Ca[sub 2]al[sub 2]sio[sub 7]:Ce[sup 3+], Tb[sup 3+]: A White-Light Phosphor Suitable for White-Light-Emitting Diodes

Haiyan Jiao,Yuhua Wang
DOI: https://doi.org/10.1149/1.3097191
IF: 3.9
2009-01-01
Journal of The Electrochemical Society
Abstract:Rare-earth-activated, white-emitting phosphors Ca2-x-yAl2SiO7:xCe(3+), yTb(3+) were prepared under a weak reducing atmosphere by conventional solid-state reaction and their luminescence properties under 352 nm excitation were investigated in detail. Ca2Al2SiO7:Tb3+ shows excitation at short-UV wavelength light lambda(ex) = 241 nm. Ca2Al2SiO7:Ce3+, Tb3+ showed optimal excitation at long-UV light excitation lambda(ex) = 352 nm. By incorporation of Ce3+, an efficient energy transfer from Ce3+ to Tb3+ was found and generated white light under long-UV excitation. The emission spectra consisted of a blue band (similar to 419 nm) and a green band (similar to 542 nm), the relative intensities of which changed with the rare earth dopant concentration x and y. As a result, the optimal concentration for the best luminescence intensity was obtained in Ca2Al2SiO7:0.0075Ce(3+), 0.030Tb(3+), and the closest to daylight white emission was found with a composition of Ca2Al2SiO7:0.0075Ce(3+), 0.020Tb(3+), which has chromaticity coordinates x = 0.316, y = 0.336. This is considered to be a potential white-emitting phosphor for white light-emitting diodes. (C) 2009 The Electrochemical Society. [DOI: 10.1149/1.3097191] All rights reserved.
What problem does this paper attempt to address?