The formation of a layer of Fe3O4 nanoplates between two carbon films

Na Fan,Xicheng Ma,Xinzheng Liu,Liqiang Xu,Yitai Qian

DOI: https://doi.org/10.1016/j.carbon.2007.04.029

IF: 10.9

2007-01-01

Carbon

Abstract:Monodispersed Fe3O4 nanoplates between two carbon films were synthesized by pyrolyzing ferrocene and sodium oxalate in a stainless steel autoclave of 64mL capacity at 600°C. The Fe3O4 nanoplates are triangular single crystals, sometimes truncated, with edge lengths ranging from 50 to 100nm. In an experiment where the pressure of the reaction system was increased, carbon-encapsulated Fe3O4 nanorods were obtained. The inner Fe3O4 nanorods are also single crystal with a diameter ca. 100nm and lengths up to 1μm. A possible formation mechanism for the layered structure is proposed based on the experimental results. Magnetic property measurements show that the layered nanoplates display ferromagnetic properties at room temperature.