Synthesis and Characteristics of Large-Scale ZnO Rods by Wet Chemical Method

Wei Su-feng,Jiang Qing,Lian Jian-she
DOI: https://doi.org/10.1016/s1003-6326(08)60186-7
IF: 3.752
2008-01-01
Transactions of Nonferrous Metals Society of China
Abstract:The large-scale ZnO rods of submicrometer were prepared on the bare glass using a wet chemical method under different experimental parameters, such as the reactant concentration and the growth time. The microstructure of the ZnO rods was characterized by X-ray diffractometry(XRD) and field emission scanning electron microscopy (FESEM) with the energy dispersive X-ray spectroscopy(EDX), and the optical property was investigated by the room-temperature photoluminescence (PL) spectra. XRD and FESEM results show that the wurtzite structure and rod-like ZnO is obtained. The length (3–8 μm) and the diameter (400 nm– 3 μm) vary with the experimental parameters. A strong UV emission at 384 nm and a weak visible yellow-green emission around 570 nm are observed in the PL spectrum. After annealing at 600 °C in air, the UV peak intensity increases obviously and the yellow-green peak intensity decreases greatly. The near-band-edge UV emission is attributed to the exciton recombination; the yellow-green emission can be associated with the defect recombination; and some defect complexes may be responsible for the latter emission.
What problem does this paper attempt to address?