Asymmetric capacitance response from the chemical characteristics of activated carbons in KOH electrolyte
Gangwei Sun,Donghui Long,Xiaojun Liu,Wenming Qiao,Liang Zhan,Xiaoyi Liang,Licheng Ling
DOI: https://doi.org/10.1016/j.jelechem.2011.05.017
IF: 4.598
2011-01-01
Journal of Electroanalytical Chemistry
Abstract:Highlights ► Effect of oxygen-containing functional groups on capacitance behaviors are compared in KOH and H 2 SO 4 electrolyte. ► Asymmetric capacitance behaviors are observed in KOH electrolyte. ► Gravimetric capacitance of positive and negative electrode is 409 F g −1 and 271 F g −1 respectively. Abstract The positive and negative capacitance behaviors of heat-treated activated carbons are separately studied in a three-electrode configuration using 6 M KOH and 1 M H 2 SO 4 as electrolytes. Heat treatment of activated carbons at 400–800 °C causes slight changes in surface area accompanied by a significant removal of oxygen-containing functional groups. Consequently, the specific surface capacitance with a 25% reduction in the negative and an 8% reduction in the positive are monitored in KOH electrolyte. The unequal capacitance reductions as well as the asymmetric CV curves reveal that the negative pseudo-capacitances are much larger than the positive ones in KOH electrolyte. These results could be ascribed to the redox reactions preferring in the negative region. The insertion process of cation also plays a significant effect on the asymmetric capacitance behavior. Compared with the identical electrochemical response in H 2 SO 4 electrolyte, huge difference in the capacitance values of both electrodes in KOH electrolyte will give a less contribution to the cell capacitance. To optimize the cell performance, a suitably increasing the weigh of active materials in the positive, especially for activated carbon with high level of oxygen-containing functional groups, is recommended. Keywords Electrochemical capacitors Oxygen-containing functional groups Pseudo-capacitance Inorganic electrolyte Asymmetric capacitance response 1 Introduction Electrochemical capacitors (ECs) are extensively studied due to their promising properties in terms of energy storage and power supply, which could fill the gap between the secondary batteries and the conventional dielectric capacitors [1–5] . In the last decade, activated carbons (ACs) have been proved as the most promising electrode materials for ECs, due to their high specific surface area, tunable pore structure, adjustable surface chemical characteristics, high chemical stability and favorable price [6–9] . For ACs-based ECs, although charge is stored mainly through the formation of the electrical double-layer, the overall capacitance can also be significantly improved through the introduction of foreign atoms, such as oxygen, nitrogen, phosphorus, etc. [10–15] . These foreign atoms are believed to form the pseudo-capacitance via fast faradic redox reactions. However, the electrochemical events of surface chemistry occurring in carbon materials are very complex, which may take place depending on, for instance, the kind and distribution of heteroatoms on carbon surface, the population of surface functional groups, history of the carbon materials, kind of electrolytes, pHs values, applied electrode potential and cell design, etc. [16–23] . It has been reported that the oxygen-containing functional groups can be categorized into CO-desorbing and CO 2 -desorbing oxides, the former (such as carbonyl, hydroxyl and quinone groups) is responsible for pseudo-capacitance rather than the latter (carboxyl, lactones and anhydrides) [20] . Conway et al. suggested that redox reactions had a large dependence on the pH values of electrolytes [21] . The redox with the quinine/hydroquinone pair required protons to proceed, whereas pyridinic group might be electrochemically active at the working potential of the basic solution [21,22] . Besides, the redox reactions occurring in the positive and negative regions should be different, as different electrolyte ions located and different potentials applied on each electrode [22] . Papers [24–26] compare positive and negative electrode characteristics in acid and alkaline environment. It is clearly indicated in these papers that in the alkaline environment (KOH), the capacitance of negative electrodes is much higher, while in the acidic environment (H 2 SO 4 ), the relationship could be reverse and the capacitances of both electrodes are similar. And a new type of high energy asymmetric capacitor has been developed to enlarges the operating voltage up to 1.5 V in acidic medium [27,28] . The present paper aimed to compare the pseudo-capacitance behaviors in H 2 SO 4 with that in KOH through the separate study of both electrodes. We used a special-designed configuration where a reference electrode was added to the symmetric two-electrode cell. The oxygen-containing functional groups of ACs were changed simply by a heat treatment. Differing from results literature reported that the contribution of pseudo-capacitance in basic medium was significantly lower than that in acidic medium [23] ; we found that the pseudo-capacitance contributed by oxygen-containing functional groups in KOH electrolyte was actually much larger than that in H 2 SO 4 electrolyte, especially for the negative electrode. It was the asymmetric capacitance distribution of both electrodes that mislead us to consider the minor effect of pseudo-capacitance in KOH electrolyte. Based on these results, the mass matching ratio of two electrodes in KOH electrolyte was theoretically optimized to improve the overall capacitance of ECs. 2 Experimental 2.1 Preparations of samples Petroleum coke was chemically activated using KOH (the mass ratio of KOH to coke is 2.5:1) at 800 °C for 2 h under nitrogen atmosphere. The resultant AC (denoted RAC) was then subjected to the heat treatment under a nitrogen flow for 2 h at 400, 500, 600, 700 and 800 °C, respectively. The heat-treated samples were labeled as N – X , where X represented as the heat-treated temperature (HTT). 2.2 Characterization of samples The pore textural characterization of samples was based on the nitrogen adsorption at 77 K (ASAP 2020 M, Micromeritics). Before the measurement, samples were degassed in vacuum at 573 K for at least 12 h. BET surface area ( S BET ) was calculated from a set of adsorption data obtained at relative pressure below 0.3. The pore size distribution was determined from non-local DFT equation using slit-pore model. Elemental analysis was performed using an elemental analyzer (Elementar Co., Vario EL III). XPS spectra were achieved with a Kratos Axis Ultra DLD photoelectron spectrometer using non-monochromatized Al Kα radiation, the source being operated at 15 kV and 10 mA. Prior to elemental analysis and XPS measurement, samples were dried for 2 h at 120 °C. 2.3 Electrochemical measurements Electrodes were made in the form of pellets composed of ACs (85%), polyterafluoroethlyene (5%) and acetylene black (10%). Two-electrode capacitors were built in a Teflon Swagelok® type system with two identical carbon pellets and a porous polymeric separator (Celgard, USA), in which Hg/HgO and Hg/Hg 2 SO 4 placed between the electrodes acted as reference electrode for 6 M KOH and 1 M H 2 SO 4 , respectively. Galvanostatic charge–discharge tests were conducted with the cell voltage range from 0 to 0.9 V using an Arbin SCTS supercapacitor testing system (Arbin instrument, TN, USA). The potential variation of each electrode was automatically recorded during charge–discharge process. The specific discharge capacitance of a single electrode (positive or negative electrode) in a capacitor was calculated according to C = It / m Δ V , where Δ V , I , t and m were the working voltage of each electrode, discharge current, discharge