Abstract:Ceria-rare earth solid solutions are known as solid electrolytes with potential applications in solid oxide fuel cell (SOFC). Trivalent rare earth ions enter into solid solution introducing anion vacancies for charge compensation. These oxygen vacancies are quite mobile at moderate temperatures giving rise to a comparatively high ionic conduction. In this study, rare-earth co-doped Ce0.8Sm0.2−xYxO1.9 (x=0.0–0.20) fine powders were prepared by a sol–gel method. The XRD results showed that all powders crystallite calcined at 800°C were single phase with cubic fluorite structure; the average crystallite size was between 24 and 35nm, which was in good agreement with the results of TEM and particle size distribution measurements. The SEM results exhibited that electrolyte pellets sintered at 1400°C were dense, and the relative densities of these pellets were over 99%. Impedance spectra analysis of these electrolytes has been performed at 250–850°C. The results displayed that Ce0.8Sm0.15Y0.05O1.9 and Ce0.8Sm0.1Y0.1O1.9 appeared higher conductivity and lower activation energy than the singly doped ceria with the same dopant concentration (20% trivalent rare earth) at the temperature range of 550–700°C. The maximum power density and the maximum current density for the single SOFC based on the two samples were higher than singly doped sample with the same vacancy concentration. Therefore, it is concluded that co-doping with an appropriate ratio of samarium and yttrium can further improve the electrical performance of ceria-based electrolytes.

Sol-Gel Synthesis and Electrical Properties of Ceria-Based Solid Electrolytes

Sol-gel Synthesis and Properties of Ce1-xPrxO2-x/2 Solid Solutions

Sol-Gel Synthesis and Properties of Ce1-Xgdxo2-X/2 Solid Solutions

Preparation and Characterization of Ceria-based Solid Electrolyte Via Sol-gel Method

Study on Rare Earth Electrolyte of Ce0.9RE0.1O2-δ (RE=Pr, Nd, Sm, Gd, Dy)

Preparation and properties of rare earth co-doped Ce0.8Sm0.2-xYxO1.9 electrolyte materials for SOFC

Improved Electrical Conductivity of Ce0.9Gd0.1O1.95 and Ce0.9Sm0.1O1.95 by Co-Doping

PROGRESS IN STUDY OF CERIA-BASED SOLID ELECTROLYTE MATERIALS

Synthesis, Characterization and Electrical Properties of the New Solid Electrolyte Materials Ce6 Xerxmoo15- (0.0 <x< 1.5)

Study on Sm2O3 and Nd2O3 Co-doped Ceria Based Electrolyte

Properties and application of double alkali earth doped Ce0.9Ca0.1-xSrxO1.90

Microstructure and Electrical Properties of Solid Electrolytes Ce0.9er0.1-Xprxo1.95+Delta

Effect of Nd/Mg Co-Doping on the Electrical Properties of Ceria-Based Electrolyte Materials

Electrical Properties of Ce0.8Sm0.1Nd0.1O2-delta/La10Si6O27 Composite Electrolytes

Synthesis and Characterization of Ce0.8Sm0.2–xPrxO2–δ(x=0.02–0.08) Solid Electrolyte Materials

Electrochemical Study on Co-Doped Ceria–carbonate Composite Electrolyte

Influence of the Sintering Temperature on Electrical Property of the Ce0.8Sm0.1Y0.1O1.9 Electrolyte

Properties of a Ceria-Based ( C 6 S 2 G 2 ) Solid Oxide Electrolyte Sintered with Al 2 O 3 Additive

Study on La and Y co-doped ceria-based electrolyte materials

Effect of the Composition of the Ceramics (MCeMgSr)O2-δ (M = Y, Sm) on the Microstructure, Mechanical and Electrical Properties for Solid Electrolyte

Electrical Conductivity of Ceria Co-Doped with Zr and Re (Re=la,y)