Preparation and photocatalytic activity of ZnO/TiO2/SnO2 mixture

Cun Wang,Bo-Qing Xu,Xinming Wang,Jincai Zhao

DOI: https://doi.org/10.1016/j.jssc.2005.09.005

IF: 3.3

2005-01-01

Journal of Solid State Chemistry

Abstract:ZnO/TiO2/SnO2 mixture was prepared by mixing its component solid oxides ZnO, TiO2 and SnO2 in the molar ratio of 4ː1ː1, followed by calcining the solid mixture at 200–1300°C. The products and solid-state reaction process during the calcinations were characterized with powder X-ray diffraction (XRD), thermogravimetric and differential thermal analysis (TG-DTA), UV-Vis diffuse reflectance spectroscopy (UV-Vis DRS) and Brunauer–Emmett–Teller measurement of specific surface area. Neither solid-state reaction nor change of crystal phase composition took place among the ZnO, TiO2 and SnO2 powders on the calcinations up to 600°C. However, formation of the inverse spinel Zn2TiO4 and Zn2SnO4 was detected at 700–900 and 1100–1200°C, respectively. Further increase of the calcination temperature enabled the mixture to form a single-phase solid solution Zn2Ti0.5Sn0.5O4 with an inverse spinel structure in the space group of Oh7-Fd3m. The ZnO/TiO2/SnO2 mixture was photocatalytically active for the degradation of methyl orange in water; its photocatalytic mass activity was 16.4 times that of SnO2, 2.0 times that of TiO2, and 0.92 times that of ZnO after calcination at 500°C for 2h. But, the mass activity of the mixture decreased with increasing the calcination temperature at above 700°C because of the formation of the photoinactive Zn2TiO4, Zn2SnO4 and Zn2Ti0.5Sn0.5O4. The sample became completely inert for the photocatalysis after prolonged calcination at 1300°C (42h), since all of the active component oxides were reacted to form the solid solution Zn2Ti0.5Sn0.5O4 with no photocatalytic activity.