time, and mass of either electrode, respectively. For calculating capacitances of cell, m and Δ V should be the overall weight of both electrodes and the full voltage of the capacitor, respectively. A standard three-electrode configuration was also set up using activated carbon as working electrode, platinum foil and Hg/HgO or Hg/Hg 2 SO 4 as counter electrode and reference electrode, respectively. Cyclic voltammograms (CV) were recorded with a PCI4/300 potentiostat (Gamry, PA, USA) on three-electrode system in the potential range of −0.9 to 0.1 V vs. Hg/HgO and −0.7–0.3 V vs. Hg/Hg 2 SO 4 . Several disks were analyzed in order to obtain reliable data. 3 Results and discussion 3.1 Characteristics of pores structure Fig. 1 presents N 2 adsorption–desorption isotherms and resultant DFT pore size distributions of all samples. The porosity parameters are summarized in Table 1 . All isotherms exhibit a very similar type I isotherm according to the classification of IUPAC, with a typical microporous characteristics. The thermal treatment leads to some decreases of N 2 adsorption amount, corresponding to the textural modifications. When the RAC is treated below 700 °C, there is a slight reduction in the N 2 adsorption volume, and the S BET and V t decrease from 2023 to 1757 m 2 g −1 and from 1.09 to 0.92 cm 3 g −1 , respectively. However when the temperature increases to 800 °C, the texture changes more significantly. The DFT pore size distributions of all samples are almost similar with the pore size range from 0.4 to 3.5 nm, suggesting that the pore size is unchanged but the amount of pores decreases. Apart from the possibility of the pores collapse, the formation of micro-crystalline structure of activated carbons may also lead to the deterioration of the pores texture. 3.2 Characteristics of surface chemistry Table 2 lists the elemental analysis of the raw and heat-treated samples. The RAC contain ca. 88.9% carbon, 0.9% nitrogen, 9.3% oxygen. After the heat treatment, the percentage content of nitrogen is almost similar, being independent on the heat-treated temperature. The carbon percentage content increases gradually with the increase of the HTT, which is at the expense of the remarkable decrease of the oxygen percentage content. XPS characterization of samples is performed to further study the changes of surface chemistry during the heat treatment. The O/C atomic ratios based on the areas of C 1s and O 1s peaks are also summarized in Table 2 . RAC display the highest O 1s /C 1s ratio (0.21). This ratio decrease to 0.16 at the HTT of 400 °C and final to 0.058 at 800 °C. These results suggest that the oxygen functional groups could be removed effectively by the heat treatment. 3.3 Electrochemical characteristics 3.3.1 Asymmetric capacitance response in KOH electrolyte Galvanostatic characteristics have been recorded vs. the Hg/HgO reference electrode in a three-electrode cell. In such a configuration, the performances of each individual electrode (positive and negative) as well as the cell can be monitored separately. Fig. 2 depicts a typical example of the galvanostatic charge–discharge curves at the current density of 0.1 A g −1 . The potential of negative and positive electrodes (right Y -axis) are automatically recorded corresponding to applied cell voltage of 0.9 V (left Y -axis) in KOH electrolyte. When the cell is in the completely discharged state (0.08 V), the positive and negative potential locates at −0.47 and −0.55 V vs. Hg/HgO, respectively. While the cell is in the completely charged state (0.9 V), the positive potential reaches 0.03 V vs. Hg/HgO, whereas the negative potential decreases to −0.87 V vs. Hg/HgO. In our investigations, working potentials of capacitor electrodes shift in the range from −0.87 to 0.03 V, so within a thermodynamic stability electrochemical windows from −0.97 to 0.25 V according to the Nernst equation. A close look at Fig. 3 reveals that the potential range of positive electrode (ΔE + ) is larger than that of negative one (ΔE + > ΔE − ), indicating that the cell voltage splits unequally between two electrodes. The gravimetric capacitances of positive and negative electrodes at 0.1 A g −1 in KOH electrolyte, which are calculated from the galvanostatic charge/discharge measurement, as a functional of HTT are plotted in Fig. 3 a. All negative capacitances are obviously larger than the positive ones. RAC presents the highest capacitances both in negative and positive electrodes, which are 409 F g −1 and 271 F g −1 , respectively. Heat treatment cause unavoidable decrease in gravimetric capacitance for both electrodes, with a remarkable reduction of 182 F g −1 in the negative and relatively slight reduction of 81 F g −1 in the positive. The deterioration of gravimetric capacitance could be associated with the decrease of S BET and the removal of oxygen functional groups. We exclude the effect of S BET through the normalized specific surface capacitance by dividing the S BET of samples. As shown in Fig. 4 , specific surface capacitance of the positive experiences a slight change (<8%), indicating that it mostly depends on porosity characteristics. On the contrary, a significant reduction of specific surface capacitance (from 20.2 to15.0 μF cm −2 , over 25%) is found for the negative causing by the heat treatment. In this case, specific surface capacitance should be contributed from pure electrostatic capacitance and pseudo-capacitance; the former directly is governed by pore-ions electrostatic interaction, whereas the latter is related to the oxygen-containing functional group. Heat treatment leads to the improvement of electrical conductivity, which should play a positive effect on the pore-ions interaction and improve the capacitance values. Therefore, it is apparent that the reduction of capacitance in the negative can be related to the weakened pseudo-capacitance with HTT increasing. Fig. 3 b shows the influence of current density on the difference of gravimetric capacitance value (Δ C ) between negative and positive electrodes. As the average pore size of the active material is large enough to allow the accessible to the electrolyte ions, ion-sieving effect could be eliminated. Such huge differences with respect to gravimetric capacitance of both electrodes would be understood as a consequence of the pseudo-capacitances. Oxygen-containing functional groups exhibit an asymmetric contribution to the capacitance of each electrode, having a more sensitive effect on the improvement of capacitance in the negative electrode. As revealed by Fig. 3 b, Δ C reduces with the HTT increasing. This can be related to the thermal instability of functional groups, which decompose gradually with the intensity of heat-treatment. Consequently, the extra capacitance of the negative electrode produced from functional groups decreases, leading to the reduction of Δ C with the HTT raising. On the other hand, the decrease of Δ C as a function of current density can also be found for each sample. This can be attributed to the electrochemical instability of oxygen-containing functional groups as the cycle increasing and the kinetic limit of redox reaction with the current density increasing. It is worthy to note that Δ C for RAC presents the more prominent reduction as compared to that of other samples. This is due to the fact that most of oxygen-containing functional groups in RAC are electrochemical instability as reported in literature [20] . With the cycling increasing, a large amount of groups would be removed. Meanwhile, the high content of functional groups would also increase the electrochemical resistance of RAC. As a consequence, Δ C for RAC decreases dramatically at the current density of 4 A g −1 , being lower than that for N400 and N500. CV curves of all samples in KOH electrolyte (shown in Fig. 5 ) exhibit a clear deviation from the ideal rectangular shape, shifting to the negative potential. The response capacitances in the negative region are much higher than that in the positive ones. With the HTT increasing, the distortion degree of CV curves becomes less, and CV for sample N800, is more excellent. The variation of both positive and negative capacitances with the HTT increasing is in good agreement with the results of galvanostatic charge–discharge tests. With the voltage sweep rate increasing, response capacitances of both electrodes become similar, which is linked to the limited kinetic process involving in the redox reactions in the negative potential range. 