Abstract:Objective To observe the vascularization of porous silk fibrion scaffolds(PSFSs) following spinal cord injuries in rats so as to lay the foundation for the application of PSFSs in tissue engineering. Methods PSFSs were prepared with certain pore sizes and porosity.28 female Sprague-Dawley rats,250~300g in body weight,were selected and devided into two groups(A:experimental group,n=16;B:control group,n=12). All the animals received an operation of semi-transection in spinal cord.PSFSs were transplanted in animals in A group while other animals in B group received Polyvinyl Alcohol(PVA). After a survival period of 4~28 days,rats were killed following a perfusion,the spinal cords including materials were cut for histological and immunohistological staining. Furthermore,the unltrastructure of microvessels was detected with TEM in A group. Results HE staining shows that the inflammatory response was more moderate in A group than that in B group,and the degradation of materials was more obvious in A group than that in B group. MVD at 7d,10d,14d,21d,28d postoperation in A group was 1.4,3.6,10.6,8.6,8.8,respectively. On the contrary,the quantity in B group was 0,2.2,4.8,4.6,4.0. The microvessels in A group were observed even at 7d postoperation,and the peak appeared at 14d postoperation. Then the quantity decreased to a stable level. The trend of MVD in B group was similar to that in A group. Conclusion PSFSs can be vascularized in spinal cord of rats,and it can be applied for nerve tissue repair in tissue engineering.

Vasculaerization of porous silk fibroin scaffolds following spinal cord injury in rats