Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Preparation and Photocatalytic Performance of Ag-Doped Titanium Dioxide Whiskers

Preparation of WO<sub>x</sub>-TiO<sub>2</sub> and the Photocatalytic Activity under Visible Irradiation

Influence of Preparation Method on Morphology and Photocatalysis Activity of Nanostructured TiO2.

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Preparation of AgI Sensitized Amorphous TiO2 As Novel High-Performance Photocatalyst for Environmental Applications

PREPARATION OF IRON-DOPED TITANIA NANOCRYSTALLINE GRAINS AND ITS PHOTOCATALYTIC PROPERTY

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Preparation of Nanoparticle WO_3-doped TiO_2 and Research on Its Photocatalytic Activity

Preparation and Photocatalytic Properties of Fe(III)-Grafted TiO<sub>2</sub> Nano-Composite Powders

Facile Synthesis of Ni-doped TiO2ultrathin Nanobelt Arrays with Enhanced Photocatalytic Performance

(001)-Exposed TiO2 Microcrystals Decorated with Few-Layer Nanobelts for Enhanced Photocatalytic Activity

Preparation and Photocatalytic Activity of Vanadium-doped Nano-TiO_2

Study on Preparation and Decontamination Properties of Hybrid-Photocatalysis Based on Graphene and TiO<sub>2</sub>

Preparation and activity of Ag-TiO2 photocatalyst with multi-valency state

Preparation and Photocatalytic Activity of Nanoparticle Fe/TiO2 by Chemical Precipitation Method

Co-Modified Commercial P25 Tio2 by Fe Doping and G-C3n4 Coating As High Performance Photocatalyst under Visible Light Irradiation

Synthesis and characterization of ZnTiO3 with high photocatalytic activity

Preparation and Photocatalytic Properties of Mo-doped TiO2

Anatase-TiO2 nano-particle preparation with a micro-mixing technique and its photocatalytic performance

Synthesis and Photocatalysis Properties of Sulfur Doped Nanocrystalline TiO2 Photocatalyst

Acid-assisted Synthesis of TiO2 Nanoparticles for Enhancement of Visible Light Photocatalytic Efficiency