3.3.2 Symmetric capacitance response in H 2 SO 4 electrolyte In H 2 SO 4 electrolyte, the gravimetric capacitances of positive and negative electrodes at 0.1 A g −1 are plotted in Fig. 6 . Unlike the remarkable capacitance difference between the positive and negative electrode in KOH electrolyte, the negative electrode in H 2 SO 4 electrolyte demonstrates only slightly higher capacitance as compared to positive one. Heat treatment also causes a significant capacitance reduction of both electrodes to the same extent. Fig. 7 demonstrates that CV recorded in a three-electrode cell shows a relatively symmetric shape in positive and negative regions. Well-defined redox humps can be observed from RAC both in the anodic and cathodic regions. Redox peaks are significantly small for the heat-treated samples and almost negligible for N800. In H 2 SO 4 electrolyte, the almost same capacitances of both electrodes and symmetric CV shape reveal that the pseudo-capacitance equally takes place in the positive and negative regions. 3.3.3 Comparison of capacitance behaviors in H 2 SO 4 and KOH electrolyte A separate study of capacitive performance of each electrode reveals oxygen-containing functional groups exhibit an asymmetric contribution to the capacitance, having a more sensitive effect on the improvement of capacitance of the negative electrode in KOH electrolyte, whereas, the pseudo-capacitances in H 2 SO 4 electrolyte contribute to the overall capacitance of each electrode to the same extent. The pseudo-capacitances involving in the oxygen-containing functional group in H 2 SO 4 solution are widely referred [29,30] . The most well documented case is the oxidation/reduction of hydroquinone/quinine groups. These quinine groups are responsible for a significant percentage of the cell capacitance. Even if the mechanisms of complex reactions are not thoroughly understood until now, we could conclude, at least in partial, that oxygen-containing functional groups exhibit symmetric capacitive behaviors in both electrode. On the contrary, with the presence of functional groups, an equilibrium reaction may occur in the carbon negative electrode especially in KOH medium [22,31,32] : (Reaction (1)) - C x O - + K + ↔ - C x O - ‖ K + (Reaction (2)) - C x O + e - 1 + K + ↔ - C x - OK These reactions may facilitate an excess specific capacitance in the negative electrode due to interaction between surface functional groups and cation. Additionally, as calculated according to the Nernst equation, underpotential hydrogen adsorption/desorption process might be occur at −0.9 V vs. Hg|HgO as follows [33] : (Reaction (3)) - C x - O + e - 1 + H 2 O ↔ - C x - OH + OH - In alkaline electrolytes, water is reduced to hydrogen atom which can be adsorbed on the surface and electrochemical oxidation during the discharge, thus providing extra pseudo-capacitance. Finally, the cation insertion process could also account for higher capacitance in negative region. In order to prove the occurrence of K + insertion reaction, the capacitive performances of all samples in 0.5 M K 2 SO 4 electrolyte are investigated. For all samples, except for N800, capacitance in negative electrode is higher than that in positive one as presented in Fig. 8 . And the differences in capacitance decrease with HTT increasing. For neutral medium, the effect of oxygen-containing functional groups can be negligible. The extra capacitance in negative electrode can be ascribed to insertion of K + into the lattice of activated carbons under effect the electric field. After subjected to heat treatment, the rearrangement and reorganization of carbon microcrystal would cause the passivation and closure of exposed sites. Consequently, the effect of insertion is diminished. As the aforementioned analysis, pseudo-capacitance resulted from oxygen-containing functional groups should exhibit more significant in KOH than in H 2 SO 4 electrolyte. Nevertheless, Fig. 9 shows that rather similar deterioration of capacitance in both electrolytes. Results can be ascribed to an asymmetric capacitance behavior of functional groups in KOH electrolyte which would weaken its contribution to the improvement of capacitance properties. 3.3.4 Mass matching of both electrodes in KOH electrolyte for asymmetric ECs Since pseduocapacitance exhibits an asymmetric distribution between the positive and negative electrodes in KOH electrolyte, the poor capacitive performance of the positive electrode would limit the capacitance of whole device [34,35] . Therefore, mass matching between two electrodes is necessary for maximizing the capacitance of cell according to the capacitive characteristics of samples. The capacitance of the cell ( C c ) is determined by the series equivalent circuit consisting of the positive capacitance C P and negative capacitance C N , according to the following equation: (Equation (1)) 1 / C c = 1 / C p + 1 / C N If the mass ratio of positive to negative electrode is r , the specific capacitance C (F g −1 ) of cell should be expressed as: (Equation (2)) C c = C P C N / ( C N + rC R ) 1 + 1 / r The capacitance values (e.g. C P , 274 F g −1 ; C N , 401 F g −1 for RAC) at the current density of 0.1 A g −1 are adopted for calculation. The dependence of the cell capacitance of asymmetric ECs on the mass ratio is shown in Fig. 10 . A strong correlation of specific capacitance with the mass ratio is observed, with the optimum mass ratio of 1.2 for RAC, 1.1 for N600 and 1.00 for N800. This suggests that improvement in the capacitor performance can be achieved by increasing the weight of active materials in positive electrode, especially for these materials with high level of oxygen functional groups. However, as revealed from theatrical calculation, we find that the improvement of capacitance is negligible through mass matching, even though difference in capacitance of both electrodes is huge. Additionally, it should be clear that the optimum mass ratio is not constant at various charge/discharge currents, since the variation extent of capacitance of each electrode differs along with the charge/discharge current. 