV. In this work, ZnO nanoparticles had been successfully fabricated at low temperature (60 degrees C). The structures, morphologies and optical properties of ZnO nanoparticles were investigated by X-ray diffraction (XRD), a scanning electron microscope (SEM), UV-Visible absorption and photoluminescence (PL) spectra, respectively. Measurement results of XRD showed that the as-prepared ZnO nanoparticles are a random orientation. The nanoparticles are approximately particle shape with an average size of about 50 nm by SEM observation, UV-Vis absorption spectrum indicated that the as-prepared ZnO nanoparticles dispersed in chloroform are highly transparent in the visible region and have a strong absorption band in the UV region, at the same time, we found a sharp absorption edge at near 370 nm. In addition, in the as-prepared ZnO nanoparticles/chloroform solution, both a near band edge (NBE) ultraviolet photoluminescence peak at 372 nm and a defect related deep level emission (DLE) green peak at 513 nm were observed. It suggested that the NBE photoluminescence peak should be attributed to free excitons transition, the DLE green peak should be ascribed to intrinsic defects of the single ionized oxygen vacancy (V-o*) through our research results. Furthermore, we obtained R (R=I-NBE/I-DLE) value as 0.91. This indicates that there are a large amount of single ionized oxygen vacancies in as-prepared ZnO nanoparticles, which results in poor crystalline quality of ZnO nanoparticles.

Selective Growth and Properties of Zinc Oxide Nanostructures

Rod-Like Zinc Oxide Constructed by Nanoparticles: Synthesis, Characterization and Optical Properties

Effect of Solution Concentrations on Crystal Structure, Surface Topographies and Photoluminescence Properties of ZnO Thin Films

Zinc Oxide Nanostructures: Epitaxially Growing from Hexagonal Zinc Nanostructures

Low-temperature growth of uniform ZnO particles with controllable ellipsoidal morphologies and characteristic luminescence patterns.

Catalyst-free Growth and Tailoring Morphology of Zinc Oxide Nanostructures by Plasma-Enhanced Deposition at Low Temperature

Synthesis and Optical Property Study on ZnO Nanostructures Via Vapor Phase Growth

Morphology, Structures and Properties of Zno Nanobelts Fabricated by Zn-Powder Evaporation Without Catalyst at Lower Temperature

Large-scale Synthesis of Zinc Oxide Rose-Like Structures and Their Optical Properties

Zinc Oxide Micro- and Nanoparticles: Synthesis, Structure and Optical Properties

Controllable Preparation and Photocatalytic Activity of ZnO Microstructures with Different Morphology

Controlling Morphologies and Tuning the Related Properties of Nano/Microstructured ZnO Crystallites

Multistep Synthesis, Growth Mechanism, Optical, and Microwave Absorption Properties of ZnO Dendritic Nanostructures

Growth of ZnO Nanoparticles at Low Temperature and Optical Properties

Synthesis and morphology control of ZnO nanostructures in microemulsions.

Preparation and Photoluminescence of ZnO Complex Structures with Controlled Morphology

The Synthesis and Crystallography of Some Novel ZnO Nano- and Micro-Crystals and Structures

Renucleation and Sequential Growth of ZnO Complex Nano/Microstructure: From Nano/Microrod to Ball-Shaped Cluster

Synthesis and Characterisation of Three-Dimensional Dendritic Zno Nanorods

Synthesis and synchrotron light-induced luminescence of ZnO nanostructures: nanowires, nanoneedles, nanoflowers, and tubular whiskers.

Synthesis and Photo-Catalytic Degradation Property of Nano Structured-Zno with Different Morphology