Abstract:In order to improve the thermal conductivity of polypropylene (PP) and expand its applications,low cost com-mercial graphite was used to modify PP and the PP/graphite composites were prepared by using Haake torque rheometer. The ef-fects of graphitefillers with particle size of 2μm and 20μm and their compound on the thermal conductivity and mechanical properties were researched. The results show that increasing graphite content can apparently increase the thermal conductivity of the composites and the composites with 20μm graphite have a higher thermal conductivity. Due to anisotropy of graphite,the in-plane thermal conductivity is apparently higher than the through-plane thermal conductivity. Additionally,mixing the two graphite fillers,controlling the total mass fraction of thefillers to 40%,when the mass ratio of the 2μm graphite and 20μm graphite is 1︰5,the through-plane and in-plane thermal conductivity value reach peak and they are 1.125 W/(m·K) and 2.897 W/(m·K), respectively,which increases by 121%,61% than the compositefilled with 2μm graphite and by 3.6%,20% than the composite filled with 20μm graphite under same contents. When the graphite content increases,the tensile and bending strength of the compositesfilled by graphite with single particle size tend to declinefirstly and then increase,and with the increase of the content of 20μm graphite in the two graphitefillers compound,the mechanical properties of the composites decrease,but the bending strength decreases slightly and the tensile strength is also above 10 MPa.

Preparation of Oriented Graphite/polymer Composite Sheets with High Thermal Conductivities by Tape Casting

Vertically Aligned and Interconnected Graphite and Graphene Oxide Networks Leading to Enhanced Thermal Conductivity of Polymer Composites

Preparation and characterization of graphitized polyimide film/epoxy resin composites with high thermal conductivities

Modeling the In-Plane Thermal Conductivity of a Graphite/polymer Composite Sheet with a Very High Content of Natural Flake Graphite

Preparation of Functionalized Graphene/thermal Conductive Polyurethane Films

Polyimide-assisted Fabrication of Highly Oriented Graphene-Based All-Carbon Foams for Increasing the Thermal Conductivity of Polymer Composites

Enhanced thermal conductivity of epoxy composites reinforced with oriented polydopamine-graphene foam complexed by metal ions

Preparation of graphite flakes/Al with preferred orientation and high thermal conductivity by squeeze casting

Preparation and Properties of Polypropylene/Graphite Composites with High Thermal Conductivity

Significant Enhancement of Thermal Conductivity in Graphite/polyester Composite Via Interfacial Π–π Interaction

Enhanced Thermal Conductivity in Oriented Polyvinyl Alcohol/Graphene Oxide Composites

High Thermal Conductivity in Polydimethylsiloxane Composite with Vertically Oriented Graphene Nanosheets by Liquid-Phase Exfoliation

Research on Graphite/Carbon Fibre/Polypropylene Composites with High Strength and Heat Conductivity

Preparation and Characterization of Large Diameter Pitchbased Carbon Fiber/abs Resin Composites with High Thermal Conductivities

Enhanced thermal conductivity of PP hybrid films induced by filler orientation and laminated structure

Polyimide-assisted Fabrication of Highly Oriented Graphenebased All-Carbon Foams for Increasing the Thermal Of

A highly orientational architecture formed by covalently bonded graphene for achieving high through-plane thermal conductivity of polymer composites

Experiments and Modeling of Thermal Conductivity of Flake Graphite/polymer Composites Affected by Adding Carbon-Based Nano-Fillers

Graphite films/carbon fiber fabric/polyurethane composites with ultrahigh in-plane thermal conductivity and enhanced mechanical properties

Effects Of Heat-Treatment Temperature And Binder Content On The Microstructure And Thermal Conductivity Of Graphite Flake-Carbon Composites

Thermal conductivity and mechanical properties enhancement of CF / PPBESK thermoplastic composites by introducing graphene