4 Conclusion The electrochemical performances of activated carbons are tested in a three-electrode system to evaluate separately the positive and negative capacitive behavior. In KOH electrolyte, the negative capacitance is remarkably larger that the positive one, whereas the nearly same capacitance values for each electrode are found in H 2 SO 4 electrolyte. Heat treatment of activated carbons causes slight changes in pore texture accompanied by a significant reduction of oxygen content. Consequently, the positive and negative capacitances as well as the cell capacitance of EDLC decrease both in KOH and H 2 SO 4 electrolyte. The remarkable decrease in negative and slight decrease in positive specific surface capacitance, as well as the asymmetric shapes in CV curves, confirms that the contribution of pseudo-capacitances in the negative electrode are much larger than that in the positive electrode in KOH electrolyte. Compared with symmetric electrochemical responses on each electrode in H 2 SO 4 electrolyte, the asymmetric behavior of pseudo-capacitance in KOH electrolyte could give a less contribution to the total cell capacitance. Thus, optimum mass matching ratio between positive and negative electrodes should be recommended to improve the total supercapacitor performance. Acknowledgments This work was partly supported by National Science Foundation of China (No. 50730003 ), National Project of Scientific and Technical Supporting Programs funded by Ministry of Science & Technology of China (No. 2007BAE55B00 ), National High Technology Research and Development Program of China (No. 2007AA05Z311 ), and Program for New Century Excellent Talents in University ( NCET-07-0285 ). References [1] M. Winter R.J. Brodd Chem. Rev. 104 2004 4245 [2] H.S. Chen T.N. Cong W. Yang C.Q. Tan Y.L. Li Y.L. Ding Prog. Nat. Sci. 19 2009 291 [3] I. Hadjipaschalis A. Poullikkas V. Efthimiou Renew. Sust. Energy Rev. 13 2009 1513 [4] A. Burke Electrochim. Acta 53 2007 1083 [5] A. Lewandowski M. Galinski J. Power Sources 173 2007 822 [6] E. Frackowiak Phys. Chem. Chem. Phys. 9 2007 1774 [7] J.S. Huang B.G. Sumpter V. Meunier Chem. Eur. J. 14 2008 6614 [8] L.L. Zhang X.S. Zhao Chem. Soc. Rev. 38 2009 2520 [9] A.G. Pandolfo A.F. Hollenkamp J. Power Sources 157 2006 11 [10] D. Hulicova-Jurcakova A.M. Puziy O.I. Poddubnaya F. Suarez-Garcia J.M.D. Tascon G.Q. Lu J. Am. Chem. Soc. 131 2009 5026 [11] D. Hulicova-Jurcakova M. Seredych G.Q. Lu T.J. Bandosz Adv. Funct. Mater. 18 2008 1 [12] C.X. Zhang D.H. Long B.L. Xing W.M. Qiao R. Zhang L. Zhan X.Y. Liang L.C. Ling Electrochem. Commun. 10 2008 1809 [13] D. Hulicova-Jurcakova M. Seredych G.Q. Lu N.K.A.C. Kodiweera P.E. Stallworth S. Greenbaum T.J. Bandosz Carbon 47 2009 1576 [14] H.L. Guo Q.M. Gao J. Power Sources 186 2009 551 [15] E. Raymundo-Pinero F. Leroux F. Beguin Adv. Mater. 18 2006 1877 [16] I.Y. Jang H. Muramatsu K.C. Park Y.J. Kim M. Endo Electrochem. Commun. 11 2009 719 [17] G. Lota B. Grzyb H. Machnikowska J. Machinikowski E. Frackowiak Chem. Phys. Lett. 404 2005 53 [18] N.D. Kim W. Kim J.B. Joo S. Oh P. Kim Y. Kim J. Yi J. Power Sources 180 2008 671 [19] M. Seredych D. Hulicova-Jurcakova G.Q. Lu T.J. Bandosz Carbon 46 2008 1475 [20] P.Z. Cheng H.S. Teng Carbon 41 2003 2057 [21] H.A. Andreas B.E. Conway Electrochim. Acta 51 2006 6510 [22] D. Hulicova J. Yamashita Y. Soneda H. Hatori M. Kodama Chem. Mater. 17 2005 1241 [23] V. Ruiz C. Blanco E. Raymundo-Pinero V. Khomenko F. Beguin R. Santamaria Electrochim. Acta 52 2007 4969 [24] K. Jurewicz R. Pietrzak P. Nowicki H. Wachowska Electrochim. Acta 53 2008 5469 [25] K. Jurewicz K. Babel R. Pietrzak S. Delpeux H. Wachowska Carbon 44 2006 2368 [26] R. Pietrzak K. Jurewicz P. Nowicki K. Babel H. Wachowska Fuel 86 2007 1086 [27] E. Raymundo-Pinero K. Kierzek J. Machnikowski F. Beguin Carbon 44 2006 2498 [28] V. Khomenko E. Raymundo-Pinero F. Beguin J. Power Sources 195 2010 4234 [29] B.E. Conway Electrochemical Supercapacitors 1999 Kluwer Academic/Plenum New York [30] H. Malmberg V. Ruiz C. Blanco R. Santamaria A. Lundblad P. Bjornbom Electrochem. Commun. 9 2007 2320 [31] H.F. Li H. Xi S. Zhu Z. Wen R. Wang Micropor. Mesopor. Mater. 96 2006 357 [32] H. Oda A. Yamashita S. Minoura M. Okamoto T. Morimoto J. Power Sources 158 2006 1510 [33] V. Ruiz H. Malmberg C. Blanco A. Lundblad P. Bjornbom R. Santamaria J. Electroanal. Chem. 618 2008 33 [34] J.L. Li F. Gao J. Power Sources 194 2009 1184 [35] Y.H. Wen J. Cheng G.P. Cao Y.S. Yang J. Appl. Electrochem. 37 2007 543
What problem does this paper attempt to address?
-
The Capacitances of the Negative and Positive Electrodes of Supercapacitors, Using Nitrogen-Doped Mesoporous Carbons As the Active Materials, in Different Electrolytes
Chen Ming-qi,Pan Min,Tian Meng,Wang Ji-tong,Long Dong-hui
DOI: https://doi.org/10.1016/j.carbon.2017.12.087
IF: 10.9
2018-01-01
Carbon
Abstract:Nitrogen-doped mesoporous carbons (NMCs) with controllable nitrogen contents and similar pore structures were prepared by a sol-gel process coupled with hard templating method, using melamine, phenol and formaldehyde as precursors, and colloidal silica as hard templating. The effects of nitrogen doping content on the asymmetric capacitance of the mesoporous carbon in H2SO4, KOH and Et4NBF4/PC electrolyte were systematically investigated. The nitrogen-doping has significantly improved the capacitance performance, and both positive and negative electrodes deliver the highest specific capacitance at a nitrogen-doping content of around 8%. In the KOH electrolyte, the negative pseudo-capacitances is significantly higher than that of the positive ones, and the capacity difference is up to 57. 9 F/g. In H2SO4 electrolyte, the nearly same capacitances for each electrode are found for all samples. And in the organic Et4NBF4/PC system, the increased capacitance is mainly attributed to the negative. The study on asymmetrical capacitance response of nitrogen-doped mesoporous carbon paves the way for optimizing the ratio of positive and negative electrode active materials, leading a higher energy density.
-
Effect of Alkaline-Basic Electrolytes on the Capacitance Performance of Biomass-Derived Carbonaceous Materials
Boryana Karamanova,Antonia Stoyanova,Maria Shipochka,Svetlana Veleva,Radostina Stoyanova
DOI: https://doi.org/10.3390/ma13132941
IF: 3.4
2020-06-30
Materials
Abstract:The present work explores in detail the effect of alkaline-basic electrolytes on the capacitance performance of biomass-derived carbonaceous materials used as electrodes in symmetric supercapacitors. The proof-of-concept is demonstrated by two commercial carbon products (YP-50F and YP-80F, Kuraray Europe GmbH, Vantaa, Finland), obtained from coconuts. The capacitance performance of YP-50F and YP-80F was evaluated in three types of basic electrolytes: 6 M LiOH, 6 M NaOH and 6 M KOH. It was found that the capacitance performance of YP-50F improved in the following order: NaOH < LiOH < KOH; Meanwhile, for YP-80F, the order changes to LiOH < NaOH < KOH. After 1000 cycles, the cycling stability of both YP-50F and YP-80F increased in the order NaOH < LiOH < KOH. This order of performance improvement is determined by both the electrolyte conductivity and the interaction between the functional groups of carbonaceous materials and alkaline electrolytes. The reactivity of the functional groups was assessed by postmortem SEM/EDS and X-ray photoelectron spectroscopy (XPS) analyses of the electrodes after prolonged cycling.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
-
Non-porous activated mesophase carbon microbeads as a negative electrode material for asymmetric electrochemical capacitors
Cheng Zheng,Jichao Gao,Masaki Yoshio,Li Qi,Hongyu Wang
DOI: https://doi.org/10.1016/j.jpowsour.2012.12.041
IF: 9.2
2013-01-01
Journal of Power Sources
Abstract:Non-porous activated (mesophase carbon microbeads) MCMBs have been prepared by calcinations at 1100 °C and then activated with KOH at 800 °C in a nitrogen flow. This spherical carbon material could store a large number of ions after having been subjected to an “extra” electrochemical activation. It has been used as the negative electrode for asymmetric electrochemical capacitors of MCMB/activated carbon. The charge storage mechanism at the MCMB negative electrode has been investigated by XRD and TEM. The results demonstrate that the intercalation of quaternary alkyl ammonium cations from the electrolytes causes an irreversible expansion of interlayer spaces between adjacent carbon layers, which provides accommodation for subsequent ion adsorption. A series of quaternary alkyl ammonium-based electrolytes have been tested in the capacitors and the effect of the cation has been studied. Spiro-(1,1′)-bipyrrolidinium increases the storage ability most significantly although it is not the lightest quaternary alkyl ammonium cation.
