Epitaxial Crystallization and Oriented Structure of Linear Low-Density Polyethylene/Isotactic Polypropylene Blends Obtained Via Dynamic Packing Injection Molding

Run Su,Ke Wang,Qin Zhang,Feng Chen,Qiang Fu,Nan Hu,Erqiang Chen

DOI: https://doi.org/10.1002/pat.1522

IF: 3.348

2011-01-01

Polymers for Advanced Technologies

Abstract:In this work, as a part of a long-term project aimed at controlling of crystal structure and phase morphology for a injection molded product, we investigated the oriented structure and possible epitaxial growth of polyolefin blend (low-density polyethylene (LLDPE)/isotatic polypropylene (iPP)), achieved by dynamic packing injection molding, which introduced strong oscillatory shear on the gradually-cooled melt during the packing process. The crystalline and oriented structures of the prepared blends with different compositions were estimated in detail through 2D X-ray diffraction, calorimetry, and optical microscopy. As iPP was the dominant phase (its content was more than 50 wt%), our results indicated that it could be highly oriented in the blends. In such case, it was interesting to find that LLDPE epitaxially crystallized on the oriented,PP through a crystallographic matching between (100)(LLDPE) and (010)(iPP) resulting in an inclination of LLDPE chains, about 50 degrees to the iPP chain axis. On the other hand, as iPP was the minor phase, iPP was less oriented and no epitaxial growth between iPP and LLDPE was observed; even LLDPE remained oriented. The composition-dependent epitaxial growth of LLDPE on oriented iPP could be understood as due to: (1) the effect of crystallization sequence, it was found that iPP always crystallized before LLDPE for all compositions; (2) the dependence of oriented iPP structure on the blend composition; (3) the "mutual nucleation" between LLDPE and iPP due to their partial miscibility. Copyright (C) 2009 John Wiley & Sons, Ltd.