-
Synthesis and Electrochemical Performances of Fluffy Carbonized Hexagonal KCoPO4 as Pseudocapacitive Electrode for High performing Hybrid Supercapacitor Applications
Krishna Gopal Nigam,Abhijeet Kumar Singh,Soham Mukherjee,Preetam Singh
DOI: https://doi.org/10.1002/slct.202403266
2024-10-29
ChemistrySelect
Abstract:Carbonized KCoPO4 synthesized via sol‐gel method shows intercalative pseudocapacitance due to storage of OH− ion through involvement of Co2+/3+ redox couple in aqueous 2 M KOH electrolyte delivering energy density of 121.1 Wh/kg and a power density of 6945 W/kg in asymmetric (AC// KCoPO4) full cell in the potential window of 1.5 V. Electrochemical energy storage is one of the effective ways that can address the mentioned issues as alternative energy/power produced through solar or windmills can effectively be stored for continuous usage. Hybrid/Asymmetric supercapacitors can deliver a significant amount of power density as well as increased energy density with better rate capability and longer lifespan. The fluffy carbonized hexagonal KCoPO4 synthesized via a simple sol‐gel method accompanied by calcination has delivered high capacitance and longer cyclibility as a positive electrode in aqueous asymmetric supercapacitors. The fluffy carbonized hexagonal KCoPO4 exhibited a specific capacitance equal to 725 F/g at 0.5 A/g current density with excellent cyclic stability. The predominant intercalative pseudocapacitive charge storage behavior seems to be the reason behind the high capacitance of the electrode due to the active involvement of Co2+/3+ redox couple mediate charge storage as intercalative (inner) and capacitive, (outer) surface charges storage on the electrode were close to 37 % and 63 % respectively. Aqueous Asymmetric supercapacitor mode with KCoPO4 being a positive electrode and activated carbon being a negative electrode (KCoPO4//AC) was designed to address its performance in 2 M KOH aqueous electrolyte. The fabricated device in AASc mode (AC//KCoPO4) achieved the highest energy density close to 121.1 Wh/kg with a high power density of 6945 W/kg in the potential window of 1.5 V in 2 M KOH electrolyte.
chemistry, multidisciplinary
-
Preparation and Electrochemical Properties of PF-based Activated Carbon
ZHANG Minmin,TIAN Yanhong,ZHANG Xuejun,MA Xiaofeng
DOI: https://doi.org/10.3969/j.issn.0438-1157.2012.07.047
2012-01-01
Abstract:Activated carbon serving as electrode materials for supercapacitors were prepared by a polymer blend carbonization and steam activation method using phenol formaldehyde resin(PF)as carbon precursor and polyethylene glycol(PEG)as pore-forming agent.Heating program was determined by the pyrolysis behavior of PF,PEG and their blend(PF-PEG)in the heating process characterized by the TG.The specific surface area and pore structure parameter of the activated carbon were calculated by the N2-BET method.Galvanostatic charge-discharge,cyclic voltammetry and alternating current impedance were used to characterize electrochemical performance of activated carbon.Activation temperature,water vapor flow rate and activation time affected the pore structure and electrochemical performance of activate carbon.The results showed that with increasing activation temperature and increasing activation time,the capacitance increased.At activation temperature of 900℃,steam flow rate of 1 ml·min-1 and activation time of 2 h,the structure and properties of prepared activated carbon were better.Its pore size was mainly smaller than 2 nm.With electrolyte solution 1 mol · L-1 KOH/H2O solution,its capacitance reached 105.4 F·g-1 with a traditional three-electrode test system,and cycling performance was better.
-
Mesoporous Carbon Materials As Electrodes for Electrochemical Double-Layer Capacitor
Park Sea,Liang Chengdu,Sheng Dai,Dudney Nancy,DePaoli David
DOI: https://doi.org/10.1557/proc-0973-bb07-04
2006-01-01
Abstract:Nanostructured carbon materials with a regular array and narrow size distribution of mesopores have been synthesized at Oak Ridge National Laboratory via the self-assembly of block copolymers as soft templates. One promising application for these materials is as electrodes for electrochemical double-layer capacitors. To evaluate the performance, electrodes were prepared by coating the precursor onto fibrous carbon paper, followed by curing and pyrolysis at 850°C. The resulting mesoporous carbon has a surface area of 310 m 2 /g and an average pore size of 8.5 nm. Results from cyclic voltammetry and impedance spectroscopy experiments using a sulfuric acid electrolyte showed high specific capacitance values of up to 300 F/g. For comparison, a commercially available aerogel carbon coated paper was also examined.
-
Performance of Electric Double Layer Capacitors Using Active Carbons Prepared from Petroleum Coke by Koh and Vapor Re-Etching
XF Wang,DZ Wang,J Liang
2003-01-01
Abstract:The electrochemical storage of energy in a special kind of active carbon materials used as capacitor electrodes is considered. Petroleum coke was used for preparation of carbons with different porosities by KOH and vapor etching with catalysis of FeCl3 in turn. Carbon electrodes were fabricated and used as electrodes of double layer capacitors. Nitrogen adsorption was used to characterize the porous structure of the carbons. The electrochemical performance of the capacitors in 6 mol/L KOH was investigated with constant current charge and discharge experiments. A specific capacitance larger than 160 F/g was achieved with an electrode composed of 75% active carbon with a specific surface area of 1180 m(2)/g and 20% graphite as conductive agent. Evaluation of capacitor performance was conducted by different techniques, e.g. voltammetry and impedance spectroscopy. Characteristics of the capacitor were also discussed. A hybrid power source consisting of nickel- hydrogen and double layer capacitor was demonstrated by powering successfully a simulated power load encountered in communication equipment.
-
Activated 2D biocarbon nanosheets from kapok fiber as an electrode material for supercapacitor with high energy density in redox electrolyte
Xi Zheng,Ze-Le Lei,Jun-Rui Wang,Qiu-Feng Lü
DOI: https://doi.org/10.1016/j.biombioe.2024.107063
IF: 5.774
2024-01-21
Biomass and Bioenergy
Abstract:Water-based biocarbon as an electrode material of supercapacitor for energy storage equipment has been widely studied because of its simple preparation, low cost, environmental friendliness and good cycle stability, but its low specific capacitance and energy density are the keys to hinder its development. In this study, 2D biocarbon nanosheets from kapok fibers were prepared via KOH activation. AC KF -2, an as-prepared activated biocarbon with an alkali-carbon mass ratio of 5:1, had a very high specific surface area of 3359.2 m 2 /g and a high pore volume of 2.1415 m 3 /g. Thus, AC KF -2 exhibits a high specific capacitance of 405 F/g at a current density of 1 A/g in a 6 mol/L KOH electrolyte. To further improve the electrochemical performance of AC KF -2, two redox additives, K 3 Fe(CN) 6 and K 4 Fe(CN) 6 , were chosen as novel redox electrolytes. At a current density of 10 A/g, AC KF -2 showed a superhigh specific capacitance of 3380 F/g in the 1 mol/L H 2 SO 4 electrolyte with adding K 3 Fe(CN) 6 and K 4 Fe(CN) 6 . A symmetrical-supercapacitor device consisting of AC KF -2 and the new-type redox electrolyte can achieve an extremely high energy density of 264.1 Wh/kg at a high power density of 4593 W/kg. Therefore, this study provides a new energy storage scheme that can greatly improve the water-based carbon supercapacitor.
energy & fuels,biotechnology & applied microbiology,agricultural engineering
-
The Electrode/Electrolyte Interface in MXene-Based Electrochemical Capacitors
Masoud Foroutan Koudahi,Elzbieta Frackowiak
DOI: https://doi.org/10.1149/ma2023-02602906mtgabs
2023-12-22
ECS Meeting Abstracts
Abstract:The operating voltage of electrochemical capacitor (EC) in aqueous medium is considerably limited due to the theoretical stability of water (1.23V). Hence, the delivered energy density of such systems is restricted compared to that of batteries. A traditional approach to tackle this issue is to focus on improving the capacitance rather than the working voltage of ECs. Especially, combining traditionally used carbons with pseudocapacitive materials has been investigated by many researchers. Adopting this strategy improves the delivered capacity of the system, but key metrics such as a power performance and cycle life of ECs may face a serious failure. The slow nature of faradaic reactions affects the frequency response, while the parasitic activities downgrades the favorable cyclability of the device. Hence, a realistic pathway to improve the energy performance of ECs must be taken. Transition metal carbides, carbonitrides, and nitrides (MXenes) are a new family of 2D layered materials. They have the general formula of M n+1 X n , in which M indicates the transition metal, like Ti, Mo, Nb, etc., and X is carbon or nitrogen. Considering favorable properties such as a high conductivity and the ability of cation intercalation, many ECs designs based on MXenes have been reported. Nevertheless, there is a lack of clear elucidation of the charge storage mechanism in these materials. Here, the interface of electrode-electrolyte was studied to gain a better insight into the hydrogen storage mechanism and overpotential of MXenes (Ti 3 C 2 T x ) in acidic and neutral media. It has been found that MXene-based ECs are suffering from an unbalanced capacitive performance between negative and positive electrodes. Especially, a low capacitance in the positive potential range limits the cell voltage to 0.8V and 1.3V in 1M H 2 SO 4 and 1M Li 2 SO 4 , respectively. To extend the cell voltage, self-standing composites based on 3D graphene and Ti 3 C 2 T x were designed. Interestingly, it was observed that during the negative polarization, a significant redox couple activity was observed at the surface of 3DG/ Ti 3 C 2 T x composite electrode. The working potential of the positive electrode was enlarged using micro/mesoporous Black Pearl (BP2000) as electrode material. The realized asymmetric cell was operated in a wider potential window. A higher expansion was realized after balancing the charge of both electrodes. The addition of redox-active salt (KI) to the electrolyte medium improved the capacitive performance of the positive electrode, due to the activity of iodide/iodine species. Excessive increase of the positive electrode capacity was further equalized by balancing the mass of electrodes. In the neutral medium, an asymmetric design of the cell based on Ti 3 C 2 T x (negative electrode) and BP2000 (positive electrode) allowed the cell to operate in a broad range of voltage (up to 2V) with a stable cycling (more than 7000 cycles). The prepared electrodes were characterized using different physiochemical techniques, including XRD, XPS, BET, and SEM analyses. For the electrochemical characterization in two and three-electrode cells, electrodes in the form of pellets or self-standing discs were utilized. The performance of EC cells was studied by cyclic voltammetry, galvanostatic charge-discharge, and electrochemical impedance spectroscopy.
-
Electrochemical performance of lithium ion capacitors with different types of negative electrodes
Meirong Yuan,Weiqiang Liu,Yongfa Zhu,Yongjin Xu
DOI: https://doi.org/10.1134/S1023193514020074
2014-01-01
Russian Journal of Electrochemistry
Abstract:The electrochemical properties of various commercial carbon materials (activated carbon (AC), graphite (GP) and hard carbon (HC)) have been investigated for use as negative electrode for lithium ion capacitors. The rate capabilities and cycle durabilities are tested up to 20 C and 1000 cycles using full cell configurations. It is found that the lithium ion could not efficiently intercalate into the activated carbon materials. The symmetrical AC/AC capacitor shows good cycle durabilities at 10 C with capacity of 17 mA h g −1 . The asymmetrical capacitors AC/GP and AC/HC with intercalated negative electrodes show higher capacities than that of AC/AC capacitor. Moreover, the AC/HC has better rate capabilities than AC/GP.
-
Investigating electrochemical impedance and performance variation in nanostructured Mn3O4/activated carbon/reduced graphene oxide asymmetric supercapacitors with different electrolytes
Aishwarya Jayakumar,Sivakumar Thiripuranthagan,Mohamed Ismail Mohamed Abubakkar,Elangovan Erusappan
DOI: https://doi.org/10.1007/s10800-024-02189-7
IF: 2.925
2024-10-03
Journal of Applied Electrochemistry
Abstract:The synthesis of Mn 3 O 4 nanoparticles and activated carbon/reduced graphene oxide (AC/rGO) nanocomposite involved surfactant-assisted chemical precipitation and sonochemical methods, respectively, to produce high-quality electrode materials. The morphology of the spherical Mn 3 O 4 nanoparticles and the wrinkled sheet-like structure of rGO were found to enhance the electrochemical performance and stability of the electrodes significantly. Electrochemical investigations were conducted using two electrolytes: 2 M KOH and LiNO 3 . In half-cell analyses, Mn 3 O 4 and AC/rGO exhibited specific capacitances of 138 F g −1 and 609 F g −1 , respectively, with 2 M KOH, and 104 F g −1 and 49.8 F g −1 with 2 M LiNO 3 electrolyte, at 1 A g −1 . The observed differences in performance were discussed regarding ionic radius, ionic conductivity, and diffusional coefficient of ions. Furthermore, asymmetric supercapacitor pouch cell devices (Mn 3 O 4 //AC/rGO, MAGASC) were fabricated employing both electrolytes, demonstrating enhanced electrochemical performance. The MAGASC pouch cells exhibited specific capacitances of 273 F g −1 and 130 F g −1 at. 100 mV s −1 with KOH and LiNO 3 electrolytes, respectively. Energy and power density were measured to be 35.2 Wh kg −1 and 1.4 kW kg −1 for KOH electrolyte, and 10.9 Wh kg −1 and 1.6 kW kg −1 for LiNO 3 electrolyte at 0.6 A g −1 . Electrochemical impedance spectroscopy (EIS) analysis revealed a lower equivalent series and charge transfer resistance for MAGASC with KOH electrolyte than for ASC pouch cells with LiNO 3 electrolyte. Complex capacitance and relaxation time constant of the MAGASC were determined using EIS data to analyze frequency behavior. Moreover, the ASC pouch cell demonstrated excellent cyclic stability, retaining 90% of its initial capacitance over 5000 cycles in both electrolytes. These findings underscore the superior energy storage capacity of MAGASC with KOH electrolyte and its broader operating potential with LiNO 3 electrolyte.
electrochemistry
-
Understanding the pore-structure dependence of supercapacitive performance for microporous carbon in aqueous KOH and H2SO4 electrolytes
Mingzhe Liu,Xinping Yang,Xiaozhong Wu,Xin Wang,Yanyan Li,Fanteng Ma,Jin Zhou
DOI: https://doi.org/10.1016/j.electacta.2021.139422
IF: 6.6
2022-01-01
Electrochimica Acta
Abstract:Fifteen microporous carbons with variable nanotextural characteristics were prepared by KOH activation through tuning the KOH/carbon ratio and activation temperature. The prepared porous carbons have a high ratio of micropores and specific surface area up to 95% and 1410 m2 g−1, respectively. Combining the pore-structure analyzes and electrochemical measurements in aqueous KOH and H2SO4 electrolytes, it is shown that the complexity of the pore structure has a significant effect on the electrochemical performance. The solvated/naked K + can penetrate across the narrow pore entrance of the microporous carbons with an average pore size smaller than 0.6 nm and form electric double-layer (EDL) capacitance, while solvated/naked SO4 2− cannot due to its larger ionic size. However, the penetration of SO4 2− followed by hydrated H + become available when the average pore size is larger than 0.6 nm. With the combination of pseudocapacitance and EDL capacitance, microporous carbon shows a much higher supercapacitive performance in H2SO4 than that in KOH electrolyte. This work on pore-structure dependence of supercapacitive performance paves a guide for tailoring pore-structure suitable for aqueous KOH and H2SO4 electrolytes.
electrochemistry
-
First-Principles-Based Insight into Electrochemical Reactivity in a Cobalt-Carbonate-Hydroxide Pseudocapacitor
Kenji Oqmhula,Takahiro Toma,Ryo Maezono,Kenta Hongo
DOI: https://doi.org/10.1021/acsomega.2c07362
IF: 4.1
2023-02-09
ACS Omega
Abstract:Cobalt carbonate hydroxide (CCH) is a pseudocapacitive material with remarkably high capacitance and cycle stability. Previously, it was reported that CCH pseudocapacitive materials are orthorhombic in nature. Recent structural characterization has revealed that they are hexagonal in nature; however, their H positions still remain unclear. In this work, we carried out first-principles simulations to identify the H positions. We then considered various fundamental deprotonation reactions inside the crystal and computationally evaluated the electromotive forces (EMF) of deprotonation (V dp). Compared with the experimental potential window of the reaction (<0.6 V (vs saturated calomel electrode (SCE)), the computed V dp (vs SCE) value (3.05 V) was beyond the potential window, indicating that deprotonation never occurred inside the crystal. This may be attributed to the strong hydrogen bonds (H-bonds) that formed in the crystal, leading to structural stabilization. We further investigated the crystal anisotropy in an actual capacitive material by considering the growth mechanism of the CCH crystal. By associating our X-ray diffraction (XRD) peak simulations with experimental structural analysis, we found that the H-bonds formed between CCH planes (approximately parallel to the ab-plane) can result in 1-D growth (stacked along the c-axis). This anisotropic growth controls the balance between the total "non-reactive" CCH phases (inside the material) and the "reactive" hydroxide (Co(OH)2) phases (surface layers); the former stabilizes the structure, whereas the latter contributes to the electrochemical reaction. The balanced phases in the actual material can realize high capacity and cycle stability. The results obtained highlight the possibility of regulating the ratio of the CCH phase versus the Co(OH)2 phase by controlling the reaction surface area.
-
Electrochemical Performance of Chemically Activated Carbons from Sawdust as Supercapacitor Electrodes
Meruyert Nazhipkyzy,Mukhtar Yeleuov,Shynggyskhan T Sultakhan,Anar B Maltay,Aizhan A Zhaparova,Dana D Assylkhanova,Renata R Nemkayeva
DOI: https://doi.org/10.3390/nano12193391
2022-09-28
Abstract:Activated carbons (ACs) have been the most widespread carbon materials used in supercapacitors (SCs) due to their easy processing methods, good electrical conductivity, and abundant porosity. For the manufacture of electrodes, the obtained activated carbon based on sawdust (karagash and pine) was mixed with conductive carbon and polyvinylidene fluoride as a binder, in ratios of 75% activated carbon, 10% conductive carbon black, and 15% polyvinylidene fluoride (PVDF) in an N-methyl pyrrolidinone solution, to form a slurry and applied to a titanium foil. The total mass of each electrode was limited to vary from 2.0 to 4.0 mg. After that, the electrodes fitted with the separator and electrolyte solution were symmetrically assembled into sandwich-type cell construction. The carbon's electrochemical properties were evaluated using cyclic voltammetry (CV) and galvanostatic charge-discharge (CGD) studies in a two-electrode cell in 6M KOH. The CV and CGD measurements were realized at different scan rates (5-160 mV s-1) and current densities (0.1-2.0 A g-1) in the potential window of 1 V. ACs from KOH activation showed a high specific capacitance of 202 F g-1 for karagash sawdust and 161 F g-1 for pine sawdust at low mass loading of 1.15 mg cm-2 and scan rate of 5 mV s-1 in cyclic voltammetry test and 193 and 159 F g-1 at a gravimetric current density of 0.1 A g-1 in the galvanostatic charge-discharge test. The specific discharge capacitance is 177 and 131 F g-1 at a current density of 2 A g-1. Even at a relatively high scan rate of 160 mV s-1, a decent specific capacitance of 147 F g-1 and 114 F g-1 was obtained, leading to high energy densities of 26.0 and 22.1 W h kg-1 based on averaged electrode mass. Surface properties and the porous structure of the ACs were studied by scanning electron microscopy, energy-dispersive X-ray analysis, Raman spectroscopy, and the Brunauer-Emmett-Teller method.
-
High‐performance activated carbons for supercapacitor: Effects of porous structures, heteroatom doping, and morphology
Xinyu Cai,Qingyuan Ren,Wei Sun,Fuqian Yang
DOI: https://doi.org/10.1002/er.7191
IF: 4.6
2021-09-01
International Journal of Energy Research
Abstract:In this work, we prepare a series of activated carbons (ACs) of different morphologies, porous structures, and oxygen contents from glucose with hydrothermal synthesis (HTS) followed by a one-step (H2O-steam or KOH) or two-step (H2O-steam-KOH or KOH-H2O-steam) activation. The largest surface area of the prepared ACs is more than 3400 m2/g, and the corresponding mesopore volume is 1.21 cm3/g. The fraction of oxygen in the ACs varies in a range of 3.94 to 9.9 at%. The electrochemical performance of the symmetric supercapacitor cells (SCs) made from the as-prepared ACs is characterized in different aqueous electrolytes. The optimum capacitance of the SCs is 421 F/g at 0.5 A/g and 304 F/g at 10 A/g. The oxygen-enriched functional groups have limited contribution to the energy storage for the SCs with neutral electrolyte and profound effects on the increase of the energy storage for the SCs with strong acidic and alkaline electrolytes. The processing routes developed in this work likely open an avenue to tailor the structures and oxygen-enriched functional groups of ACs.
energy & fuels,nuclear science & technology
-
Activating the Highly Reversible Mo 4+ /Mo 5+ Redox Couple in Amorphous Molybdenum Oxide for High-Performance Supercapacitors
Xiang Cai,Xiao-Guang Sang,Yu Song,Di Guo,Xiao-Xia Liu,Xiaoqi Sun
DOI: https://doi.org/10.1021/acsami.0c13692
2020-10-13
Abstract:Molybdenum oxide provides high theoretical capacity, but the moderate charge transfer kinetics and cycle life have limited the applications for capacitive energy storage. Herein, the electrochemical performance of molybdenum oxide is modified by tuning the active redox couple through an electrochemical activation process. The activated electrode K-MoO<sub><i>x</i></sub> with a 10 mg cm<sup>–2</sup> loading shows excellent pseudocapacitive behavior within the large potential range of −1.2–0 V and delivers 313 F g<sup>–1</sup> capacitance at 5 mA cm<sup>–2</sup>. It also presents an ultrastable cycle life, with a 98% capacitance retention after 10,000 cycles. The activation process involves the insertion of K<sup>+</sup> into MoO<i><sub>x</sub></i>, which modifies the Mo electronic structure and introduces Mo<sup>4+</sup> sites according to X-ray photoelectron spectroscopy. As a result, the charge storage redox couple shifts from Mo<sup>5+</sup>/Mo<sup>6+</sup> to Mo<sup>4+</sup>/Mo<sup>5+</sup>, with the latter delivering higher electrochemical activity due to improved conductivity. Electrochemical impedance spectroscopy also suggests faster ion diffusions and thus higher power capability in K-MoO<i><sub>x</sub></i>, resulting in the enhanced performance. A 2.4 V asymmetric supercapacitor is assembled using K-MoO<i><sub>x</sub></i> as the anode with a MnO<i><sub>x</sub></i> cathode. The work demonstrates a feasible and facile strategy to promote the pseudocapacitive behavior of metal oxide materials.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c13692?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c13692</a>.The GCD profiles of the K-MoO<i><sub>x</sub></i>//MnO<i><sub>x</sub></i> ASC device during the first discharge and the following charge–discharge cycle, the HRTEM image of K-MoO<i><sub>x</sub></i>, EDS of the K-MoO<i><sub>x</sub></i> electrode, XPS survey spectra of K-MoO<i><sub>x</sub></i> before and after 10 nm etching, EDS of the MoO<i><sub>x</sub></i> electrode at the ∼3500th activation cycle and GCD profile compared with K-MoO<i><sub>x</sub></i>, K 2p XPS of K-MoO<i><sub>x</sub></i>, the areal and specific capacitance evolution of the MoO<i><sub>x</sub></i> electrode cycling in the 3 M LiCl or NaCl aqueous electrolyte, N<sub>2</sub> adsorption–desorption isotherms of MoO<i><sub>x</sub></i> and K-MoO<i><sub>x</sub></i> at 77 K, electrochemical performance of 3DGS, post-cycling analysis on K-MoO<i><sub>x</sub></i>, the <i>C</i>″ vs frequency plots for MoO<i><sub>x</sub></i> and K-MoO<i><sub>x</sub></i>, the element contents in K-MoO<i><sub>x</sub></i> measured by ICP, and capacitance and cycling stability of the reported molybdenum pseudocapacitive electrodes (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c13692/suppl_file/am0c13692_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology
-
Ultrahigh-surface-area activated biocarbon based on biomass residue as a supercapacitor electrode material: Tuning pore structure using alkalis with different atom sizes
Nopparat Sangtong,Thanyalak Chaisuwan,Sujitra Wongkasemjit,Hatsuo Ishida,Wikrom Redpradit,Kessara Seneesrisakul,Uthen Thubsuang
DOI: https://doi.org/10.1016/j.micromeso.2021.111383
IF: 5.876
2021-10-01
Microporous and Mesoporous Materials
Abstract:This work aims to develop an electrode material based on activated biocarbon made from rubber wood sawdust waste using alkali activating agents – KOH, NaOH, and LiOH – via a solvent-free mechanical mixing. The role of different alkali metal atom sizes plays in resulting pore structure has been studied for the first time. The influence of standard reduction potentials on the pore structure and electrochemical performance of the activated biocarbon are also investigated. The biocarbons activated with KOH or NaOH exhibit a microporous characteristic and a wide range of specific surface area of 1323–3040 m2/g, while the one activated with LiOH exhibits a mesoporous nature. The comparatively small atom size of Li and its low standard reduction potential may have caused the slow reactivity of LiOH with carbon matrix. This leads to the low specific surface area of 1134 m2/g and the formation of tiny lithium particles that could intercalate into biocarbon structure more readily than potassium or sodium particles. Mesoporosity tends to be generated by using alkali activating agent with small metal atom size and low standard reduction potential, whereas microporosity has an opposite trend. Cyclic voltammetry curves and charge-discharge profiles confirm the dominant EDLC behavior along with partial pseudocapacitance for activated biocarbons. The maximum specific capacitance is 195.3 F/g at 0.25 A/g for biocarbon activated with KOH at 4:1. This value is reduced to 69.4% of its original values at 4 A/g. The biocarbons activated with LiOH or NaOH retain the rate capability by 82.9% and 80.4%, respectively.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology, applied
-
Electrolyte-Dependent Supercapacitor Performance on Nitrogen-Doped Porous Bio-Carbon from Gelatin
Jie Deng,Jing Li,Shuang Song,Yanping Zhou,Luming Li
DOI: https://doi.org/10.3390/nano10020353
IF: 5.3
2020-02-18
Nanomaterials
Abstract:The carbon supercapacitance strongly relies upon the electrolyte’s nature, but the clear-cut structure–performance nexus remains elusive. Herein, a series of bio-carbons with gradually varied pore structure and surface chemistry are derived using a new salt template protocol (with eco-benign KNO3 as the template, activator, and porogen, and cheap gelatin as the carbon precursor), and are used as model systems to probe the dependence of the electrochemical mechanism of such nanocarbons on two typical electrolytes (KOH and EMIBF4). By only adjusting the KNO3 dosage, two pivotal figures of merit of biochar—multiscale porosity and surface functionalization—were finely modulated to construct electric double layers. Electrochemical data clarify that the combined porosity and doping effects all contribute to enhanced supercapacitance, but with only one of the two factors playing the leading role in different electrolytes. Kinetic analysis corroborates the fact that ample heteroatom doping can effectively compensate capacitance by intensive surface redox insertion in KOH, while a suitable pore size dispersion plays a preponderant part in self-amplifying the ion partitioning, and thus dictating a good charge separation in EMIBF4. A quasi-quantitative model of performance–structure relevance in EMIBF4 is judiciously conjectured to hint at a superb ion–pore-size compatibility, in which the bi- and mono-layer ion confinement coupling in integrated single and double ion-sized pores is found to be more useful for curbing notorious over-screening effects and for changing the coordination number, Coulombic ordering, and phase conformation of EMIBF4 in several nm-sized nanopores. This unique energy storage fashion in ion-matching pores promotes the energy density of optimal samples to a novel level of 88.3 Wh kg−1 at 1 kW kg−1, which rivals the overwhelming majority of the reported carbon materials. In short, the comparison case study here reveals a valuable correlation of carbon’s figure of merit and electrolyte type, which may act as a vital rudder to design electrolyte-contingent state-of-the-art supercapacitor materials.
materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology,chemistry
-
Acid-treated waste sisal fiber derived activated carbon as efficient electrode material for solid-state supercapacitor
Yashi Saxena,Ashish Gupta,Pooja Devi,Ashavani Kumar
DOI: https://doi.org/10.1016/j.diamond.2024.111672
IF: 3.806
2024-10-19
Diamond and Related Materials
Abstract:Activated Carbon (AC), obtained from biomass is highly adaptable and valued for its versatile benefits including high surface area, conductivity, chemical inertness, etc. in various applications. It is also used as an electrode in supercapacitors for applications requiring a high-power supply. Sisal fiber, derived from the Agave sisalana plant, has several advantages, including its fibrous and porous framework, that make it suitable for conversion into activated carbon for energy storage applications in the context of sustainability and reduced environmental impact. In this study, we have prepared H 2 SO 4 treated KOH activated carbon from residual Sisal fiber (SFH 2 AC) which is then utilized as an electrode material for supercapacitors. SFH 2 AC exhibits hierarchical and structure-based porosity with a large specific surface area (S A ) of 1185 m 2 /g and shows the maximum specific capacitance (C s ) of 340 F/g @ 0.5 A/g in 6 M KOH electrolyte. In KOH electrolyte, strong cycling retention (during the length of 9000 GCD cycles) is attained as; 98 % up to the first 3000 cycles at 10 A/g, 93 % up to next 3000 cycles at 20 A/g, and 90 % up to the last 3000 cycles at 30 A/g. Furthermore, the SFH 2 AC//SFH 2 AC(Gel) device was built by using SFH 2 AC as electrodes with PVA/KOH gel as an electrolyte in order to assess the supercapacitor performance in real time. The device has a specific power density of 7500 W/kg and a maximum energy density of 12 W h/kg. The device reveals an exceptional 97 % cycling stability, maintaining up to 9000 repeated GCD cycles at an increased current density (C D ) of 30 A/g.
materials science, multidisciplinary,physics, applied, condensed matter, coatings & films
-
Mos2 Being Used As Negative Electrode for Asymmetric Electrochemical Capacitors
Zhao Li-Ping,Wang Hong-Yu,Qi Li
DOI: https://doi.org/10.3724/sp.j.1077.2013.12630
IF: 1.292
2013-01-01
Journal of Inorganic Materials
Abstract:MoS2 was adopted as a negative electrode material for the asymmetric electrochemical capacitors of MoS2/activated carbon (AC) using Li+-based organic electrolytes. This type of capacitors possesses the working voltage as high as 3.4 V. The physical properties of the negative electrode were characterized by XRD and SEM, etc. The charge storage mechanism at the negative electrode was studied and the effect of weight ratio of AC/MoS2 was investigated. The electrochemical performance tests reveal that the capacitors have relatively high energy density and power density, i.e., 28.7 Wh/kg and 1203.4 W/kg, respectively. The capacitors also show good cycle stability, displaying a 76.6% capacity retention after 1000 cycles at current density of 0.4 A/g.